Possibilities and extension of XRD material response analysis in failure research for the advanced evaluation of the damage level of Hertzian loaded components

Due to clearly distinguishable damage symptoms, it is differentiated between the surface and sub‐surface failure mode of rolling bearings. Material states red out by X‐ray diffraction (XRD) residual stress measurements point to a variety of loading conditions especially at raceway surfaces that are associated with several competing failure mechanisms. The corresponding lifetime reduction can range from the lower fatigue strength region to material ratcheting in extreme cases. Relevant position of the microstructural changes and nature of the failure mechanisms are characterized. The time alteration of the XRD material parameters measured at or near the surface and at the depth of the maximum equivalent stress correlates, in a different manner, with the statistical parameter of the 10 % bearing life. Both failure modes are illustrated by concrete examples. Contaminated lubricant and boundary lubrication, which represent practically important surface‐induced failures, are discussed in more detail. Gray staining, i.e. shallow pitting, often occurs without distinct indication of global material aging by means of XRD characteristics. Here, scanning electron microscopy observations and electron microprobe analyses point to corrosion fatigue as acting surface failure mechanism. The interaction between material and lubricant under complex loading regimes particularly of mixed friction and corrosion opens further failure research areas in the field of tribology.     

A multilevel soliton communication system

A multilevel soliton communication system is proposed and assessed. In this system, at the transmitter end each channel transmits its data via fundamental solitons with a pre-specified amplitude (i.e., soliton width). At the receiver end we take advantage of the sensitive relationship between the amount or fundamental soliton self-wavelength shift and the width of the soliton in the subpicosecond region. We first compress the incoming soliton noises to the subpicosecond level and pass them through a short length of fiber at the end of which the pulses have become separated in the wavelength domain since each soliton, corresponding to a data channel, has experienced a different Raman self-wavelength shift. The channels are then easily separated by optical filters. We have derived the design constraint relations for such a system. We have then heuristically designed a 40 Gbs (four channels) system for a 1000 km propagation distance (total data-rate distance product of 40 Tb/km). Numerical simulations and noise analyses have verified the feasibility and practicality of the proposed system with very good design margins. The wavelength jitter is found to be much smaller than the desired filter spacing, and thus its contribution to the bit error rate is negligible. We also argue that the system is more tolerant to Gordon-Haus timing jitter than conventional TDM soliton systems. The system is all fiber and is, therefore very cost effective as it does not require sophisticated electro-optic and microwave circuits for demultiplexing. The system can potentially operate at much higher speeds than those achievable in conventional soliton systems and it can be used in parallel with WDM soliton system     

传输线衰减常数与柱形谐振器Q值的关系

文中严格地讨论了任意截面形状，任意模式的柱形谐振腔Ｑ值与构成该谐振器的传输线衰减常数间的关系，给出了更一般的公式，推广了Ｄａｖｉｄｓｏｎ和Ｓｉｍ－ｍｏｎｄｓ＾［１］、Ｂａｒｌｏｗ和Ｃｕｌｌｅｎ＾［２］以及Ｙｅｈ和Ｓｈｉｍａｂｕｋｕｒｏ＾［３，４］的结果。     

淀积条件对GDa—SiNx薄膜电学特性的影响

本文讨论了用辉光放电法制备氮化硅薄膜时衬底温度、射频功率和气体流量比对薄膜的电导率、介电常数和击穿强度的影响。通过优化生长条件，制备了优质非晶氮化硅薄膜，其介电常数为７．５、击穿强度为５．５ＭＶ／ｃｍ、电导率为１０－１３（Ωｃｍ）－１。     

极尖断面为折线的四极透镜磁性能研究

对传统双曲线极尖的四极透镜进行了磁性能分析。在此基础上，提出了极尖断面为折线的四极透镜结构。磁场的数值分析以及测量结果表明：该结构产生的场梯度均匀，且具有磁场集中、磁场梯度高、便于加工和安装的对称性控制等优点。该结构的四极透镜已用于ＣＹＣＩＡＥ－３０回旋加速器和ＨＩ－１３串列加速器束流输运线之中     

Production and properties of micro‐porous glas bubble zinc and aluminium composites

Micro‐porous syntactic foams were produced by means of integration of glass bubbles into aluminium and zinc matrices. Preforms of glass bubbles were pressure infiltrated with the alloys AlSi9Cu9 ans ZnAl4Cu using squeeze casting. The preforms were sintered thermically without the use of bonding agents. Using the combination of different sintering steps syntactic foams with locally different densities could be produced. The mechanical properties of the foams were tested indicating a high compression strength of the foams and a very good compression energy absorption. Furthermore, corrosion behaviour and behaviour at higher temperatures were investigated.     

From information to probability: An axiomatic approach—Inference is information processing

We define the very rich language of composed conditionals on a three‐valued logic and use this language as the communication tool between man and machine. Communication takes place for three reasons: knowledge acquisition, query, and response. Learning, thinking, and answering questions are of a pure information theoretical nature. The pivot of this knowledge processing concept is the amount of information (bit) we receive if a conditional becomes true. We follow an axiomatic approach to information theory rather than the classical probabilistic approach of Shannon; information comes first, and then comes probability. In the light of this philosophy, query and response experience new interpretations. Both, acquisition and response are realized by maximizing entropy and minimizing relative entropy, respectively. The iterative solution of these mathematical optimization problems gives new insights into the adaptation of prior knowledge to new information. Our expert system shell SPIRIT supports this kind of knowledge processing, which will be established by suitable examples. © 2003 Wiley Periodicals, Inc.     

Prediction of fire classification for wood based products. A multivariate statistical approach based on the cone calorimeter

Wood has long traditions as a building material, and is often used in construction elements, and as interior and exterior surfaces in the Nordic countries. In most applications, there are reaction to fire requirements to products used as surfaces, e.g. in escape routes and larger public spaces. Most wood products will therefore have to be treated with fire retardant (FR) agents to fulfil the strict requirements to properties connected to heat release and flame spread. Unfortunately, FR agents usually also increase the smoke production, as they cause a more incomplete combustion of the wood. The wood product manufacturers seek to find the optimal amount of FR additives where both heat release and smoke production in the classifying test are within the requirements given in the building regulations. This paper describes models for prediction of the European reaction to fire classes of wood products. The models are based on multivariate statistical analysis, and use test results from the cone calorimeter test as input. The presented models are, with very good precision, able to predict which Euroclass and additional smoke class a wood based product would obtain if it were to be tested in the single burning item test. Copyright © 2006 John Wiley & Sons, Ltd.     

Characterization and comparison of PECVD silicon nitride and silicon oxynitride dielectric for MIM capacitors

In this letter, we report on the electrical characteristic and the comparison of the metal-insulator-metal (MIM) capacitors with PECVD silicon nitride (SiN) and silicon oxynitride (SiON). Both capacitors are found to exhibit low leakage and high breakdown field strength, as well as absence of dispersive behavior, good linearity, and comparable quality factor behaviors.