Photocatalytic,magnetic, and electrochemical properties of La doped BiFeO3 nanoparticles

We successfully prepared La_1?xBi_xFeO₃ (L_xB_1?xFO, x?=?0.01–0.1) nanoparticles using a sol-gel technique, and studied their photocatalytic, magnetic, and electrochemical properties. Structural refinement studies of the prepared nanoparticles revealed a gradual structural transition from rhombohedral to orthorhombic. The average grain size was observed to decrease with increasing the concentration of La. The photocatalytic degradation of Rhodamine B (RhB) in the presence of the prepared nanoparticles was studied under visible light irradiation. The L_0.06B_0.94FO nanoparticles showed higher degradation efficiency compared to pure BiFeO₃ (BFO) nanoparticles. Magnetic studies showed that La doping improved the magnetization of BFO due to the reduction in grain size and destruction of cycloid coupling of spins. Higher specific capacitance values were obtained for La doped BFO (LBFO) nanoparticles compared to BFO nanoparticles. A maximum specific capacitance of 219?F?g^?1 was obtained at a current density of 1?A?g^?1 for LBFO nanoparticles.     

Turmeric nanofiber-encapsulated natural product formulation act as a phytogenic feed additive—A study in broilers on growth performance,biochemical indices of blood,and E. coli in cecum

A phytogenic feed additive (PFA) formulation was prepared with bioactive molecules—curcuminoids, gingerol, and carvacrol by encapsulating in nanofiber isolated from turmeric spent (turmeric nanofiber, TNF). This formulation was completely characterized by scanning electron microscope, ultra performance liquid chromatography, and gas chromatography and evaluated for its efficacy. PFA-encapsulated TNF (PFA@TNF) considerably increased mean body weight, decreased cholesterol level, mortality rate, and reduced Escherichia coli content of broilers than antibiotic growth promoter (AGP). The depth of crypts in the ileum of broilers was considerably reduced by the inclusion of PFA@TNF in diets compared with the AGP.     

Phase Evolution,Magnetic, Optical,and Dielectric Properties of Zr‐Substituted Bi0.9Gd0.1FeO3 Multiferroics

Polycrystalline BiFeO₃ (BFO) and Bi_0.90Gd_0.10Fe_1?xZr_xO₃ (x = 0.0–0.10; BGFZ_x) ceramics were synthesized by solid‐state reaction method. Rietveld analysis of X‐ray diffraction patterns showed that BFO and BGFZ_x = 0.0 samples are stabilized in rhombohedral structure (space group R3c), whereas a small fraction of orthorhombic phase (space group Pn2₁a) is observed for BGFZ_{x = 0.03–0.10} samples. Suppression and disappearance of some Raman modes indicated a structural phase transition with addition of Zr dopant at Fe site. Magnetic measurements exhibited weak ferromagnetic behavior of BGFZ_x samples with increasing Zr⁺⁴ concentrations. The insertion of Gd⁺³ ions at Bi⁺³ sites and nonmagnetic Zr⁺⁴ ions at Fe⁺³ sites in Fe–O–Fe network suppressed the spin cycloid structure of BFO which in turn enhanced the magnetization of these ceramics. Electron spin resonance spectra revealed the breaking of spin cycloid of BFO due to the development of free spins with addition of Zr⁺⁴ dopants at Fe sites. UV–Visible diffuse reflectance spectra showed one d–d crystal field transition and two charge‐transfer (C–T) transitions along with a sharp absorption of light in visible region for all samples. Almost frequency‐independent dielectric constant and dielectric loss along with very low values of dielectric loss indicated greatly improved dielectric properties for BGFZ_{x = 0.03–0.10} samples.     

ENGAGE compatibilized HDPE/EPDM blends: Modification of some industrially pertinent properties and morphology upon incorporation of Mg(OH)2 filler and electron beam crosslinked network

To observe the effect of ENGAGE (a poly‐olefin elastomer) on compatibilization of industrially important incompatible blend, high‐density polyethylene (HDPE)/ethylene‐propylene diene elastomer (EPDM), 15 wt % ENGAGE is incorporated into the system and the latter is found satisfactorily efficient as compatibilizer for the above system. To improve some industrially pertinent properties another strategies are also followed in addition, incorporation of magnesium hydroxide [Mg(OH)₂] and electron beam (EB) crosslinking into the system. The gel content was found to increase with radiation dose, EPDM content and Mg(OH)₂ dispersion. ENGAGE interestingly increases the gel content that is, promotes crosslinking. It is unique that filler dispersion and crosslinked network formation maintain the compatibility of the ternary system, which is confirmed by X‐ray diffraction, differential scanning calorimetry, mechanical properties, and scanning electron microscope. The compatibilization, Mg(OH)₂ dispersion, and EB crosslinking improve the mechanical, thermo mechanical, flame retardant properties, and phase morphology considerably. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44922.     

Aromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups: synthesis and characterization

A new bisphenol, 1,1-bis-[(4-hydroxyphenyl)-1-(4-phenylsulfonyl)phenyl)]ethane (DPSBP) was synthesized starting from diphenylsulfide and was characterized by spectroscopic methods. DPSBP was polycondensed with isophthalic acid chloride (IPC), terephthalic acid chloride (TPC) and a mixture of IPC and TPC (50:50 mol%) by phase-transfer catalysed interfacial polymerization method to obtain aromatic polyesters containing pendent 4-(phenylsulfonyl)phenyl groups. A series of copolyesters was also obtained by polycondensation of varying molar proportions of DPSBP and bisphenol-A (BPA) with TPC. (Co)polyesters exhibited inherent viscosities in the range 0.56–1.57 dLg^?1 and number average molecular weights (Mn) were in the range 28,650–80,230 g/mol. Polyesters dissolved readily in common organic solvents such as dichloromethane, chloroform, tetrahydrofuran and aprotic polar solvents such as N-methylpyrrolidone, and N,N-dimethylacetamide. Tough, transparent and flexible films of polyesters could be cast from their chloroform solutions. X-Ray diffraction studies indicated amorphous nature of aromatic polyesters. Polyesters showed T_g values in the range 223–257 °C while T₁₀ values were in the range of 469–484 °C indicating their excellent thermal stability.     

Destruction of chlorinated organics by hydrotreatment using Ru/TiO2 catalyst

Catalytic hydrodechlorination reactions of p‐chloro‐m‐cresol (PCMC) and p‐chloroaniline (PCA) were investigated in a slurry reactor using a Ru/TiO₂ catalyst. The organic reaction intermediates, m‐cresol and aniline, were further converted into methylcyclohexanol and cyclohexylamine respectively. Kinetics of PCMC hydrogenation was studied over the ranges in temperature, 323–373 K, H₂ partial pressure, 0.34–1.38 MPa, PCMC concentration, 3.5–14 mM and catalyst loading, 0.1–2 kg/m³. The reaction orders with respect to PCMC and H₂ were evaluated as 0.5 and 0.8 respectively. It was found that aniline hydrogenation is the rate‐determining step in the hydrotreatment of PCA. Kinetics of aniline hydrogenation was studied at 343 and 363 K over the ranges in H₂ partial pressure, 0.34–1.38 MPa, aniline concentration, 5.4–21.5 mM and catalyst loading, 0.1–0.6 kg/m³. The reaction orders with respect to aniline and H₂ were found to be 1.3 and 1.0 respectively. © 2012 Canadian Society for Chemical Engineering     

Exceptionally High Dielectric Constant in Ceramic Pr2CuO4

The pristine layered cuprate Pr₂CuO₄ samples of >95% density were fabricated as thin disks. The samples, analyzed by X‐ray diffraction and Scanning electron microscopy, showed clean T′‐type phase with Rietveld refined lattice parameters a = b = 3.95805(±5) Å and c = 12.2262(±5) Å. The measured dielectric properties of the Pr₂CuO₄ ceramics, in the temperature range ?100°C–150°C and frequencies (ν) 0.1 Hz–1 MHz, showed extremely high ε_r′ > 10⁴ (above ?30°C), and dissipation (tan δ = ε_r′′/ε_r′) between 0.1 and 5 (for 500 Hz ≤ ν ≤ 1 MHz, and ?100 ≤ T ≤ 150°C). The ac conductivity of Pr₂CuO₄ ceramics ranged between 10^?6 and 10^?3 Scm^?1 for the measured frequencies and temperatures, and showed frequency‐dependent double power law behavior akin to a modified Jonscher's power law.     

Bubble columns for condensation at high concentrations of noncondensable gas: Heat‐transfer model and experiments

Carrier gas based thermodynamic cycles are common in water desalination applications. These cycles often require condensation of water vapor out of the carrier gas stream. As the carrier gas is most likely a noncondensable gas present in very high concentrations (60–95%), a large additional resistance to heat transfer is present. It is proposed to reduce the aforementioned thermal resistance by condensing the vapor–gas mixture in a column of cold liquid rather than on a cold surface using a bubble column heat exchanger. A theoretical predictive model for estimating the heat‐transfer rates and new experimental data to validate this model are described. The model is purely physics based without the need for any adjustable parameters, and it is shown to predict heat rates within 0 to ?20% of the experimental values. The experiments demonstrate that heat‐transfer rates in the proposed device are up to an order magnitude higher than those achieved in existing state‐of‐the‐art dehumidifiers. © 2012 American Institute of Chemical Engineers AIChE J, 59: 1780–1790, 2013