UV curable lens production using molecular weight controlled PEEK based acrylic oligomer (Ac-PEEK)

We produced UV curable lenses with properties blocking short wave UV light. In the UV-curable formulations, we used an oligomer (Ac-PEEK) with another urethan oligomer (Mw = 2000). Radically active, molecular weight controlled Ac-PEEK was obtained by reacting 2-hydroxyl ethyl methacrylate with molecular- weight- controlled and isocyanate terminated PEEK (Mn = 4500). We characterized all synthesized monomer, oligomer and optical materials with UV/Vis spectrophotometer with interferogram, elemental analyser, mass spectrophotometer, proton nuclear magnetic resonance, Fourier transform infrared spectroscopy, thermal gravimetric analyzer, differential scanning calorimeter, scanning electron microscopy and gas chromatography. Results suggested that newly synthesized oligomer with the structure of PEEK absorbs short wave UV-light. Ageing tests [ISO 11979-5, Ophthalmic implants—intraocular lenses (IOL)—Part 5: Biocompatibility] performed on the IOL materials were successful. High contact angle of the obtained lenses suggests that all lenses were hydrophobic and SEM results revealed that lenses are morphologically homogeneous. Based on all positive properties just mentioned, we safely conclude that the lenses produced in this study are very promising for IOL production.     

Investigation of current‐voltage characteristics and current conduction mechanisms in composites of polyvinyl alcohol and bismuth oxide

Temperature dependent current‐voltage (I–V) measurements of Au/Polyvinyl Alcohol + Bi₂O₃/n‐Si structure were conducted between 100 and 350 K for investigating the temperature dependence of I–V characteristics and current conduction mechanisms in the structure. Series resistance of the structure is calculated using Ohm's law and Cheungs' method. Ideality factor (n) and zero‐bias barrier height (Φ_Bo) were obtained considering thermionic emission theory. From 100 to 350 K, n changed from 32.1 to 3.54, and Φ_Bo changed from 0.27 to 0.99 eV. Obtained temperature dependent values of n and Φ_Bo suggested that thermionic emission is not the dominant current conduction mechanism. Therefore, Ln(I)–Ln(V) curves of the studied structure were plotted for investigating current conduction mechanisms in the structure and current flow is explained considering space charge limited current. Moreover, density of interface states (D_it) in the structure were calculated and its temperature dependence was investigated such that D_it values are reduced to the order of ～10¹³ eV^?1 cm^?2 from ～10¹⁴ eV^?1 cm^?2 with increasing temperature. POLYM. ENG. SCI., 54:1811–1816, 2014. © 2013 Society of Plastics Engineers     

Poly(azomethine-imide)s containing siloxane moities: Optical,thermal, mechanical,and morphological properties

A new series of poly(azomethine-imide)s having siloxane moities in backbone was prepared using different dianhydrides.Thermal, optical, and morphological properties of these polymers were clarified. Also, bulky  CO and  CF₃ group effects and meta or para-substituted aldeyhde effects on the mentioned properties were evaluated. The structural characterization of poly(azomethine-imide)s was carried out using a FT-IR spectroscopy. The optical properties of the polymers were performed via an UV–Vis spectrophotometer. Optical band gap of the poly(imide)s containing azomethine was calculated between 2.20 and 2.33 eV. Thermal behavior of poly(azomethine-imide)s was also studied using TG-DTA, DSC, and DMA techniques. The onset degradation temperature and percentage char values of the polyimides were found in the range from 429 to 545 °C and 22 to 35%, respectively. Thermal stability results demonstrated that benzophenone bearing poly(azomethine-imide)s have higher onset temperature, percentage char, and the glass transition temperature than poly(azomethine-imide)s derived from hexafluoroisopropylidene. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48364.     

The Effects of Heat Treatment on Some Mechanical Properties of Juvenile Wood and Mature Wood of Eucalyptus grandis

Heat treatment is a well-known method for modifying wood that is applied in different ways, and treatment schedules change from tree to tree. This treatment improves the physical properties of wood but, in general, it reduces the mechanical properties of wood. The effects of heat treatment on the mechanical properties of juvenile and mature wood of the same tree species have not been well-defined. Therefore, we focused our study on the differences in the mechanical properties of juvenile wood and mature wood of Eucalyptus grandis after both were subjected to heat treatment. Wood samples were treated at temperatures of 120, 150, and 180°C for 4, 6, and 8 h. The test results showed that decreases in the mechanical properties of juvenile wood (e.g., modulus of elasticity (MOE), modulus of rupture (MOR), compression strength (CS), and impact bending (IB)) were greater than the decreases that occurred in mature wood that was heat treated at the same conditions.     

Competitive adsorption of uranyl ions in the presence of Pb(II) and Cd(II) ions by poly(glycidyl methacrylate) microbeads carrying amidoxime groups and polarographic determination

The adsorption capacity of UO in the presence of Pb(II) and Cd(II) ions was investigated with amidoximated poly(glycidyl methacrylate) (PGMA) microbeads with an average size of 135 μm packed in a glass column (0.5‐cm i.d. and 20‐cm length, flow rate = 3 mL/min) under competitive conditions. A differential pulse polarography technique was used for the determination of trace quantities of uptaken elements by the measurement of the reduction peak currents at ?200/?950, ?400, and ?600 mV (vs a saturated calomel electrode) for UO, Pb(II), and Cd(II) ions, respectively. When only UO was found in the eluate, its adsorption was 85.3% from a 50 μM initial solution. However, when there was UO with binary systems of Pb(II) or Cd(II), it was 78.2 and 76.3%, respectively. On the other hand, in a ternary mixture of UO with Pb(II) and Cd(II), the adsorption was found to be 75.2% with the same initial concentration. According to the results, the competitive adsorption studies showed that these amidoximated PGMA microbeads had good adsorption selectivity for UO with the coexistence of Pb(II) and Cd(II) ions. The ionic strength of the solution also influenced the UO adsorption capacity of the amidoximated PGMA microbeads. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 4168–4172, 2007     

Effects of use of higher strength interlayer and external cooling on properties of friction stir welded AA6061-T6 joints

Although sound AA6061-T6 joints can be produced by friction stir welding, a loss in strength takes place in the weld region. In this study, it was demonstrated that the strength of the nugget could be increased by the use of a higher strength interlayer during friction stir welding. This strength recovery cannot, however, be attainable in the heat affected zone. Although an external cooling was applied during welding in order to increase strength in the heat affected zone, it was not sufficient for achieving the required cooling condition for improved strength.     

Infrared drying of button mushroom slices

The effect of different infrared power levels on the drying kinetics of button mushrooms was investigated. Mushroom slices were dried at infrared power levels of 83, 125, 167, and 209 W. The power level affected the drying and rehydration characteristics of mushroom slices. Drying time was reduced from 300 min to 40 min as the infrared power level increased from 83 to 209W. Mathematical models frequently used to represent drying of agricultural products were fitted to experimental data of mushroom drying. The parabolic model was the best for representation of mushroom drying. Effective moisture diffusivity varied from 3.81×10^?10 to 4.20×10^?9 m²/s over the infrared power levels used. The activation energy was estimated using a modified Arrhenius-type equation and calculated to be 7.55 kW/kg.     

Properties of pumice aggregate concretes at elevated temperatures and comparison with ANN models

The mechanical properties and thermal conductivity of concretes including pumice aggregate (PA) exposed to elevated temperature were analyzed by thermal conductivity, compressive strength, flexure strength, dynamic elasticity modulus (DEM) and dry unit weight tests. PA concrete specimens were cast by replacing a varying part of the normal aggregate (0–2 mm) with the PA. All concrete samples were prepared and cured at 23 ± 10C lime saturated water for 28 days. Compressive strength of concretes including PA decreased that reductions were 14, 19, 25 and 34% for 25, 50, 75 and 100% PA, respectively. The maximum thermal conductivity of 1.9382 W/mK was observed with the control samples containing normal aggregate. The tests were carried out by subjecting the samples to a temperature of 0, 100, 200, 300, 400 500, 600 and 700 °C for 3 h, then cooling by air cooling or in water method. The results indicated that all concretes exposed to a temperature of 500 and 700 °C occurred a significant decrease in thermal conductivity, compressive strength, flexure strength and DEM. An artificial neural network (ANN) approach was used to model the thermal and mechanical properties of PA concretes. The predicted values of the ANN were in accordance with the experimental data. The results indicate that the model can predict the concrete properties after elevated temperatures with adequate accuracy. Copyright © 2016 John Wiley & Sons, Ltd.     

Anaerobic digestion of Aegean olive mill effluents with and without pretreatment

BACKGROUND: Olive oil production is an important economical activity in the Aegean region of Turkey. However, the effluents of the olive oil producing mills with their high organic loads and toxic compounds are causing serious environmental problems. The anaerobic biological treatment of olive mill wastewater (OMWW) using the treatment plants of the regional industries could be a method of choice and within the scope of this study floccular and granular sludges were investigated in batch mode for their success in the treatment of OMWW while producing biogas. The major limitation of this treatment is the inhibition of methanogenic bacteria by the phenolic compounds in OMWW. Thus an integrated solution was suggested in which a pre‐treatment step (dephenolization) was also introduced before biological step. RESULTS: The effluents of 27 olive mills out of 47 were found to have total phenolics (TP) less than 3 g L^?1 and could be treated anaerobically after simple dilution. The biogas production for the untreated OMWW was higher for floccular sludge than for the granular sludge (68.5 mL and 45.7 mL respectively). Combined pre‐treatment experiments, first coagulation with polyaluminum chloride, followed by flocculation with cationic polyelectrolyte and finally Fenton's oxidation, could remove 80% of TP and 95% of the total suspended solids. CONCLUSION: OMWW having TP values less than 3 g L^?1 can be treated anaerobically using floccular sludge after simple dilution and biogas can be produced. For OMWW samples having higher TP values pre‐treatment is necessary and the pre‐treatment given in this study may be used effectively. Copyright © 2010 Society of Chemical Industry