Effect of rhenium addition on isothermal oxidation behavior of single-crystal Ni-based superalloy

The isothermal oxidation behavior of a nickel-based superalloy, which we designate as DD32, containing 4 wt.% rhenium and another alloy (DD32M) without rhenium were investigated at 900, 1000 and 1100 °C. Oxidized alloys were characterized by SEM, EDX, EPMA and XRD. The two alloys revealed similar oxidation rates at 900 °C, while the DD32 alloy showed a slightly higher mass gain than that of the DD32M alloy during 1000 and 1100 °C exposure. Surface and cross-sectional examination indicated that DD32 alloy showed nonuniform oxidation between dendritic and interdendritic areas at all temperatures. Similar different oxidation behavior between dendritic and interdendritic regions was also observed in the DD32M alloy at 900 °C. However, DD32M showed relatively uniform oxidation at 1000 and 1100 °C exposure. Therefore, Re addition clearly induced the nonuniform oxidation of the alloy.     

SnAgCuY系稀土无铅钎料显微组织与性能研究

研究了添加微量稀土Y对Sn3.8Ag0.7Cu钎料合金显微组织和性能的影响,通过对钎料的熔化温度、润湿性能、接头剪切强度的测试及显微组织观察,指出含微量稀土的SnAgCuY合金是性能优良的无铅钎料合金,同时确定了最佳的Y含量范围.     

HSi80-3硅黄铜船用舵盖铸件精铸工艺的凝固模拟

运用Procast软件对HSi80-3硅黄铜船用舵盖零件在两种浇注工艺方案下的凝固过程进行模拟计算,在此基础上分析探讨了该铸件可能产生缩孔或缩松的部位。模拟显示第一种浇注工艺会在零件主体部位产生严重缩孔,而第二种浇注工艺则能自下而上顺序凝固,避免缩孔或缩松的产生,据此确定了第二种铸造工艺方案,并采用试验进行验证。结果表明,此浇注工艺没有产生技术要求缺陷,证明了凝固模拟的可行性。     

再结晶退火对Ni_（47）Ti_（44）Nb_9合金冷轧板相组成及板材织构的影响

采用Ｘ射线衍射术和ＯＤＦ研究了再结晶退火对Ｎｉ４７Ｔｉ４４Ｎｂ９合金冷轧板相组成和织构的影响。结果表明，冷轧板材的相组成为Ｂ２＋β－Ｎｂ＋Ｂ１９＇；织构类型为面织构｛００１｝ｐ＋｛１１０｝ｐ再结晶退火期间，马氏体相Ｂ１９＇逆转变为母相Ｂ２，合金的相组成为：Ｂ２十β－Ｎｂ，而再结晶织构为：｛００１｝＜１１０＞ｐ。     

直角密集台阶轧齐曲线

本文在分析具有密集性质的直角台阶轧齐问题中，提出里台阶轧齐曲线相对独立，外台阶轧齐曲线受里台阶影响，并形成某种叠加的基本设想。逐个分析了密集台阶存在的四种状态，推导出各种状态下每个台阶的轧齐曲线方程，并给出了各种状态的判别式及各方程的区间。文章最后以简图方式汇总了各种状态，并用例题归纳了计算步骤。     

搅拌工具尺寸和工艺参数对塑料搅拌摩擦焊焊缝质量的影响

用不同尺寸的搅拌工具对聚氯乙烯(PVC)板材进行了搅拌摩擦对接焊工艺试验.试验证明,在搅拌工具肩部直径为30 mm,搅拌头直径为10 mm,搅拌头旋转速度为1 660 r/min,焊接速度为25 mm/min的情况下,可以得到焊缝饱满、成形美观的焊接接头.提高搅拌头的旋转速度可以成比例地提高焊接温度;焊接速度的影响较复杂,增大焊接速度一方面会降低焊接热输入,一方面又会间接地增大搅拌头的进给阻力,从而增大摩擦发热功率,提高焊接温度;搅拌工具肩部直径直接影响肩部与被焊材料表面的摩擦发热功率,增大肩部直径可以提高焊接温度,还有利于阻止焊缝材料的飞溅和外溢;而搅拌头直径的影响较复杂,增大它既可以提高搅拌头侧面与被焊材料之间的相对运动线速度,从而提高焊接温度,又会增加被焊材料的吸热功率和传热面积,从而降低焊接温度.     

江苏油田涂层防腐现状及发展要求

本文简单介绍了小断块油气田油气管道、储罐的内外腐蚀环境、腐蚀状态，防腐措施及控制效果。     

20G高压锅炉管裂纹原因分析

对20G高压锅炉管产生裂纹的原因进行了分析，结果表明是冷拔工艺不当所致。     

LF2铝合金搅拌摩擦焊接头的疲劳特性

对LF2铝合金搅拌摩擦焊接头的疲劳特性进行了研究，建立了焊接头的S-N曲线。疲劳试验结果表明，搅拌摩擦焊接头表现出良好的疲劳性能，疲劳寿命N=10^6次的疲劳强度值约为59～65MPa。搅拌摩擦焊接头具有细小的等轴晶粒和狭窄的热影响区，阻碍了滑移带的形成和裂纹的扩展，从而提高了接头的疲劳性能。疲劳断口分析显示，随着驻留滑移带的扩展逐渐萌生裂纹，在交变应力作用下最终导致失效。     

Low vibration control system in turning

This paper presents a system developed for on-line vibration control on a CNC lathe. The on-line vibration control system is composed of two subsystems, namely, the vibration monitoring subsystem, and the vibration reduction subsystem. A simple chatter criterion was adopted in the vibration monitoring subsystem in order to detect the occurrence of chatter as soon as possible. The vibration reduction subsystem is then triggered to suppress vibrations when chatter was detected. It was shown that chatter can be detected by comparing the standard deviation of signal collected on-line to an off-line experimentally determined value. The vibration reduction subsystem provides possible ways to reduce vibrations by adjusting cutting parameters including cutting speed and feed rate. Series of experimental tests were conducted to verify the feasibility of the proposed system. It was shown that the proposed system can generally detect the occurrence of chatter and reduce vibrations effectively when chatter occur.