Fabrication of Cu(In,Ga)Se2 thin films by ion beam sputtering deposition from a quaternary target at different substrate temperatures

Cu(In, Ga)Se₂ (CIGS) thin films were fabricated by ion beam sputtering deposition from a single quaternary target at different substrate temperatures (T _sub). The thin films were characterized with X-ray diffractometry, scanning electron microscopy, energy-dispersive X-ray spectroscopy and four-point probe technique to study the microstructures, surface morphology, composition and electrical properties, respectively. The results show that the films grown above 400?°C are of chalcopyrite structure. Cu(In_0.7Ga_0.3)Se₂ thin film was obtained when T _sub is 550?°C. The Cu and Se atomic percentage when T _sub is above 500?°C is higher than when T _sub is below 500?°C. With the increase in T _sub, the surfaces morphology of the films is denser and the resistivity of the films decreases.     

25英寸700线彩色显像管偏转线圈的优化设计

在组合法计算彩色显像管偏转系统的基础上，对25英寸700线彩色显像管所用偏转线圈进行了优化设计。选取荧光屏光栅结点上的像差作为优化目标函数，选取线圈调制极上绕线密度的傅里叶展开系数作为优化参数，采用分步阻尼法优化设计出了25英寸700线彩色显像管用偏转线圈。根据实际的实验条件，绕制了25英寸700线彩色显像管用垂直偏转线圈，并与已有的25英寸同类彩色显像管所用偏转线圈进行了比较和分析。     

Analysis of the drude model in metallic films

A method, believed to be new, to simulate Drude parameters for collective oscillation of the free carriers in metallic films is proposed. Plasma resonance frequency and relaxation were simulated simultaneously from both the real and the imaginary parts of the dielectric function of a metallic film after consideration of their correlation in the Drude model. As examples, the contributions of the electrons in Ag films and of the free carriers in metallic silicide, NbSi(2) and TaSi(2), films have been studied.     

Microstructure and mechanical property of laser melting deposition (LMD) Ti/TiAl structural gradient material

This article presents fabrication, microstructure and mechanical properties study of Ti/TiAl functional gradient material. Ti–47Al–2.5V–Cr/Ti–6Al–2Zr–Mo–V gradient material was successfully fabricated by the laser melting deposition (LMD) manufacturing process. Microstructure and chemical composition was characterized by OM, SEM, TEM and EPMA. The Vickers hardness and room-temperature tensile property was evaluated on longitudinal direction. Results showed that fully lamellar (FL) microstructure consisted of γ-TiAl and α₂-Ti₃Al was formed on the Ti–47Al–2.5V–Cr side, while coarse basket weave microstructure was formed on the Ti–6Al–2Zr–1Mo–1V side. No cracking was found in the gradient zone after aging at 800 °C for 48 h. The room-temperature tensile strength of the as-deposited specimen is up to approximately 1198.8 MPa in the longitudinal direction, while the tensile elongation is approximately 0.4%, indicating a typical brittle fracture.     

Phase formation mechanism and kinetics in solid-state synthesis of undoped and calcium-doped lanthanum manganite

LaMnO_3+δ and La_0.7Ca_0.3MnO₃ were synthesized from La₂O₃(La(OH)₃), CaCO₃ and MnO₂ powder mixture with solid-state reaction technique. X-ray diffraction and thermal analysis were employed in the present study on the process of synthesizing of the two compound powders. The kinetic study on solid-state reaction between La₂O₃ and MnO₂ in the powder mixture was isothermally carried out for LaMnO_3+δ formation. The result showed that the reaction process was controlled by three-dimensional solid-ionic diffusion. Both Jander and Ginstling-Brounstein model can be used to describe the reaction kinetics satisfactorily. The relevant apparent activation energy values obtained were as great as 205 ± 11 and 189 ± 8 kJ/mol. The reaction process of La_0.7Ca_0.3MnO₃ preparation from La₂O₃, SrCO₃ and MnO₂ powder mixture was also studied using X-ray diffraction and thermal analysis. The result indicated that the following steps composed the overall reaction: the decomposition of the reactant; the formation of La_1−xCa_xMnO_3+δ; La₂O₃ and Mn₃O₄ reacted with La_1−xCa_xMnO₃ to form final La_0.7Ca_0.3MnO₃ phase. The latest step was the most time-consuming one among others in the overall reaction.     

氯化聚乙烯对氯丁橡胶与甲基丙烯酸甲酯接枝共聚反应的影响

研究了高氯氯化聚乙烯(HCPE)对氯丁橡胶与甲基丙烯酸甲酯接枝共聚及其反应产物的影响。结果表明,HCPE能加快聚合速率,提高转化率、接枝效率和接枝度。含HCPE的产物,含有较高分子量的级份,分子量分布较宽,树脂相的分布比较均匀,并具有较好的机械性能和较高的粘接强度。     

一种改进的气动弹性时域推进方法

针对气动弹性控制方程,结构项采用标准龙格库塔方法推进,广义气动力项采用时间上的插值技术,发展了一种在每一时间步内只用计算一次非定常气动力的近似四阶龙格库塔推进方法。通过计算非线性Bernoulli方程和某一超音速翼面的气动弹性响应,证明该方法的时间准确度远高于采用气动力冻结技术的四阶龙格库塔方法。其准确度与标准龙格库塔方法相差不大,而其调用非定常气动力求解器的次数仅为其四分之一,大大提高了气动弹性数值模拟的效率。对于一般的气动弹性响应而言,该时间推进方法只用保证每个周期内的时间步在20～30个左右就能满足较高的准确度要求。     

Effect of doping cobalt on the micro-morphology and electrochemical properties of birnessite MnO2

Birnessite-type MnO₂ nanoparticles are synthesized by mixing KMnO₄ solution directly with ethylene glycol under ambient conditions. When cobalt exists in the solution, the micro-morphology of the products transforms from conglomeration to dispersive state. The result of transmission electron microscopy (TEM) and field emission scanning electron microscopy (FE-SEM) shows that the product is constructed with nanosphere in sizes of ca. 40 nm. These nanospheres are twisted by nanorods clusters. X-ray diffraction (XRD) pattern shows that the products are birnessite-type. The electrochemical properties of the prepared materials are studied using cyclic voltammetry (CV) and galvanostatic charge–discharge test in aqueous electrolyte. The product shows a very high specific capacity of 326.4 F g⁻¹. These results indicate that cobalt has great effects on the micro-morphology and electrochemical properties of manganese dioxide.