Synthesis and electrochemical properties of Th-doped LiMn2O4 powders for lithium-ion batteries

To improve the cycle performance of eco-friendly and cost-effective spinel LiMN2O4 as the Li secondary batteries, the Th-doped LiThxMn1-xO4 spinel powers were synthesized by solid-state method. The starting materials, Li2CO3,MnO2 and Th(NO3)4·4H2O, were mixed uniformly using a traditional ball milling, which resulted in a uniform particle size distribution in the mixed powers. Tests of X-ray diffraction, SEM, impedance spectra and charge-discharge were carried out for LiThxMn1-xO4 cathode materials. Results show that the synthesized LiTh0.01Mn1.99O4 material exhibits standard spinel structure, regular particle morphology and excellent property of charge-discharge for big current. The capacity retention of the material modified by doping Th is more than 85.1% of the first discharge specific capacity of 111.5 mAh·g -1 after 20 cycles at the current rate 1C, while the pristine LiMN2O4 is only 57% of the first discharge specific capacity of 110.2 mAh·g-1 after the same cycles at the same current rate.     

钴纳米颗粒的制备及其表征

采用简单的溶液还原方法，以聚乙烯吡咯烷酮（PVP，MW=58，000）作为高分子表面修饰剂，用水合肼（50％）作为还原剂，经回流处理，成功地制备出了分散性较好的钻纳米颗粒。利用XRD、TEM、SQUID等实验方法对产物的形貌、物相及磁性进行了表征。结果表明，产物为六方结构。其饱和磁化强度为153emu／g-1．62μB／Co，是体相材料的饱和磁矩的95％，其矫顽力为5174A·m^-1。此方法的优点在于反应条件温和、成本较低，重复性强、产率高且宜于控制。     

Study on the flash butt welding of 400 MPa ultra-fine grain steel

A 400 MPa ultra-fine grain steel possesses high strength and toughness. Due to its fine grain size, the heat affect zone (HAZ) of the weld joint will soften during welding. The weldability of 400 MPa ultra-fine reinforced steel bar of flash butt welding is investigated by using the micro metallographical examination and macro-mechanical-property tests. The joint of flash butt welding has a superior mechanical property. The HAZ in the weld joint does not show apparent softening. There is only a localized softening spot inside the weld seam, which does not affect the property of the whole joint. Therefore, flash butt welding is appropriate for joining the 400 MPa ultra-fine grain reinforced steel bars. The resulting weld joint has excellent mechanical properties.     

基于有限元的大型铝型材拉伸矫直设备设计方法研究

介绍了大型铝型材拉伸矫直设备的研究现状,分析了现有拉伸矫直设备的缺点,提出并设计了新型的大型铝型材拉伸矫直设备。采用有限元数值模拟方法,对大型铝型材拉伸矫直机的关键零部件受力变形状况进行了数值模拟,得到了设备关键零部件如拉伸头、移动横梁等的应力和应变分布情况,并对结构进行了优化。此种方法降低了设备制造成本,提高了设备的精度和刚度。生产实践表明:采用此方法设计的拉伸矫直机运行平稳可靠。     

基于DXF文件的曲线拟合方法的设计与实现

现有的基于微机开发的数控加工系统都是人工调试完成后加载运行,为了能够依据AUTOCAD绘图系统提供的信息自动生成数控加工代码,本文对基于PMAC卡的数控加工代码生成及动态在线监测系统研制过程中遇到的问题进行了研究,重点研究了如何利用DXF文件中的参数进行曲线拟合,详细介绍了NURBS曲线算法的实现,为后续的工作打下了基础。     

冲压成形仿真过程中有限元网格模型的建立

网格模型对冲压成形模拟的精度和效率影响极大 ,文中阐述了有限元网格模型建立的方法 ,并从单元尺寸、单元类型、自适应网格再划分技术等方面论述了如何解决精度与效率的问题。     

Na2SiO3—KOH—（NaPO3）6溶液中Ti6Al4V微弧氧化陶瓷膜研究

用非平衡交流微弧氧化法于Na2SiO3-KOH-(NaPO3)6溶液中在Ti6Al4V表面形成氧化物陶瓷膜。分别用扫描电镜、电子探针及X射线衍射研究了陶瓷膜的组织形貌、元素分布和相组成。相对致密均匀的膜层主要由TiO2(钙钛矿相及金红石相)及非晶相组成。厚约20μm的膜可分为3层：过渡层、致密层与疏松层。电解液所含元素Si，P进入到膜层中，表明电解液组元急烈参与微弧氧化反应，这为通过选择电解液来设计膜层的相组成进而对膜层进一步改性提供途径。     

1—HBTA对钢,黄铜的缓蚀作用

研究在3％NaCl水溶液和模拟冷却水介质中,不同pH值时不同浓度(0.05％、0.1％、0.5％)的1-羟基苯骈三氮唑(以下简称1-HBTA)对钢、黄铜的缓蚀作用,1-HBTA是一种阳极型缓蚀剂,对金属腐蚀的阳极过程有明显的阻滞作用,而对阴极过程影响不大。     

原位生成Al2O3、TiB2和Al3Ti/Al复合材料的热循环行为

本文研究了Al-TiO2-B系原位生成Al2O3、TiB2和Al3Ti/Al颗粒增强铝基复合材料的热循环行为，研究结果表明了纯铝及B／TiO2摩尔比分别为0、1和2的颗粒增强铝基复合材料的热循环行为具有以下结果，纯铝和复合材料热循环后均产生了残余应变和滞后环；Al-TiO2-B系列复合材料热循环应变的各项指标均比纯铝基体大大降低，且具有较小的内耗功和较好的热稳定性，可以预测其具有较高的热疲劳寿命，热循环曲线能很好的评估复合材料在温度循环变化的环境中工作时的热稳定性和热疲劳。     

铁氮共掺杂纳米TiO2的水热法制备及其在可见光下抗菌性能的研究

以硫酸氧钛为前驱体，硝酸铁和盐酸胍作为掺杂的铁源和氮源，采用水热法制备了铁氮共掺杂纳米TiO2粉体。利用XRD、BET对样品进行表征，研究了掺杂后TiO2粉体的晶型、粒径、比表面积等性能。结果表明，所制备的共掺杂TiO2粉体呈黄色，均为锐钛矿相TiO2，经谢尔公式计算其粒径约为10nm，比表面积分布为（135～150）m^2／g。采用紫外．可见光漫反射光谱对样品进行表征，结果表明经过铁氮共掺杂改性后的TiO2具有很强的紫外线的吸收能力，并实现了良好的可见光响应。采用菌落计数法进行了样品抗菌性能的研究，在可见光照射下样品对大肠杆菌表现出良好的杀灭性能。