Surface Analysis of Cr2O3‐, CoO‐, and Al2O3‐Doped Iron–Phosphate Glasses at High Temperature

Surface structures of iron–phosphate glasses were examined using X‐ray photoelectron spectroscopy (XPS). Cr₂O₃, CoO, and Al₂O₃ were introduced to the glass by the replacement of a part of Fe₂O₃, and the simulated fission products are also added. The obtained glasses showed high chemical durabilities by MCC‐1 test. In situ high‐temperature and room‐temperature XPS measurements were conducted on the polished sample surfaces and also those after 1‐week chemical durability test. Unique trends were observed in XPS spectra on heating and after the chemical durability test, respectively. Nature of the glass surface of iron–phosphate glasses was explained from the point of view of surface energy, and the origin of high chemical durability and the effect of chromium ions were discussed based on the changes on surface composition and valence states of transition‐metal ions.     

Morphology and crystallization behavior of nylon 6‐clay/neat nylon 6 bicomponent nanocomposite fibers

Nylon 6‐clay hybrid/neat nylon 6, sheath/core bicomponent nanocomposite fibers containing 4 wt % of clay in sheath section, were melt spun at different take‐up speeds. Their molecular orientation and crystalline structure were compared to those of neat nylon 6 fibers. Moreover, the morphology of the bicomponent fibers and dispersion of clay within the fibers were analyzed using scanning electron microscopy and transmission electron microscopy (TEM), respectively. Birefringence measurements showed that the orientation development in sheath part was reasonably high while core part showed negligibly low birefringence. Results of differential scanning calorimetry showed that crystallinity of bicomponent fibers was lower than that of neat nylon 6 fibers. The peaks of γ‐crystalline form were observed in the wide‐angle X‐ray diffraction of bicomponent and neat nylon 6 fibers in the whole take‐up speed, while α‐crystalline form started to appear at high speeds in bicomponent fibers. TEM micrographs revealed that the clay platelets were individually and evenly dispersed in the nylon 6 matrix. The neat nylon 6 fibers had a smooth surface while striped pattern was observed on the surface of bicomponent fibers containing clay. This was speculated to be due to thermal shrinkage of the core part after solidification of the sheath part in the spin‐line. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2014 , 131, 39996.     

Preparation of CaCO3‐based biomineralized polyvinylpyrrolidone–carboxymethylcellulose hydrogels and their viscoelastic behavior

In the blend of natural and synthetic polymer‐based biomaterial of polyvinylpyrrolidone (PVP) and carboxymethylcellulose (CMC), fabrication of CaCO₃ was successfully accomplished using simple liquid diffusion technique. The present study emphasizes the biomimetic mineralization in PVP–CMC hydrogel, and furthermore, several properties of this regenerated and functionalized hydrogel membranes were investigated. The physical properties were studied and confirmed the presence of CaCO₃ mineral in hydrogel by Fourier transform infrared spectroscopy and Scanning electron microscopy. Moreover, the absorptivity of water and mineral by PVP–CMC hydrogel was studied to determine its absorption capacity. Further, the viscoelastic properties (storage modulus, loss modulus, and complex viscosity) of mineralized and swelled samples (time: 5–150 min) were measured against angular frequency. It is interesting to know the increase of elastic nature of mineralized hydrogel filled with CaCO₃ maintaining the correlation between elastic property and viscous one of pure hydrogel. All these properties of biomineralized hydrogel suggest its application in biomedical field, like bone treatment, bone tissue regeneration, dental plaque and tissue replacement, etc. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40237.     

The correlation between the ionic degree of covalent bond comprising polymer main chain and the ionic yield due to mechanical fracture

The mechanical force to polymeric materials in vacuum at 77 K produces mechano radicals, mechano anions and mechano cations due to homogeneous and heterogeneous scissions of the covalent bonds comprising polymer main chain. The ionic degree of the covalent bond was estimated by calculating the “absolute ΔMulliken atomic charge,” which was defined as the difference between the Mulliken atomic charges of the two adjacent atoms comprising the covalent bond of the polymer main chain. The ionic yield of the covalent bond increased with increasing the absolute ΔMulliken atomic charge. The empirical formula for the ionic yield was obtained with the absolute ΔMulliken atomic charge, and indicates that the ionic yield could be estimated from its chemical structure.     

Vitamin E reduces cholesterol esterification and uptake of acetylated low density lipoprotein in macrophages

The effects of vitamin E on cholesteryl ester (CE) metabolism in 1774 cells were examined. Pretreatment of 1774 cells with vitamin E at concentrations above 50 μM significantly decreased acetylated low density lipoprotein (LDL)-induced incorporation of [¹⁴C]oleate into CF in cells in a dose-dependent manner. This was partly due to vitamin E Also significantly inhibiting the uptake of [³H]CE-labeled acetylated LDL by 1774 cells. A trend existed toward suppression of acyl-CoA:cholesterol acyltransferase (ACAT) activity in the cell lysate at high vitamin E concentration, but there was no effect on hydrolysis of CE. These data indicate that vitamin E reduces the uptake of modified LDL and suppresses ACAT activity, resulting in less cholesterol esterification in macrophages; a novel mechanism underlying the antiatherogenic properties of vitamin E.     

Fabrication of Functionally Graded SiO2‐Mo Material by Centrifugation and Floc‐Casting of Highly Concentrated Slurry

To fabricate functionally graded materials, a highly concentrated slurry of SiO₂‐Mo system was prepared and centrifugal force was applied in an attempt to achieve a graded composition. Subsequently, we formed a homogeneous green body with compositional gradation by floc‐casting at 80°C, which was then fired at 1750°C for 10 min in Ar. The sintered body had compositional ratios of SiO₂ and Mo as well as electrical conductivities that changed gradually along the direction of centrifugal force. The results demonstrate that centrifugation and control of slurry characteristics such as flocculation are effective in fabricating functionally graded SiO₂‐Mo materials.     

Ca-α SiAlON hollow spheres prepared by carbothermal reduction–nitridation from different SiO2 powders

The formation process of hollow spheres composed of nanosized Ca-α SiAlON particles was investigated using SiO₂ starting powders with different characteristics in particle size, shape and crystalline state. TEM observations showed Ca-α SiAlON hollow spheres composed of a large number of nanosized particles in the products prepared at 1450 °C for 120 min in nitrogen. In all systems, the Ca-α SiAlON hollow spheres were always produced through an intermediate Si–Al–Ca–O liquid phase in the same mechanism, regardless of the characteristics of SiO₂ starting powders used. Spherical solid particles consisted of amorphous phase containing Si, Al, Ca, O and a small amount of N were generated at the initial stage of carbothermal reduction–nitridation. These spherical solid particles changed into hollow particles with the progression of the reaction from the liquid phase to the crystalline Ca-α SiAlON with increasing temperature.     

Stereocomplex crystallization and spherulite growth behavior of poly(l-lactide)-b-poly(d-lactide) stereodiblock copolymers

The non-isothermally and isothermally crystallized stereodiblock copolymers of poly(l-lactide) (PLLA) and poly(d-lactide) (PDLA) with equimolar l-lactyl and d-lactyl units and different number-average molecular weights (M_n) of 3.9 × 10³, 9.3 × 10³, and 1.1 × 10⁴ g mol⁻¹, which are abbreviated as PLLA-b-PDLA copolymers, contained only stereocomplex crystallites as crystalline species, causing higher melting temperatures of the PLLA-b-PDLA copolymers compared to those of PLLA homopolymers. In the case of non-isothermal crystallization, the cold crystallization temperatures of the PLLA-b-PDLA copolymers during heating and cooling were respectively lower and higher than those of PLLA homopolymers, indicating accelerated crystallization of PLLA-b-PDLA copolymers. In the case of isothermal crystallization, in the crystallizable temperature range, the crystallinity (X_c) values of the PLLA-b-PDLA copolymers were lower than those of the PLLA homopolymers, and were susceptible to the effect of crystallization temperature in contrast to that of homopolymers. The radial growth rate of the spherulites (G) of the PLLA-b-PDLA copolymers was the highest at the middle M_n of 9.3 × 10³ g mol⁻¹. This trend is different from that of the PLLA homopolymers where the G values increased monotonically with a decrease in M_n, but seems to be caused by the upper critical M_n values of PLLA and PDLA chains as in the case of PLLA/PDLA blends (in other papers), above which homo-crystallites are formed in addition to stereocomplex crystallites. The disturbed crystallization of PLLA-b-PDLA copolymers compared to that of the PLLA/PDLA blend is attributable to the segmental connection between the PLLA and PDLA chains, which interrupted the free movement of those chains of the PLLA-b-PDLA copolymers during crystallization. The crystallite growth mechanism of the PLLA-b-PDLA copolymers was different from that of the PLLA/PDLA blend.     

Solubility of NiO in Al2O3

Solubility of NiO in Al₂O₃ was determined by electron probe microanalysisy A diffusion couple method was used by coupling an NiO-doped Al₂O₃ polycrystal to a pure single crystal of Al₂O₃. The solubility of NiO in Al₂O₃ in air was 230 wt ppm (157 at. ppm of cations) and 170 wt ppm (116 at. ppm) at 2073 and 1973 K, respectively. The solubility of NiO in Al₂O₃ obtained in this work was compared with our previous work of the solubility of MgO in Al₂o₃.