Effect of heat treatment and zircon addition on the properties of low-cement castables based on recycled alumina grog

In this investigation, low-cement castables were prepared using 70% alumina grog aggregates obtained from crushed alumina brick waste. The aggregates were thermally treated at 1550 °C for 3 h. Four types of low-cement castables were prepared with various types of aggregates (alumina grog with or without thermal treatment) and fillers (with or without zircon addition), and they were evaluated in terms of their physical, thermal, and chemical properties. Microstructural analysis via scanning electron microscopy (SEM) was performed on the castables before and after slag attack. Compared to the other fabricated castables, the thermally treated alumina grog castables with zircon showed better physical properties, such as a higher bulk density, cold crushing strength, and modulus of rupture and a lower apparent porosity and water absorption. In addition, they had a higher positive linear thermal expansion, refractoriness under load, permanent linear change, and hot modulus of rupture. The results of the SEM with energy dispersive X-ray analysis of the prepared castables confirmed that the mullite and anorthite phases were predominant when zircon was not added and the zircon–mullite phase additionally appeared upon the incorporation of zircon. A quantitative elemental analysis via X-ray fluorescence spectroscopy was employed to determine the composition of the castables. X-ray diffraction analysis showed that the alumina grog castables had a high mullite and low anorthite content, and the thermally treated alumina grog had a high anorthite, low mullite, and high zircon content. The improvement in the mechanical and thermo-mechanical properties of the castables with thermally treated alumina grog and added zircon can be attributed to the formation of the zircon–mullite phase with a low mullite phase content.     

A review of phosphorescent and fluorescent phosphors for fingerprint detection

Currently, the efficient detection of fingerprints is essential for the crime investigations. Revealing fingerprints is commonly achieved with fluorescent organic compounds but they are not efficient for fingerprint detection on porous or reflective surfaces. In order to solve the problem of collecting fingerprints on porous/reflective surfaces, inorganic phosphors have been employed, since they have characteristics of variable color emission, afterglow, high chemical stability and nano-size, which allow the fingerprint detection on any porous or non-porous surfaces. Due to these last properties, this review presents a summary about the use of phosphorescent and fluorescent phosphors for the detection of latent fingerprints. First, we discussed the main physical and chemical characteristics of the fingerprints which permit their detection and collection from any surface. After this, we presented the main morphological, structural and luminescent properties of the phosphorescent and fluorescent phosphors that allow their use for fingerprint detection. Later, we demonstrated with pictures of fingerprints (with and without light emission from the phosphors deposited on them) that both, phosphorescent and fluorescent phosphors can be used to visualize fingerprints with high resolution and high contrast without interference of the background surface, which is ideal for its collection and registration in the Automated Fingerprint Identification System (AFIS). We believe that this review could be useful to understand how to select an appropriate phosphorescent or fluorescent material for fingerprint detection depending on the type of surface (porous or non-porous, reflective or not reflective) where the fingerprint is deposited.     

Multicriteria Minimax Problems: Localization of the Pareto Set and Suboptimal Control Design

Automation and Remote Control - We consider multicriteria minimax optimization problems with criteria in the form of the maxima of functionals given by the induced norms of linear operators taking...     

Blockchain for Collaborative Businesses

Mobile Networks and Applications - Blockchain applications have continuously improved ever since its first debut on cryptocurrency. From then on, its uses have branched out from the financial...     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Phase locked loop-based clock synthesizer for reconfigurable analog-to-digital converters

Analog Integrated Circuits and Signal Processing - This paper presents the complete design of a phase locked loop-based clock synthesizer for reconfigurable analog-to-digital converters. The...     

An integrated dimensionality reduction and surrogate optimization approach for plant-wide chemical process operation

With liquefied natural gas becoming increasingly prevalent as a flexible source of energy, the design and optimization of industrial refrigeration cycles becomes even more important. In this article, we propose an integrated surrogate modeling and optimization framework to model and optimize the complex CryoMan Cascade refrigeration cycle. Dimensionality reduction techniques are used to reduce the large number of process decision variables which are subsequently supplied to an array of Gaussian processes, modeling both the process objective as well as feasibility constraints. Through iterative resampling of the rigorous model, this data-driven surrogate is continually refined and subsequently optimized. This approach was not only able to improve on the results of directly optimizing the process flow sheet but also located the set of optimal operating conditions in only 2 h as opposed to the original 3 weeks, facilitating its use in the operational optimization and enhanced process design of large-scale industrial chemical systems.     

Alumina-Periclase-Carbon Refractories Produced by OOO Ogneupor

Refractories and Industrial Ceramics - Technology for producing alumina-periclase-carbon refractories of the brands APUK-D and APU-D is developed and implemented. Use of complex antioxidant and...     

Properties of High-Strength Aramid Fiber Textile Materials for Protective Clothing

Fibre Chemistry - An analysis of the aramid fiber market including the range of industrial textile materials containing chemical fibers for specialized protective clothing of metallurgical workers,...     

A novel ceramic matrix composite based on YNbO4–TiO2 for microwave applications

This work presents the dielectric properties of YNbO₄ (YNO)–TiO₂ composites in the microwave range. X-ray diffraction analysis demonstrates that the addition of TiO₂ to YNO results in the formation of a Y(Nb_0.5Ti_0.5)₂O₆ phase. In the microwave range, the values of permittivity and dielectric loss did not present major changes with the increment of TiO₂. Moreover, the addition of TiO₂ results in an improvement in the thermal stability of YNO, with YNO63 demonstrating a resonant frequency of ?8.96 ppm.°C^?1. We utilised numerical simulations to evaluate the behaviour of these materials as dielectric resonator antennae and it is found that they exhibit a reflection coefficient below ?10 dB at the resonant frequency, with a realised gain of 4.94 – 5.76 dBi, a bandwidth of 665–1050 MHz and a radiation efficiency above 84%. Our results indicate that YNO–TiO₂ composites are interesting candidates for microwave operating devices.