Catalytic epoxidation of olefins in the presence of a vanadyl porphyrin complex

It was found that vanadyl porphyrin complexes synthesized from petroleum metal porphyrin concentrates stimulated epoxidation during the olefin oxygenation process. The yields of obtained oxiranes turned out to be 38–75%, depending on the olefin structure. An epoxidation mechanism that suggests the formation of a protonated dioxygen adduct as an intermediate during oxygenation of olefins in the presence of vanadyl porphyrin complexes was proposed. An analogy is drawn between the epoxide formation reaction upon the catalytic oxygenation of olefins and the Prilezhaev reaction.     

The effect of grain size, strain rate, and temperature on the mechanical behavior of commercial purity aluminum

Commercial purity aluminum AA1050 was subjected to equal channel angular extrusion (ECAE) that resulted in an ultrafine-grained (UFG) microstructure with an as-received grain size of 0.35 μm. This UFG material was then annealed to obtain microstructures with grain sizes ranging from 0.47 to 20 μm. Specimens were compressed at quasi-static, intermediate, and dynamic strain rates at temperatures of 77 and 298 K. The mechanical properties were found to vary significantly with grain size, strain rate, and temperature. Yield stress was found to increase with decreasing grain size, decreasing temperature, and increasing strain rate. The work hardening rate was seen to increase with increasing grain size, decreasing temperature, and increasing strain rate. The influence of strain rate and temperature is most significant in the smallest grain size specimens. The rate of work hardening is also influenced by strain rate, temperature, and grain size with negative rates of work hardening observed at 298 K and quasi-static strain rates in the smallest grain sizes and increasing rates of work hardening with increasing loading rate and grain size. Work hardening behavior is correlated with the substructural evolution of these specimens.     

Sensor guided handling and assembly of active micro-systems

Positioning accuracies in the range of a few micrometers and below are necessary for the assembly of active micro-systems. In order to reach these accuracies, an assembly system for sensor guided micro-assembly is developed in the Collaborative Research Centre 516 “Design and manufacturing of active micro-systems”. The combination of a parallel robot with an integrated 3D vision sensor and a micro-gripper enables to reach relative positioning accuracies below 1 μm.     

Note on B-splines, wavelet scaling functions, and Gabor frames

Let g be a continuous, compactly supported function on such that the integer translates of g constitute a partition of unity. We show that the Gabor system (g,a,b), with window g and time-shift and frequency-shift parameters a,b>0 has no lower frame bound larger than 0 if b=2,3,... and a>0. In particular, (g,a,b) is not a Gabor frame if g is a continuous, compactly supported wavelet scaling function and if b=2,3,... and a>0. We give an example for our result for the case that g=B/sub 1/, the triangle function supported by [-1,1], by showing pictures of the canonical dual corresponding to (g,a,b) where ab=1/4 and b crosses the lines N=2,3,.     

On the origin of strain hardening in glassy polymers

The influence of network density on the strain hardening behaviour of amorphous polymers is studied. The network density of polystyrene is altered by blending with poly(2,6-dimethyl-1,4-phenylene-oxide) and by cross-linking during polymerisation. The network density is derived from the rubber-plateau modulus determined by dynamic mechanical thermal analysis. Subsequently uniaxial compression tests are performed to obtain the intrinsic deformation behaviour and, in particular, the strain hardening modulus. At room temperature, the strain hardening modulus proves to be proportional to the network density, irrespective of the nature of the network, i.e. physical entanglements or chemical cross-links. With increasing temperature, the strain hardening modulus is observed to decrease. This decrease appears to be related to the influence of thermal mobility of the chains, determined by the distance to the glass-transition temperature (T−T_g).     

Structure, properties, and thermal stability of nanocrystallite Fe-Ti-N soft magnetic films

We deposited Fe-Ti-N magnetic films with a high sputtering power of 7 W/cm/sup 2/. When the composition of the films was in the range of Fe-Ti(3.9 at.%)-N(8.8 at.%) to Fe-Ti(3.3 at.%)-N(13.5 at.%), the films were composed of /spl alpha/' and Ti/sub 2/N precipitates. With the addition of nitrogen, 4/spl pi/M/sub s/ became higher than that of pure iron, reaching a maximum of 23.8 kG. At the same time, H/sub c/ was reduced to a minimum of 1.12 Oe. The best films can meet the needs of the recording head in dual-element giant magnetoresistive/inductive heads, yielding high storage density (10 Gb/in/sup 2/). The incorporation of N in /spl alpha/-Fe brought about the /spl alpha/' phase with its higher saturation magnetization. Ti additions inhibited the equilibrium decomposition /spl alpha/'/spl rarr//spl alpha/+/spl gamma/'. Because H/sub C//sup D//spl prop/D/sup 6/, where D is average grain diameter, grain size control is very important. The nitrogen induces severe distortion of the /spl alpha/' lattice, which can cause the grains to break into pieces and reduce the grain size. High sputtering power also led to the formation of fine grains, with diameter in the order of 14 nm. Probably Ti/sub 2/N is preferentially precipitated on the grain boundary, pinning the grain boundary and stabilizing the grain size during high-temperature heat treatment. The temperature limit for stability of the structure and its associated low coercivity was not less than 520/spl deg/C.     

Experimental and modeling approaches of MR behaviors under large step strains

Rheological properties of MR fluids under large step strain shear are presented in this paper. The experiments were carried out using a rheometer with parallel-plate geometry. Under the large step strain shear, MR fluids behave as nonlinear viscoelastic properties, where the stress relaxation modulus, G(t, γ), shows a decreasing trend with step strain. The experimental results indicate that G(t, γ) obeys time-strain separability. Thus, a mathematical form based on finite exponential serials is proposed to predict MR behavior. In this model, G(t, γ) is represented as the product of a linear stress relaxation, G(t), and the damping function, h(γ), i.e. G(t, γ)=G(t) h(γ). G(t) is simply represented as a three-parameter exponential serial and h(γ) has a sigmoidal form with two parameters. The parameters are identified by adopting an efficient optimization method proposed by Stango et al. The comparison between the experimental results and the model-predicted values indicates that this mathematical model can accurately predict MR behavior.