镍氢电池负极用低成本储氢合金的研究

研究了ABS型储氢合金在低Co含量条件下，随B组元替代元素Co，Al，Si等含量的变化对合金电化学性能的影响规律，同时研究了A组元中不同La／Ce比对合金电化学性能的影响情况。结果表明，随合金中Co含量的降低，合金的活化性能和放电容量得以改善，但合金的循环寿命下降也比较明显；在试验范围内，随Al元素的加入，合金的循环寿命得以改善，但材料的放电容量和活化性能均有所下降；随合金La／Ce比的降低，合金的放电容量略有下降，但其循环寿命和放电电压平台有较大提高。     

防治水泥稳定碎石基层沥青路面裂缝的措施浅析

水泥稳定碎石基层沥青路面裂缝产生的原因复杂 ,但非荷载型裂缝更为主要。防治水泥稳定碎石基层沥青路面的裂缝应该从设计和施工两方面考虑 ,其中由结构、材料组成设计 ,以及施工工艺出发控制水泥稳定碎石基层本身的收缩也是一项重要措施。     

Spin Dependent Hopping in Ti Doped La0.67 Ca0.33 MnO3

A systematic investigation of the magnetic and transport properties of Ti doped La0.67Ca0.33MnO3 was reported. The Ti substitution for Mn ions results in a reduction in ferromagnetism and conductivity. The metal-insulator transition temperature is close to Curie temperature which decreases from 274 to 82 K as x increases from 0 to 0.17. The most important effect of Ti doping is to introduce spin clusters in the samples due to the distortion of local lattice and the inhomogeneous magnetic structure induced primarily by the random distribution of Mn ions. A maximum magnetoresistance ratio as large as 90% in 1 T at 122 K was obtained for the sample with x =0. 055, which is four times larger than that obtained for LCMO sample at 272 K. There is a remarkable field-history dependent MR in the cooling process for the doped samples while such phenomenon disappears in the warming run. The resistivity follows well the variable range hopping behavior in paramagnetic state. Both the size effect and spin dependent hopping of carriers between the spin clusters should be considered in this system.     

Cr-Mo solid solutions forced by high-energy ball milling

Mixtures of Cr and Mo elemental powders, with the nominal compositions Cr₂₅Mo₇₅, Cr₅₀Mo₅₀, and Cr₇₅Mo₂₅, are processed by high-energy ball milling at ambient temperature. Milling is observed to force the mixing of the immiscible bcc elements Cr and Mo into solid solutions. The lattice parameter of these solid solutions, measured by X-ray diffraction (XRD), displays the expected positive deviation from Vegard’s law. These deviations are compared to the ones predicted by Eshelby’s inclusion model for dilute alloys. The conventional Williamson-Hall approach is shown to fail to determine the grain size in as-milled samples, probably due to the high density of dislocations. Annealing at 700 °C for 10 hours under argon leads to a large reduction in structural defect density, without inducing any significant decomposition. The mixing measured in Cr-Mo is discussed in the broader context of the mechanical mixing forced by ball milling in moderately immiscible systems.     

AMBE-1000声码器接口电路设计方法

DVSI公司的AMBE-1000声码器芯片是一款高性能的全双工、实时语音压缩编解码芯片,可以应用于卫星通信、保密通信、视频会议等领域.文中简要介绍AMBE-1000声码器的A/D-D/A接口以及信道接口的工作原理;结合实例分别给出了AMBE-1000声码器与PCM编解码器MC14LC5480的A/D-D/A接口电路、与单片机AT89C51的信道接口电路的设计方法;最后指出了电路设计中应该注意的问题.     

关于本地传输网网络优化的探讨

根据长期工作经验,对现有网络存在的问题进行分析,提出对本地传输网网络优化的有关建议。     

关于海面无线传播模型的探讨

现有文献中一般都认为海面环境的无线传播模型近似于自由空间传播模型，但在实际测试中发现，自由空间模型预测值与实测值差别较大，不能很好地解释此类环境的信号传播。笔者根据多次海面覆盖测试的数据，分析并拟合出了新的海面传播模型。     

Parallel multilevel fast multipole method for solving large-scale problems

The Multilevel Fast Multipole Method (FMM) is a well-established method and can be applied to solve electromagnetic (EM) scattering problems. Compared with other traditional methods, it requires less computational time and memory. However, constrained by a single processor's speed and memory limitations, the problem size that can be solved by serial implementation is still relatively small. For a million-unknown target, the computational time on a single processor is intolerable, and memory could be easily exhausted. Parallel-computing technology, which can utilize multiprocessors, provides an efficient way to solve electrically large-scale EM problems. This paper will focus on discussing the parallel methodologies applied to a multilevel FMM code, as well as demonstrating the computational efficiency of the parallel approach.     

Preirradiation grafting of acrylic and methacrylic acid onto polyethylene films: Preparation and properties

The method of preirradiation grafting of acrylic acid and methacrylic acid onto polyethylene films was studied. The trapped radicals and hydroperoxides or diperoxides appeared to be able to induce graft polymerization. Mohr's salt was added to depress homopolymerization. The influences of crystallinity, dosage, and storage period on the grafting behavior were investigated from the viewpoint of practical application. At elevated temperature, the degree of grafting increased rapidly with reaction time initially, and then leveled off to the value of final percent grafting. Dosage and storage periods had greater extent of influence on the final percent grafting of LDPE than on that of HDPE. Electrical properties, transport properties, and mechanical properties were measured to compare the differences between acrylic-acid-and methacrylic-acid-grafted copolymer films. It was found that the properties of methacrylic-acid-grafted copolymer film was superior to those of acrylic-acid-grafted copolymer film, especially in electrical conductivity. The KOH diffusion test confirmed that grafting occurred not only on the surface but also in the interior of the polymer matrix, and the grafting is believed to proceed from the surface to the interior of the matrix.     

Al-Zn-Ce非晶合金的相选择与组织结构演化

本文研究了具有典型分解特征的Al-Zn-Ce非晶合金的形成和晶化过程，探讨了各种相的生成顺序。XRD和DSC测试结果表明强烈的化合物短程序有利于Al-Zn-Ce非晶合金的形成。在Al-Zn-Ce非晶合金的晶化过程中存在复杂的相选择行为，多种相的竞争形核和有限生长使其具有复杂的结构特点。同时，结果也表明冷速对该体系非晶的形成有很大影响。