Effects of annealing at high pressure on structure and mechanical properties of Al87Ni7Gd6 metallic glass

The effects of annealing and annealing with a superimposed pressure of 940 MPa on the primary crystallization behaviour of α-Al and the resulting micro-hardness have been studied for as-quenched Al₈₇Ni₇Gd₆ metallic glass. Isothermal annealing experiments were conducted for 30 min at 188 °C, 191 °C, and 205 °C in silicone oil maintained either at atmospheric pressure (i.e. 0.1 MPa) or at 940 MPa. XRD analyses detected the evolution of structure with annealing at 0.1 MPa, while specimens annealed with 940 MPa pressure exhibited sharper diffraction peaks than those annealed at 0.1 MPa. DSC measurements were conducted on the as-received amorphous ribbons as well as ribbons annealed at different temperatures at either 0.1. MPa or with 940 MPa superimposed pressure. Specimens annealed with 940 MPa pressure exhibited higher onset temperatures (i.e. T_x1) and temperatures for the first exothermic peak (i.e. T_p1) for primary crystallization. TEM measurements revealed an increase in the volume fraction of α-Al with increases in annealing temperature, while micro-hardness measurements revealed an increase in hardness with increasing amounts of α-Al. Specimens annealed with 940 MPa pressure exhibited further increases in both the volume fraction of α-Al and resulting micro-hardness.     

MECHANISM OF NON-EQUILIBRIUM SEGREGATION OF SOLUTE TO GRAIN BOUNDARIES

本文以空位-溶质原子拖曳机制为基础,并考虑了空位、溶质原子和复合体三者的反应平衡及晶界平衡偏聚的作用,得到了溶质原子的非平衡晶界偏聚动力学方程。对硼在奥氏体中等温及连续冷却时所产生的非平衡晶界偏聚现象进行了理论计算,得到了与实验较为一致的结果。     

Stability of nonlinear 2D systems described by the continuous-time Roesser model

This paper considers systems with two-dimensional dynamics (2D systems) described by the continuous-time nonlinear state-space Roesser model. The sufficient conditions of exponential stability in terms of vector Lyapunov functions are established. These conditions are then applied to analysis of the absolute stability of a certain class of systems comprising a linear continuous-time plant in the form of the Roesser model with a nonlinear characteristic in the feedback loop, which satisfies quadratic constraints. The absolute stability conditions are reduced to computable expressions in the form of linear matrix inequalities. The obtained results are extended to the class of continuous-time systems governed by the Roesser model with Markovian switching. The problems of absolute stability and stabilization via state- and output-feedback are solved for linear systems of the above class. The solution procedures for these problems are in the form of algorithms based on linear matrix inequalities.     

Analysis of the correlation between acoustic noise and vibration generated by a multi-layer ceramic capacitor

Acoustic noise generated by a multi-layer ceramic capacitor (MLCC) makes users uncomfortable, so the problem must be analyzed to reduce the noise. There is a correlation between the acoustic noise and the vibration of MLCCs and the circuit board. Therefore, the acoustic noise problem must be investigated from a vibration perspective. In this study, the acoustic noise-generating mechanism was investigated, and the relationship between the characteristics of the noise and the dynamic characteristics of the circuit board with MLCC was analyzed. And a correlation criterion was proposed to predict the acoustic noise using the vibration response of the circuit board.     

Production of nanoparticles of copper compounds by anodic dissolution of copper in organic solvents

The anodic behaviour of copper was investigated in ethanol solution containing LiClO₄, LiCl electrolyte and water. The type of electrolyte and the water content influences the mechanism of the anodic process and the formation of anodic products. In LiClO₄ electrolyte the dissolution of copper is related to the oxidation of Cu(I) to Cu(II). In solutions of LiCl the etching of copper begins with the creation of soluble complexes of Cu(I) with chloride ions and solvent molecules. At potentials above 0.4 V the formation of alkoxides was observed in both solutions, characterized by a yellow tint. On the other hand, above 0.8 V (i.e. above the equilibrium potential of alcohol oxidation) copper dissolution is accompanied by the formation of a blue colloidal suspension of Cu (II) copper salt. Anodic etching of copper in solutions containing 3% H₂O at potentials higher than 0.4 V leads to the formation of colloidal suspension of copper oxide nanoparticles.     

Selective Oxidation of Methanol to Formaldehyde Using Modified Iron-Molybdate Catalysts

Methanol selective oxidation to formaldehyde over a modified Fe-Mo catalyst with two different stoichiometric (Mo/Fe atomic ratio = 1.5 and 3.0) was studied experimentally in a fixed bed reactor over a wide range of reaction conditions. The physicochemical characterization of the prepared catalysts provides evidence that Fe₂(MoO₄)₃ is in fact the active phase of the catalyst. The experimental results of conversion of methanol and selectivity towards formaldehyde for various residence times were studied. The results showed that as the residence time increases the yield of formaldehyde decreases. Selectivity of formaldehyde decreases with increase in residence time. This result is attributable to subsequent oxidation of formaldehyde to carbon monoxide due to longer residence time.     

Preparation of nanosize Pt clusters using ion exchange of Pt(NH3) 4 2+ inside mesoporous channel of MCM-41

Mesoporous molecular sieve MCM-41 with a Si/Al ratio of 35 was obtained by hydrothermal synthesis using a gel mixture with a molar composition of 6 SiO₂0.1 Al₂O₃1 hexadecyltrimethylammonium chloride 0.25 dodecyltrimethylammonium bromide 0.25 tetrapropylammonium bromide0.15 (NH₄)₂O1.5 Na₂O300 H₂O. The MCM-41 sample was calcined in O₂ flow at 813 K and subsequently ion exchanged with Ca²⁺. A small Pt cluster has been supported on the MCM-41 sample following a procedure using ion exchange of Pt(NH₃) ₄ ²⁺ . The Pt(NH₃) ₄ ²⁺ ion supported on MCM-41 has been activated in O₂ flow at 593 K and subsequently reduced with Fh flow at 573 K, in the same way used for the preparation of a Pt cluster entrapped inside the supercage of zeolite NaY. The resulting Pt cluster supported on the MCM-41 shows hydrogen chemisorption oftotal two H atoms per Pt at 296 K (based on the total amount of Pt) and high catalytic activity for hydrogenolysis of ethane. The chemical shift in¹²⁹Xe NMR spectroscopy of adsorbed xenon indicates that the Pt cluster is located inside the mesoporous molecular sieve.     

IMAGING OF PARTICLE MOTION IN FLUID-SOLID SYSTEMS USING A GAMMA CAMERA

A new approach is presented for the characterization of particle motion in fluid-solid systems based on dynamic imaging with a gamma scintillation camera. A two-dimensional spouted bed of 200-500 micron diameter anion exchange resin beads was used as a test system. One or several beads were radiolabeled with the 140 keV gamma emitting radionuclide 99m-Tc pertechnetate, and particle velocity, panicle path, the spatial distribution of particle residence times, and local bed density were determined from the measured temporal and spatial distributions of particle activity. While care must be exercised in the interpretation of data when the scale for changes in the spatial distribution of activity approaches the limits of camera resolution, the method is quantitative, non-invasive, and well suited to the study of systems having symmetry in one spatial dimension.     

Migration of Intergranular Liquid Films and Formation of Core-Shell Grains in Sintered TiC–Ni Bonded to WC–Ni

When TiC–20 wt% Ni powder mixtures are sintered at 1400°C, relatively large TiC grains possibly containing some Ni form with near-equilibrium shapes. When these specimens are heat-treated again at 1400°C in contact with sintered WC–20 wt% Ni pieces, the liquid films between the TiC grains in the contact region migrate against their increasing curvatures, forming (Ti,W)C solid solution behind them. These migrating liquid films reverse their directions on further heat-treatment. As in other alloys, this liquid film migration must be driven by the coherency strain energy produced by W diffusion at the surface of the dissolving TiC grains. Shells of (Ti,W)C solid solution also form around the cores of TiC grains near the contact region, and this process is probably driven by both coherency strain energy and free energy of mixing. At some contact regions, (Ti,W)C precipitates nucleate and grow, probably driven mainly by the free energy of mixing. In powder mixtures, the formation of core-shell grains is expected to be driven by the coherency strain energy, the free energy of mixing, and the capillary effect.     

Modification of a carbon/carbon composite with a thermosetting resin precursor as a matrix by the addition of carbon black

Carbon/carbon composites were made through the pyrolysis of stabilized PAN felt and phenolic resin with the addition of 5 or 10 wt % carbon black to the matrix and then heat treatment at 600–2500°C. The effects of adding carbon black to the matrix precursor on the physical properties, microstructure, and mechanical properties of the resultant composites were investigated. Adding carbon black not only reduced the weight loss but also limited the shrinkage of the resultant composites. Adding carbon black also accelerated the formation of carbon basal planes in the matrix. At 2500°C, the crystalline stacking height in the composite with 10 wt % added carbon black was 200% greater than that with no additive. The flexural strength of the composite also increased from 15 to 42 MPa (almost 300%). © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 333–337, 2006