Features of phase transitions in electrolyzer hearth block material between joints

Phase transitions are considered for silicon oxycarbide material between joints in hearth blocks under aluminum electrolyzer operating conditions. It is established that in the electrolyzer there is formation of aluminum subcarbide, and also there is conversion of silicon carbide polytypes as a result of impurities of aluminum, sodium, magnesium, copper and iron. Due to phase transitions there is a reduction in joint strength, and therefore it is undesirable to use material based on corundum and black silicon carbide in hearth joints between blocks for aluminum electrolyzers. Use of pure α-SiO₂ free from impurities is recommended for this purpose. Translated from Novye Ogneupory, No. 4, pp. 47–52, April 2008.     

Synthesis of nanocrystalline solid solutions based on zirconia and hafnia

Nanosized (2–8 nm) amorphous powders of the solid solution based on zirconia and hafnia are synthesized through back coprecipitation upon treatment of gels at temperatures from +20 to −77°C. Heat treatment of these powders at temperatures up to 1000 and above 1100°C leads to the formation of cubic (fluorite type, O _h ⁵ = Fm3m) and tetragonal phases of the Zr₈₂Hf₁₀Y₃Ce₅O _x composition, respectively. It is revealed that a decrease in the synthesis temperature (from +20°C to −6°C) results in a decrease in the size of gel agglomerates from 30 to 1 μm. Recrystallization processes in the gels prepared using cryochemical treatment are developed very slowly in the temperature range 500–1200°C (the crystallite size does not exceed 25 nm). Original Russian Text ? T.I. Panova, V.B. Glushkova, A.E. Lapshin, 2008, published in Fizika i Khimiya Stekla.     

Dynamic modes of Ti combustion in a coflow of N<Subscript>2</Subscript>-Ar mixture

Combustion of bulk density Ti powder (containing 20 wt % TiN as a diluent) in a coflow of N₂-Ar mixture was investigated upon variation in the nitrogen content of the gaseous mixture. The obtained data are believed to open up new horizons for fabrication of layered and composite ceramics by infiltration-mediated combustion.      

A fragmentary model of vitreous As<Subscript>2</Subscript>S<Subscript>3</Subscript>

The X-ray scattering intensity curves for vitreous As₂S₃ are experimentally measured using soft (copper) and hard (molybdenum) X rays. The inclusion of all the specific features revealed in the experimental scattering intensity curves makes it possible to obtain the experimental atomic radial distribution function (ARDF) in the ordering range up to ～1 nm. The experimental ARDF is interpreted in the framework of the fragmentary model. A comparison of the experimental ARDF with the model ARDF calculated from the crystal structure data obtained for orpiment demonstrates that the corrugated layers inherent in crystalline As₂S₃ are retained in the glass structure but the characteristic interlayer interatomic distances are absent. The layers are joined together through the As₄S₅ molecular clusters. Microcrystals consisting of several unit cells are absent in the glass structure, which involves only the structural fragments of both crystalline analogs. One of the possible variants of their joining is proposed.     

Reproducibility of plastic measurements: The need to modify State Standard GOST 1186-87

A very important characteristic of coking coal is its clinkering ability, i.e., its ability to form a nonvolatile solid residue, consisting of disparate grains, on heating in specific conditions. The clinkering ability of the coal is determined by the properties of its plastic mass. Various methods may be used to evaluate the plastic-ductile properties of the coal. However, since the 1930s, the main method used to evaluate the clinkering properties of coal, within the nations of the former Soviet Union, has been the Sapozhnikov-Bazilevich plastometric method, because it provides more information than competing approaches. For the same reason, the thickness of the plastic layer, which is one of the parameters determined by this method, is used for coal classification in State Standard GOST 25543-88 (Lignite, Coal, and Anthracite: Genetic and TEchnological Classification) and its Ukrainian counterpart DSTU 3472-96 (Lignite, Coal, and Anthracite: Classification). This explains the strict requirements on the accuracy and reliability of the plastometric characteristics.     

Swift and Selective Reduction of Nitroaromatics to Aromatic Amines with Ni–Boride–Silica Catalysts System at Low Temperature

Various nitroaromatics are successfully reduced to amines with 100% conversion and selectivity in methanol at low temperature (≈5 °C), by using versatile system of 5% Ni–SiO₂ catalyst and NaBH₄ and in situ generation of Ni boride. The catalytic efficiency of Ni loading (5%, 10% and 15%) with silica or titania as support materials is investigated for reduction of nitrobenzene. The Ni–titania/NaBH₄ system recorded lower conversion and selectivity. The IR studies indicate that silica support does not have free –OH group on its surface. Thus the nickel boride is anchored to the silica to facilitate the catalytic process.     

Robustness of classification rules that incorporate additional information

The discrimination problem for two normal populations with the same covariance matrix when additional information on the population is available is considered. A study of the robustness properties against training sample contamination of classification rules that incorporate this additional information is performed. These rules have received recently attention where their total misclassification probability (TMP) is proved to be lower than Fisher's linear discriminant rule. The results of a simulation study on the TMP which compares the behaviour of the new rules against Fisher's rule and some of its robustified versions under different types of contamination are presented. These results show that the rules that incorporate the additional information not only have lower TMP, but they also prevent against some types of contamination. In order to achieve prevention from all types of contamination a robustifed version of these rules is recommended.     

Elimination of organic matter present in wastewaters from the cork industry by membrane filtration

BACKGROUND: The first stage of the cork industrial process generates great volumes of wastewater with moderate to high organic pollutant content that must be purified using different procedures, such as filtration by membranes. RESULTS: The tangential filtration of these wastewaters was studied using two different laboratory equipments. In the first one, three ultrafiltration (UF) membranes were tested, with molecular weight cut‐off (MWCO) 100 kDa and 30 kDa, and two operating modes were used: total recycling of permeate and retentate streams, and in continuous mode, without recycling both streams. In the total recycling UF experiments, the influence of the operating variables on the permeate flux was first established. The effectiveness of the different membranes was determined by evaluating the rejection coefficients for several parameters that measure the global pollutant content of the effluent. The values found for these rejection coefficients were in the following order: ellagic acid and color > absorbance at 254 nm > tannic content > COD (chemical oxygen demand). In the continuous mode experiments, the fouling mechanism for each membrane was established by fitting the experimental data to various filtration fouling models given in the literature. The operating mode in the second equipment was batch concentration, and additional experiments were carried out with an UF membrane (2 kDa), and with a NF membrane (with MWCO in the range 150–300 Da). CONCLUSIONS: The three operating modes tested provided different rejection levels of organic matter; among them, the most effective procedure tested was batch concentration mode using a NF membrane. Copyright © 2007 Society of Chemical Industry