Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

CuInS2/SiNWs/Si composite material for application as potential photoelectrode for photoelectrochemical hydrogen generation

This work aims at developing a new composite material based on nanosized semiconducting CuInS₂ (CIS) particles combined with silicon nanowires grown on a silicon substrate (SiNWs/Si) for photoelectrochemical (PEC)-splitting of water. The CIS particles were prepared via a colloidal method using N-methylimidazole (NMI) as the solvent and an annealing treatment. The SiNWs were obtained by chemical etching of silicon (100) substrates assisted by a metal. The CIS/SiNWs/Si composite material was obtained by deposition of an aliquot of a suspension of CIS particles onto the SiNWs/Si substrate, using spin coating followed by a drying step. The XRD pattern demonstrated that CuInS₂ grows in the tetragonal/chalcopyrite phase, while SiNWs/Si presents a cubic structure. The SEM images show semi-spherical particles (～10 nm) distributed on the surface of silicon nanowires (～10 μm). The EIS measurements reveal n-type conductivity for CIS, SiNWs/Si and CIS/SiNWs/Si materials, which could favour the oxidation reaction of water molecules.     

A Giant Frequency Shift in the Raman Spectrum of Water Adsorbed on a Metallic Silver Surface

The Raman spectrum of water adsorbed on a metallic silver surface reveals an anomalously large shift of the vibrational frequency as compared to that in the bulk. The results are compared to data reported by other researchers, and possible interpretations of the observed phenomenon are discussed.     

Role of Elastic Interphase Deformations in the Formation of Crystal Structure of β-Nb Particles Precipitating in a Zr–2.5% Nb Alloy

X-ray diffraction analysis has been used to study the structure of the α-Zr matrix phase and the precipitation of β-Nb particles upon the annealing of a Zr–2.5% Nb deformed alloy. It has been found that the process of the precipitation of the strengthening β-Nb particles in the alloy is accompanied by the appearance of fields of elastic interphase deformations in the matrix α phase of the alloy due to the difference in the specific atomic volumes of the crystal structures of the matrix and precipitated phases. It has been shown experimentally that, as a result of the presence of interphase deformations in the alloy, the bcc crystal structure of the precipitating β-Nb particles undergoes monoclinic distortions.     

Performance Analysis of Pulse Generators on Residual Stress of Machined Silicon Steel Using the EDM Process

The cracks in the workpiece specimens can reduce the fatigue life of any machine components. Since the residual stress has a considerable amount of influence on determining crack formation over the machined surface, it is very essential to analyze the residual stress developed in any machining process. However, it is a very tedious process to compute the residual stress over the machined surface. In the present study, an endeavor has been made to measure and analyze the residual stress of machined silicon steel as a workpiece using the EDM process with different energy distribution. The nano-indentation method was used to compute the residual stress produced over the machined surface. From the experimental results, it was found that the uniform energy distribution has produced higher compressive residual stress owing to the tiny and uniform spark energy distribution. It has also been observed that the tool electrode has a considerable amount of influence on determining development of residual stress in the EDM process.     

Synthesis of Tritium-Labeled Deoxyglucose and Its Derivative

Radiochemistry - Reaction of solid-phase catalytic heterogeneous isotope exchange of 2-deoxy-D-glucose and its derivative, O(6)-(4-bromothiophenyl)guanine-C8-β-D-glucose with tritium has been...     

Classification of Reconfigurable Parallel Mechanisms

Russian Engineering Research - The theoretically possible reconfigurable parallel mechanisms are classified, in terms of the layout of guides on the base. Formulas are derived for the...