Preparation and electrochemical performance of nanosized Co3O4 via hydrothermal method

The hydrotalcite-type cobalt compounds were prepared through oxidation of Co（OH）2 gel using NH4OH as precipitating agent and H2O2 as oxidant. These hydrotalcite-type cobalt compounds were transformed into Co3O4 through hydrothermal decomposition with nanostructural deformation. The precursor and product were characterized by Fourier-transform infrared（FT-IR） spectrum, X-ray diffractometry（XRD） and transmission electron microscopy（TEM）. The electrochemical performances of as-prepared nanosized Co3O4 as anode materials in lithium-ion batteries were tested by charge-discharge test in the voltage range of 0-3.0 V. The influence of morphology of Co3O4 particle on the capacity and cycling performance was studied. The results show that the shape and size of the final product can be controlled by altering cobalt sources. The irregular cubic Co3O4 with the average particle size of about 10 nm shows the best electrochemical performance. After 10 charge-discharge cycles, the specific charge capacity retains 555 mA.h/g.     

A novel arc welding inverter with unit power factor based on DSP control

A novel inverter power source is developed characterized with constant output current and unit power factor input. Digital signal processor （ DSP ） is used to realize power factor correction and control of back-stage inverter bridge of the arc welding inverter. The fore-stage adopts double closed loop proportion and integration （PI） rectifier technique and the back- stage adopts digital pulse width modulation （ PWM） technique. Simulated waves can be obtained in Matlab/Simulink and validated by experiments. Experiments of the prototype showed that the total harmonic distortion （THD） can be controlled within 10% and the power factor is approximate to 1.     

树脂自硬砂型对球铁件表面组织的影响

研究了用对甲苯磺酸和磷酸作固化剂的树脂自硬砂型对球铁件表面组织的影响；结果表明，用对甲苯磺酸作固化剂的树脂砂型生产球铁件时，会在铸件表面出现片状石墨层；用磷酸作固化剂的树脂砂型生产球铁件时，当磷酸加入量过多或旧砂反复使用时，会在铸件表面出现磷共晶组织。     

铝锡合金摩擦磨损性能的研究

研究了含锡量3%～30%铝锡合金的摩擦磨损性能,结果表明:随着含锡量的增加,铝锡合金的承载能力下降,摩擦系数下降.该合金的显微组织为硬的铝锡固溶体基体上分布着软的锡相质点.常温下含锡量在9%时,合金具有优良的耐磨减摩的综合性能.     

液压系统设计与试验的虚拟样机技术

本文在介绍了虚拟样机技术的基础上，分析和阐述了开发具有虚拟样机功能的液压系统设计与试验软件的模型。     

Zn-Al系二元相图的研究

利用高温X射线衍射法（XRD）、示差扫描量热分析法（DSC）、热膨胀法（PRD）等方法重新测定Zn-Al二元体系相图。在XRD曲线图中β（ZnAl）相的存在，表明存在β（ZnAl）固溶单相区；DSC曲线图表明在274～279℃范围内存在共析相变反应；PRD曲线图表明在340℃不存在相变反应。综合XRD、DSC和PRD结果，绘制了部分Zn-Al二元体系相图，为高铝锌基合金的实际相变应用提供参考。     

PCD用钎料及钎焊工艺的研究

PCD的广泛应用给钎焊技术提出了更高的技术要求，常规钎料已不能满足高疲劳，高温抗剪的要求，根据Ag,Cu,Zn,Cd,Ni,Co,Mn等元素在钎料中的作用和特点，进行分析和选择从而配制了十几种牌号的钎料，并对其熔点，强度，钎焊工艺进行了研究，研制出一系列新型的银基钎料，研究和使用结果表明，研制的系列钎料分别适宜不同工作条件下的PCD工具的钎焊。     

弯曲晶界对10Cr-15Co-Ni基变形高温合金蠕变断裂的影响

应用两种热处理制度分别获得弯曲晶界和平直晶界,研究两种晶界状态对10Cr-15Co-Ni基变形高温合金蠕变断裂过程的影响,重点探讨弯曲晶界改善合金热强性原因。研究表明,弯曲晶界对裂纹的萌生、长大及扩展,对裂纹的形态及断裂方式,都有显著的影响。弯曲晶界能有力地阻止晶界滑动及推迟裂纹连接,使晶内参与更多的变形,弯晶的主要作用体现在蠕变第三阶段。合金经弯晶处理后蠕变断裂寿命提高26％。     

热喷涂类硬质合金涂层的组织与性能

热喷涂工艺是制取抗磨损类硬质合金涂层的一种重要的表面技术，含Ｃｏ或Ｎｉ（通常与Ｃｒ制成预合金）粘结剂的ＷＣ和Ｃｒ３Ｃ２－ＮｉＣｒ合金是这类技术最通用的材质体系，涂层的组织与性能强烈依赖于成份，喷涂粉制取技术和喷涂工艺参数。硬质合金应用于切削和涂层时的使用完全不同，因此，在研制用于涂层的新型硬质合金体系时必须考虑到它的特殊工艺和使用条件。