Annealing effect on temperature coefficient of resistivity in La1−xSrxMnO3 ceramics

We investigated annealing effects of La_1?xSr_xMnO₃ (x = 0–0.6) on electrical resistivity and the temperature coefficient of resistivity (TCR). The annealed samples’ resistivity was lower than those of non-annealed samples. For example, annealing changed the resistivity of x = 0.3 at 25 °C from 4.50 × 10^?5 to 3.71 × 10^?5 Ω m. Remarkable difference in TCR was observed after annealing, for x = 0.3, 0.45, and 0.5. For x = 0.3, the TCR after annealing was 4000 ppm/°C, which was 1250 ppm/°C greater than that before annealing. We investigated (1) crystal phase, (2) Mn average valence, (3) Mott insulator–metal transition temperature, and (4) microstructure. The microstructure was remarkably varied for annealed x = 0.3 and 0.5. The average grain size of the x = 0.3 increased from 1.60 up to 2.38 μm. Results show that annealing affects resistivity and TCR because of grain growth during annealing.     

Surface Orientation and Wetting Phenomena in Si/α-Alumina System at 1723 K

Wetting phenomena and the effect of alumina surface orientation on the wettability in Si/α-Al₂O₃ system were studied by an improved sessile drop method using     ,     , C(0001) faces of single crystals and polycrystals at 1723 K in a reducing Ar–3% H₂ atmosphere. The contact angles show a vibration behavior for all the single crystals but to a less extent for the polycrystals. The extent of the vibration correlates not only with the reaction intensity but also with the stability of the Si droplet on the alumina surfaces. The interfacial reaction leads to the formation of a series of reaction rings, which is more serious at the single crystal surfaces. More importantly, the wettability is dependent on the alumina surface orientation, with the intrinsic contact angles being about 98±2°, 101±1°, 69±1°, and 98±2°, respectively, for the     ,     , C(0001) and polycrystal α-Al₂O₃ substrates. The much smaller contact angle for molten Si on the C(0001) surface is explained by the favorable reduction in the Si/α-Al₂O₃ interfacial free energy by the terminated and enriched aluminum atoms at the reconstructed     surface. The importance of the aluminum presence at the Si/α-Al₂O₃ interface to the wettability of this system was further demonstrated by a substantial improvement in the wettability of the     α-Al₂O₃ substrates by Si–Al alloys.     

Cerebral Hyperperfusion after Revascularization Inhibits Development of Cerebral Ischemic Lesions Due to Artery-to-Artery Emboli during Carotid Exposure in Endarterectomy for Patients with Preoperative Cerebral Hemodynamic Insufficiency: Revisiting the “Impaired Clearance of Emboli” Concept

The purpose of the present study was to determine whether cerebral hyperperfusion after revascularization inhibits development of cerebral ischemic lesions due to artery-to-artery emboli during exposure of the carotid arteries in carotid endarterectomy (CEA). In patients undergoing CEA for internal carotid artery stenosis (≥70%), cerebral blood flow (CBF) was measured using single-photon emission computed tomography (SPECT) before and immediately after CEA. Microembolic signals (MES) were identified using transcranial Doppler during carotid exposure. Diffusion-weighted magnetic resonance imaging (DWI) was performed within 24 h after surgery. Of 32 patients with a combination of reduced cerebrovascular reactivity to acetazolamide on preoperative brain perfusion SPECT and MES during carotid exposure, 14 (44%) showed cerebral hyperperfusion (defined as postoperative CBF increase ≥100% compared with preoperative values), and 16 (50%) developed DWI-characterized postoperative cerebral ischemic lesions. Postoperative cerebral hyperperfusion was significantly associated with the absence of DWI-characterized postoperative cerebral ischemic lesions (95% confidence interval, 0.001–0.179; p = 0.0009). These data suggest that cerebral hyperperfusion after revascularization inhibits development of cerebral ischemic lesions due to artery-to-artery emboli during carotid exposure in CEA, supporting the “impaired clearance of emboli” concept. Blood pressure elevation following carotid declamping would be effective when embolism not accompanied by cerebral hyperperfusion occurs during CEA.     

Correlations of Hepatic Hemodynamics,Liver Function,and Fibrosis Markers in Nonalcoholic Fatty Liver Disease: Comparison with Chronic Hepatitis Related to Hepatitis C Virus

The progression of chronic liver disease differs by etiology. The aim of this study was to elucidate the difference in disease progression between chronic hepatitis C (CHC) and nonalcoholic fatty liver disease (NAFLD) by means of fibrosis markers, liver function, and hepatic tissue blood flow (TBF). Xenon computed tomography (Xe-CT) was performed in 139 patients with NAFLD and 152 patients with CHC (including liver cirrhosis (LC)). The cutoff values for fibrosis markers were compared between NAFLD and CHC, and correlations between hepatic TBF and liver function tests were examined at each fibrosis stage. The cutoff values for detection of the advanced fibrosis stage were lower in NAFLD than in CHC. Although portal venous TBF (PVTBF) correlated with liver function tests, PVTBF in initial LC caused by nonalcoholic steatohepatitis (NASH-LC) was significantly lower than that in hepatitis C virus (C-LC) (p = 0.014). Conversely, the liver function tests in NASH-LC were higher than those in C-LC (p < 0.05). It is important to recognize the difference between NAFLD and CHC. We concluded that changes in hepatic blood flow occurred during the earliest stage of hepatic fibrosis in patients with NAFLD; therefore, patients with NAFLD need to be followed carefully.     

Dynamic in situ observation of automotive catalysts for emission control using X-ray absorption fine structure

Two main pivotal subjects of research in automotive catalysts were studied by modern X-ray absorption analysis techniques. One is oxygen storage/release behaviour, and the other is sintering inhibition of Pt particles. First, three types of CeO₂–ZrO₂ (Ce:Zr = 1:1 molar ratio) compounds with different oxygen storage/release capacities and different structural properties were prepared, and the valence change of Ce as a function of temperature during oxygen release/storage processes was investigated. The reduction of surface Ce mainly occurred in the range 100–170 °C, and the reduction of bulk Ce progressed at high temperatures of 170 °C and above. The Ce reduction behaviour depended not only on the homogeneity of the Ce and Zr for bulk reduction at high temperatures but also on the particle size of the CeO₂–ZrO₂ samples for surface reduction at low temperatures. Secondly, sintering inhibition of Pt in Pt/Al₂O₃, Pt/MgO and Pt/ceria-based catalysts after 800 °C ageing in air was studied. We found that the Pt–O–M (M = Mg, Ce) bond acted as an anchor and inhibited the sintering of Pt particles on MgO or ceria-based oxide. Especially, it was noteworthy that the Pt–O–Ce⁴⁺ bond on the ceria-based support breaks easily through the reduction of Ce (Ce⁴⁺ → Ce³⁺) during the usual stoichiometric and reducing conditions.     

Role of Cu film texture in grain growth correlated with twin boundary formation

To understand the role of Cu film texture in grain growth at room temperature (RT) in relation to twin boundary formation Cu films were deposited on various barrier materials and the Cu film texture was investigated by X-ray diffraction. Cu grain growth was rapid on a barrierless SiO₂/Si substrate and very slow on a Ta barrier due to strong (1 1 1) texture. The growth rate and the average grain diameter after being kept at RT for up to ∼60 days were maximum at a (2 0 0)_Cu peak to (2 2 2)_Cu peak area ratio of ∼1.0, where {1 1 1}, {1 0 0} and {5 1 1} grains coexisted. Such coexistence of three or more orientations of grains is essential in facilitating Cu grain growth at RT. Similarly, the average twin boundary (TB) density was maximum when Cu grain growth was facilitated. TB formation in nano-sized Cu grains was not controlled by grain size, but due to grain growth. The TB could be annealing twins caused by irregularities in the stacking sequence during relatively fast grain growth. The Cu film texture is concluded to be determined at the beginning of deposition, and the wettability of various barrier materials by the Cu films plays a key role in determining the film texture.     

New type of phenolic resin: Curing reaction of phenol‐novolac based benzoxazine with bisoxazoline or epoxy resin using latent curing agent and the properties of the cured resin

In this study, we aimed to reduce the cure time, and to lower the cure temperature of the benzoxazine compound. Therefore, curing reaction of benzoxazine with bisoxazoline or epoxy resin using the latent curing agent and the properties of the cured resins were investigated. The cure behavior of benzoxazine with bisoxazoline or epoxy resin using the latent curing agent was monitored by differential scanning calorimetry and measurements for storage modulus (G′). The properties of the cured resin were estimated by mechanical properties, electrical insulation, water resistance, heat resistance, and flame resistance. As a result, it was confirmed that by using the latent curing agent, cure time of benzoxazine and bisoxazoline or epoxy resin was reduced, and cure temperature was lowered. And it was found that the curing reaction using phenol‐novolac based benzoxazine (Na) as the benzoxazine compound could proceed more rapidly than that using bisphenol‐A based benzoxazine (Ba) as the benzoxazine compound. However, the cured resins from Ba and bisoxazoline or epoxy resin using the latent curing agent showed good heat resistance, flame resistance, and mechanical properties compared with those from Na and bisoxazoline or epoxy resin using the latent curing agent. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

PVDF/PMMA composite nanofiber fabricated by electrospray deposition: Crystallization of PVDF induced by solvent extraction of PMMA component

The crystallization of poly(vinylidene fluoride) (PVDF) was observed after the poly(methyl methacrylate) (PMMA) component was extracted from the PVDF/PMMA (50/50) composite nanofiber fabricated by electrospray deposition, even though the original composite showed a completely amorphous pattern in the wide‐angle X‐ray diffraction. The content of the β‐crystal form in the crystalline region depended on the PVDF/PMMA composite ratios and the type of solvents used for the extraction of the PMMA component, e.g., chloroform and toluene. Thus, the content of the β‐crystal form can be controlled by selecting the original PVDF/PMMA composition and the solvent used to extract the PMMA component. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Experimental study of bubbly swirling flow in a vertical tube using ultrasonic velocity profiler (UVP) and wire mesh sensor (WMS)

Two-phase air-water bubbly swirling flow through a pipe is a complex turbulent flow and its prediction is still challenging. The present paper describes the experimental investigation of the air-water bubbly swirling flow in vertical co-current flow. Swirling flow is induced by a twisted tape in a 20 mm inner diameter pipe. The flow is investigated using Ultrasonic velocity profiler (UVP), which allows the measurement of liquid and gas velocities simultaneously. Furthermore, simultaneous measurement of void fraction is performed using Wire mesh sensor (WMS). The experimental results reveal that swirling flow has significant impact on bubbles’ distribution. In low liquid flow rate, the average bubble velocity is fairly uniform along the radial position and void fraction increases in the near wall region. However, increasing liquid flow rate at constant gas flow rate leads to increase in void fraction in the core region, this is mainly due to drift velocity which is affected by centrifugal force. Experimental findings and parametric trends based on the effects of swirling flow are summarized and discussed.