Effect of Intercritical Annealing Time on the Microstructure and Mechanical Properties of Dual-Phase Steel Processed by Large-Strain Asymmetric Cold-Rolling

Herein, the effect of intercritical annealing time on the microstructure and mechanical properties of dual-phase steel processed by large-strain asymmetric cold-rolling is studied. It is observed that the martensite islands are uniformly distributed in the ferrite phase in the microstructures of dual-phase steels due to performing the asymmetric cold-rolling before intercritical annealing treatment. As the intercritical annealing time increases up to 10 min, the fraction of martensite increases. By increasing the holding time and fraction of martensite, the carbon content of the martensite phase is decreased. The short-term intercritical annealing eliminates the yield point phenomenon. However, intercritical annealing at 860 °C for 20 min leads to the reoccurrence of a yield point phenomenon. Increasing the intercritical annealing time to 10 min improves the yield strength to 505 MPa and ultimate tensile strength to 834 MPa. However, the strength decreases sharply after the holding time of 20 min. There is a perfect linear relationship between the mechanical properties and the fraction of martensite. Ductile failure is observed at the center of the fracture surfaces of dual-phase steels while shear failure occurs at the edges of the fracture surfaces.     

Engineering a drug eluting ocular patch for delivery and sustained release of anti-inflammatory therapeutics

Ocular inflammation is commonly associated with eye disease or injury. Effective and sustained ocular delivery of therapeutics remains a challenge due to the eye physiology and structural barriers. Herein, we engineered a photocrosslinkable adhesive patch (GelPatch) incorporated with micelles (MCs) loaded with loteprednol etabonate (LE) for delivery and sustained release of drug. The engineered drug loaded adhesive hydrogel, with controlled physical properties, provided a matrix with high adhesion to the ocular surfaces. The incorporation of MCs within the GelPatch enabled solubilization of LE and its sustained release within 15 days. In vitro studies showed that MC loaded GelPatch supported cell viability and growth. In addition, subcutaneous implantation of the MC loaded GelPatch in rats confirmed its in vivo biocompatibility and stability within 28 days. This non-invasive, adhesive, and biocompatible drug eluting patch can be used as a matrix for the delivery and sustained release of hydrophobic drugs.     

Propagation of Terahertz Pulses in Photonic Crystal-Based Rib Silicon Waveguides

Silicon - Propagation of terahertz (THz) waves in silicon waveguides is of special interest for THz applications such as optical integrated circuits. In this paper, a photonic crystal-based rib...     

Solution combustion synthesis of FeCr2O4:Zn,Al pigment powders

FeCr₂O₄:Zn,Al pigment powders were prepared via a solution combustion synthesis method. Effects of Zn and Al dopants and less/extra Fe content on the structure, molecular bonds, and optical properties of powders were studied. Results showed that addition of dopants as well as extra/less content of Fe led to weaker combustion and consequently lower X-ray diffraction peak intensities, lattice parameters, and differential thermal analysis peak intensities. Moreover, Fourier transform infrared analysis illustrated that the band position of Cr–O and Fe–O bonds were shifted to higher frequencies with moving away from stoichiometry. In addition, scanning electron micrographs showed that in all samples, porous spongy microstructures were formed with highly flake-like agglomerated particles. Furthermore, there was a significant difference between the powder samples and the tiles colored with in glaze powders due to the partial dissolution of pigments in contact with the molten glaze of tiles. In comparison to the tile colored with the stoichiometric FeCr₂O₄ pigments without dopants, the color difference (ΔE) in the tiles colored by the iron chromite pigments doped with Zn and Al dopants and less/extra Fe content reached the high values as large as ΔE = 36.19. The solar reflectance values (R_s) in near-infrared region were above 50% in all samples. Near 80% R_s in the tile colored by the iron chromite pigment doped with 3 mol% Zn and the yellowish brown appearance (L* = 43.44, a* = 6.77, b* = 18.38, c* = 19.59, h = 69.79) showed that the sample was a good candidate for cool building materials such as roof tiles.     

Phase transformation of FeCr2O4 to (Fe,Cr)2O3 solid solution pigment powders: Effect of post-heating temperature

Iron chromite powders were synthesized via solution combustion route using iron(III) nitrate nonahydrate and chromium(III) nitrate nonahydrate as starting materials, as well as glycine–urea, glycine–citric acid, and glycine–ethylene glycol mixtures as fuels. The effect of postheating at different temperatures on the structure, molecular, microstructure, and chromatic properties of powders and tiles colored by in-glaze powders was studied. The X-ray diffraction patterns showed that as-synthesized powders were obtained in crystalline FeCr₂O₄ phases moreover, postheating of the powders led to d-space shift and oxidation and formation of (Fe,Cr)₂O₃ solid solution phase regardless of fuel type. Phase transformation of FeCr₂O₄ to (Fe,Cr)₂O₃ solid solution was observed at 500/750°C depending on the dominant phase of as-synthesized particles. Fourier transform infrared analysis illustrated that the band positions of octahedral M–O and tetrahedral M–O bonds were shifted due to Fe cations movement from their position and lattice shrinkage by increasing of post-heating temperature. Moreover, scanning electron micrographs showed that Fe_0.7Cr_1.3O₃ semispherical fine particles were formed from porous spongy FeCr₂O₄ particles due to oxidation and phase transformation during the postheating. Furthermore, chromatic properties of the samples were represented. The color properties of the pigments showed that the formation of brown pigments is provided with the phase transformation from FeCr₂O₄ to (Fe,Cr)₂O₃ at a temperature of up to 750°C. Moreover, increasing the color purity to this temperature is related to the removal of residual carbonaceous matters. The chromatic properties of the glazed tiles colored using the pigments showed that postheating between 250 and 500°C led to more brown appearance.     

Synthesis of (Fe,Cr)2O3 solid solution pigment powders for ink application

Iron chromite pigment was synthesized via solution combustion using iron(III) nitrate nonahydrate and chromium(III) nitrate nonahydrate as starting materials, and glycine, urea, citric acid, and ethylene glycol as fuels. The effect of postheating temperature on the structure, microstructure, and chromatic properties of the synthesized powders was also studied. X-ray diffraction patterns showed that the as-synthesized powders were amorphous to crystalline FeCr₂O₄ phases, depending on fuel type. Moreover, regardless of the fuel type, postheating led to the d-space shift and oxidation and formation of (Fe,Cr)₂O₃ solid solution. Phase transformation of FeCr₂O₄ to (Fe,Cr)₂O₃ solid solution was observed at 500/750°C depending on the dominant phase present in the as-synthesized particles. Fourier transform infrared analysis illustrated a shift in the band position of octahedral M–O and tetrahedral M–O bonds due to the movement of Fe cations and the lattice shrinkage by increasing the postheating temperature. Moreover, scanning electron micrographs showed that Fe_0.7Cr_1.3O₃ semispherical fine particles consisted mainly of porous and spongy FeCr₂O₄ particles due to the oxidation and phase transformation during postheating. According to chromatic measurements, the ink prepared by using the powders synthesized in the presence of glycine and post-heated at 500°C showed reddish-brown color which could be considered a promising candidate for tile decoration application. Furthermore, rheology studies revealed that the prepared ink showed non-Newtonian shear thinning behavior.     

Assessment of the thermodynamic,environmental and economic output of agro-ecosystems: onion set versus onion production

Clean Technologies and Environmental Policy - Farmers sow onion seeds either for the purpose of preparing onion sets or for producing onions. Thermodynamic, economic and environmental analyses were...