In situ observation of synthesized nanoparticles in ultra-dilute aerosols via X-ray scattering

In-air epitaxy of nanostructures (Aerotaxy) has recently emerged as a viable route for fast, large-scale production. In this study, we use small-angle X-ray scattering to perform direct in-flight characterizations of the first step of this process, i.e., the engineered formation of Au and Pt aerosol nanoparticles by spark generation in a flow of N₂ gas. This represents a particular challenge for characterization because the particle density can be extremely low in controlled production. The particles produced are examined during production at operational pressures close to atmospheric conditions and exhibit a lognormal size distribution ranging from 5–100 nm. The Au and Pt particle production and detection are compared. We observe and characterize the nanoparticles at different stages of synthesis and extract the corresponding dominant physical properties, including the average particle diameter and sphericity, as influenced by particle sintering and the presence of aggregates. We observe highly sorted and sintered spherical Au nanoparticles at ultra-dilute concentrations (< 5 × 10⁵ particles/cm³) corresponding to a volume fraction below 3 × 10^–10, which is orders of magnitude below that of previously measured aerosols. We independently confirm an average particle radius of 25 nm via Guinier and Kratky plot analysis. Our study indicates that with high-intensity synchrotron beams and careful consideration of background removal, size and shape information can be obtained for extremely low particle concentrations with industrially relevant narrow size distributions.

     

High-Alumina Mixes Based on Molded Bauxite Suspensions

Refractories and Industrial Ceramics - Results of studying the rheotechnological properties of moldable refractory mixes based on bauxite suspensions plasticized with refractory clay are presented....     

Results from Survey and Geotechnical Monitoring on Test Site No. 3 of the Zagorsk PSP-2

Power Technology and Engineering - The major results from the survey and geotechnical monitoring during the leveling of the model foundation of the Zagorsk PSP-2 in test site No. 3 are presented....     

Characterization of anisotropic gas permeability and thermomechanical properties of highly textured porous alumina

Porous alumina with a highly textured microstructure was fabricated by pulse electric current sintering (PECS) using alumina platelets. Highly oriented porous alumina with a porosity of 3%–50% was obtained by a pressure-controlled method of PECS. The properties of the highly textured porous alumina were measured in two directions. The nitrogen gas permeance and thermal conductivity at room temperature were higher in the direction along the platelet length due to the higher continuity of pores and the connectivity of alumina platelets, respectively. The anisotropy of the thermal conductivity at room temperature was investigated and explained by the effect of grain size of platelets as well as morphology and orientation of pores. The bending strength was higher with the loading direction along the platelet thickness. The thermal shock strength was clearly different in the two directions. The difference in the thermal shock strength was investigated by the measurement of properties and thermal stress analysis.     

Concerning the Data of Numerical and Physical Experiments in Studying the Adsorption of Gas and Vapors in Micropores of Active Carbons

Protection of Metals and Physical Chemistry of Surfaces - The conditions for carrying out molecular dynamics calculations of adsorption isotherms of gases and vapors in micropores of active carbons...