Effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers

In this paper, polyborosilazane precursor was synthesied from HMDZ, HSiCl₃, BCl₃ and CH₃NH₂ using a multistep method. By controlling the storage conditions, parts of the polyborosilazane fibers were hydrolyzed. FT-IR, NMR, XRD, TEM and monofilament tensile strength test were employed to study the effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers. FT-IR and NMR results indicate that Si-N group in PBSZ reacts with H₂O to form Si-O-Si group. After pyrolysis reaction at 1400℃, Si-O-Si group will finally transformed into highly ordered cristobalite and β-quartz, resulting in formation of the wrinkled surface of the obtained SiBN ceramic fiber. The strip-like defects on fiber surface, according to monofilament tensile strength test, had a significant effect on mechanical property of the obtained SiBN ceramic fiber and caused no increase in fiber tensile strength of hydrolytic polyborosilazane fiber before and after pyrolytic process.     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

秸秆微晶纤维素用作片剂崩解剂的初步评价

对实验室自制秸秆微晶纤维素用作片剂崩解剂进行了初步评价。参照《中国药典》(2010版)中微晶纤维素的有关规定,评估自制秸秆微晶纤维素的质量;以阿司匹林为模型药物,以市售微晶纤维素(PH-101)为对照,测定秸秆微晶纤维素的溶胀性、崩解性。结果表明,自制的秸秆微晶纤维素质量符合《中国药典》有关规定,且溶胀性和崩解性优于市售微晶纤维素(PH-101),可用作片剂崩解剂。在秸秆微晶纤维素含量为20%时,崩解速度最快。     

激光脉冲编码抗有源干扰效果研究

激光脉冲编码是激光制导武器的抗干扰措施之一。角度欺骗式干扰和高重频干扰是目前半主动激光制导武器的主要有源干扰来源。为研究不同激光脉冲编码方式对激光半主动制导武器抗这两种干扰性能的影响,本文针对敌方激光告警机的识别算法与我方导引头的解码过程,提出自相关函数与归一化互相关函数评价方法,并对目前主要编码方式进行仿真,仿真结果表明:激光脉冲编码的抗角度欺骗式干扰能力受编码序列周期性与脉冲间隔随机性的影响；抗高重频激光干扰能力受编码序列脉冲间隔随机性的影响；LFSR状态码的抗角度欺骗式干扰与抗高重频干扰效果均优于其他编码方式。     

基于振动实测的非均质地层钻头失效分析与对策

四川盆地作为国内页岩气开发的重点区域,通过近几年的不断攻关和实践,机械钻速得到了提高,但由于受地层复杂、可钻性差、非均质性强等地质因素的影响,导致井下钻柱系统不良振动剧烈,容易出现钻头损坏严重、钻速较低等问题,严重影响了钻井时效。为了解决上述难题,以该盆地涪陵工区上二叠统龙潭组—中二叠统茅口组为例,采用井下振动高频测量工具的实测手段,测量了钻头—钻柱系统的动态振动加速度参数,结合地层的岩性和矿物组分分析,研究钻头失效原因与对策,并开展了现场试验。研究结果表明:①在非均质地层中钻进的钻头—钻柱系统产生了大于40 m/s~2的高幅值瞬时冲击振动,高幅值的瞬时冲击是导致钻头先期失效的主要原因;②提出了抑制高幅值的瞬时冲击振动采用"减振+增压"工具组合和避免井下工具共振的钻井参数;③采用钻井新参数的试验井比邻井的高幅值瞬时振动降低了17%,单只钻头进尺增加24%,钻头工作环境得到了较大的改善,钻头使用数量减少。结论认为,该研究成果能够有效地改善钻头—钻柱系统的振动状态,有利于达成延长钻头使用寿命的目标。