LiFe2/3Mn1/3PO4/C composite was prepared by the rheological phase reaction using LiH2PO4, Li2CO3, FePO4, Mn(Ac)2·4H2O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.
The Fe/C/SiCN composite ceramics were synthesized by polymer-derived method to obtain the integration of structure and functions. The electromagnetic waves (EMW) absorption properties at X and Ku bands were investigated. The addition of nano-sized Fe particles improved the magnetic loss and impedance matching, and the carbon nanotubes generated by the iron in-situ catalysis increased the internal relaxation polarization and interfacial polarization, which together improved the EMW absorption properties significantly. In particular, the Fe/C/SiCN-9 showed the optimum reflection loss (RL) of ?31.06 dB at 10.03 GHz with an effective absorption bandwidth (EAB, RL < ?10 dB) of 3.03 GHz at 2.51 mm, indicating the excellent EMW absorption properties of Fe/C/SiCN composite ceramics. 相似文献
Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO3 (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO3 at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO3 in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains. 相似文献