应用硫酸铵提高乌拉嗄金矿石浮选回收率试验研究

经试验发现应用一种化学肥料硫酸铵可以显著提高乌拉嘎金矿石的浮选回收率。闭路试验尾矿工艺矿物学鉴定证明，以硫酸铵作为调整剂的浮选过程中，微细粒单体金和金与石英边生体被有效回收。     

OSEK/VDX——汽车电子系统的开放式平台

介绍了当前在国际汽车工业界日益占据主导地位的汽车电子系统开放式平台--OSEK/VDX体系.详细地论述了这种体系的由来、运行机制和最新的发展动向,以及它对汽车电子技术发展的深远影响.     

高分辨率电阻率测井仪在薄层评价中的应用

传统的测井仪器无法克服纵向分辨率和径向探测深度这一矛盾，高分辨率电阻率测井仪（HDRT）测量精度好、探测深度大且垂向分辨率高，能够准确识别薄互层、评价薄油气层，准确记录油层厚度，可为精细描述油气田地下地质状态提供更多依据。     

皮革去污上光用乳化蜡的研制

采用石蜡、微晶蜡为主要原料 ,经实验选出了以水为稀释剂的乳化型皮革去污上光蜡。实验优化的配方为石蜡 12 .5 g ,微晶蜡 8.0 g ,硬脂酸 8.5g ,三乙醇胺 5 .5 g ,水量 70 (涂用 )或 130 g(喷用 )。反应条件为乳化时间 4 0min ,搅拌速度 5 0 0～ 70 0r/min ,乳化温度 90℃。制得上光剂产品的去污性能可与用去污剂单独处理的效果相当 ,亮度可达 6 6 .7。     

A new family of yeast genes implicated in ergosterol synthesis is related to the human oxysterol binding protein

We have identified three yeast genes, KES1, HES1 and OSH1, whose products show homology to the human oxysterol binding protein (OSBP). Mutations in these genes resulted in pleiotropic sterol-related phenotypes. These include tryptophan-transport defects and nystatin resistance, shown by double and triple mutants. In addition, mutant combinations showed small but apparently cumulative reductions in membrane ergosterol levels. The three yeast genes are also functionally related as overexpression of HES1 or KES1 alleviated the tryptophan-transport defect in kes1Δ or osh1Δ mutants, respectively. Our study implicates this new yeast gene family in ergosterol synthesis and provides comparative evidence of a role for human OSBP in cholesterol synthesis.     

电容检测纱线传感器转换特性对纱线不匀率测试的影响

讨论了纱线测试中受电容检测纱线传感器转换特性的非线性影响，测得的条干不匀率值与纱线的实际条干不匀率值之间的差异，从理论上估计了纱线在不同的电容检测槽内测试时，由于其截面充满系数不同而引起的相对差异，并用试验数据加以验证。     

Ti-23Al-14Nb-3V合金氩弧焊接头的显微组织及其力学性能

研究了预热对Ｔｉ－２３Ａｌ－１４Ｎｂ－３Ｖ合金焊接性，特别是对消除氩弧焊冷裂纹的作用以及对接头显微组织和力学性能的影响。结果表明，焊前预热可有效降低该合金的冷裂倾向。经预热处理后，焊缝区的结晶层状线消失，热影响区的硬度峰得到缓和，整个焊缝的显微硬度分布趋于均匀，但焊缝区的枝晶发生粗化，热影响区有所扩大。焊件接头的拉伸试验表明，预热可使焊缝区的接头强度系数增加，但无论预热与否，接头强度均低于母材强度，且不显示宏观塑性。     

Preparation and characterization of polyurethane microcapsules containing n‐octadecane with styrene‐maleic anhydride as a surfactant by interfacial polycondensation

A series of polyurethane microcapsules containing a phase change material (PCM) of n‐octadecane was successfully synthesized by an interfacial polymerization in aqueous styrene‐maleic anhydride (SMA) dispersion with diethylene triamine (DETA) as a chain extender reacting with toluene‐2,4‐diisocyanate (TDI). The average diameter of microPCMs is in the range of 5–10 μm under the stirring speed of 3000–4000 rpm. Optical and SEM morphologies of microPCMs had ensured that the shell was regularly fabricated with the influence of SMA. FTIR results confirmed that the shell material was polyurethane and the SMA chains associated on core material reacted with TDI forming a part of shell material. The shell thickness was decreasing in the range of 0.31–0.55 μm with the molar ratio of DETA/TDI from 0.84 to 1.35 and the weight of core material increasing from 40 to 80% (wt %). By controlling the weight ratio of PCM as 40, 50, 60, 70, and 80% in microPCMs, it was found using DSC that the T_m and T_c of microPCMs were in the range of 29.8–31.0^oC and 21.1–22.0°C and an obvious phase change had been achieved nearly the same temperature range of that of PCM. The results from release curves of microPCM samples prepared by 1.4, 1.7, and 2.0 g of SMA indicated the release properties were affected by the amount of the dispersant, which attributed to the emulsion effect and shell polymerization structure. The above results suggest that the shell structure of microPCMs can be controlled and the properties of microPCMs determined by shell will perform proper practical usage. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4996–5006, 2006