A novel temperature-tolerant foamed resin for enhanced oil recovery

The synthesis and performance of a novel temperature-tolerant foamed resin for enhanced oil recovery were investigated using various methods, including infrared, NMR, scanning electron microscopy (SEM), and displacement experiments. Polycondensation of furfuryl alcohol prepolymers was confirmed by the infrared and NMR results. The poor temperature tolerance of furfuryl alcohol prepolymers after gelation at high temperatures is mainly due to the fracture of furan rings. The addition of ester additives is an effective method of increasing the temperature tolerance of the prepared foamed resins and can effectively reduce the weight-loss rate of the polycondensation products. The SEM results show that the skeleton structure of the foamed resin remains intact after high-temperature treatment. Thus, the novel plugging agent system has excellent thermal stability and still has a high strength (>0.8 MPa) after high-temperature aging treatment for 40 days, giving the prepared foamed resin a good plugging performance (plugging rate > 91%) at 250 °C. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47161.     

Manganese ferrite-polyaniline hybrid materials: Electrical and magnetic properties

Magnetic MnFe₂O₄ nanopowders were synthesized by an original solvothermal method in the absence and in the presence of tetra-n-butylammonium bromide (TBAB) and Tween 80 (TW) as surfactants. Manganese ferrite/polyaniline (PANI) hybrid materials were synthesized by in situ polymerization of aniline on the surface of MnFe₂O₄ using ammonium persulfate as oxidant. The purpose of the study was to investigate the influence of the two surfactants on the properties of the MnFe₂O₄ powders and of their composites with PANI. The specific surface area, the cumulative surface area of pores and the cumulative volume of pores are influenced by the nature of surfactant in case of MnFe₂O₄ powders and are higher by comparison to those of the MnFe₂O₄/PANI hybrid materials. The values of saturation magnetization in case of MnFe₂O₄ powders are higher than those of the hybrid materials and are not influenced by the surfactant nature. These features revealed that MnFe₂O₄ powders can be efficiently used as adsorbents for the purification of wastewaters. The values of the electrical conductivity of the composites exhibit a significant increase in comparison to the MnFe₂O₄ powders and depend on the surfactant nature. The highest value of electrical conductivity was achieved by the composite obtained using Tween 80 as surfactant (σ_DC = 54.5·10^?5S?m^?1) which was close to that of PANI (σ_DC = 61.2·10^?5 S?m^?1). The fact that the magnetic and electric properties of the synthesized MnFe₂O₄/PANI composites can be changed by design, demonstrate the high potential of these materials to be used in magneto-electric applications.     

N-Substituted Nipecotic Acids as (S)-SNAP-5114 Analogues with Modified Lipophilic Domains

Potential mGAT4 inhibitors derived from the lead substance (S)-SNAP-5114 have been synthesized and characterized for their inhibitory potency. Variations from the parent compound included the substitution of one of its aromatic 4-methoxy and 4-methoxyphenyl groups, respectively, with a more polar moiety, including a carboxylic acid, alcohol, nitrile, carboxamide, sulfonamide, aldehyde or ketone function, or amino acid partial structures. Furthermore, it was investigated how the substitution of more than one of the aromatic 4-methoxy groups affects the potency and selectivity of the resulting compounds. Among the synthesized test substances (S)-1-{2-[(4-formylphenyl)bis(4-methoxyphenyl)-methoxy]ethyl}piperidine-3-carboxylic acid, that features a carbaldehyde function in place of one of the aromatic 4-methoxy moieties of (S)-SNAP-5114, was found to have a pIC₅₀ value of 5.89±0.07, hence constituting a slightly more potent mGAT4 inhibitor than the parent substance while showing comparable subtype selectivity.     

Hydroxyapatite/tricalcium silicate composites cement derived from novel two-step sol-gel process with good biocompatibility and applications as bone cement and potential coating materials

Tricalcium silicate (C₃S) and hydroxyapatite (HAp) composites were fabricated through the sol-gel process. The aim of this research is to improve the biocompatibility of C₃S through HAp addition and study the potential of using this as coating materials. The composites (HAp/C₃S) were characterised by Fourier transform infrared spectrometry, thermal gravity-differential thermal analysis and X-ray diffraction. The working and setting times of cement pastes were tested using Gillmore needle. Mechanical properties were examined by nanoindentation and material testing system. In vitro biocompatibility of the materials were studied by cell attachment and viability of L929 and MG-63 cells. HAp/C₃S as a coating material on gelatin film were measured with the surface roughness and imaged by scanning electron microscope. With the addition of HAp, no undesirable free CaO was detected with the synthesis by the sol-gel preparation. The pH values of HAp added groups were between 7.54 and 8.76, which were much lower than pure C₃S group (pH?=?11.75). For in vitro studies, the presence of HAp could effectively enhance the cell attachment and viability of both L929 and MG-63 cells grown in the extract or directly on the composites. However, the mechanical properties of the composites were impaired as compared to pure C₃S. Lastly, HAp/C₃S cement could be evenly coated on gelatin film. HAp is successfully demonstrated to improve C₃S biocompatibility with this new composites HAp/C₃S. C-75 (75% C₃S and 25% HAp), in particular, has good biocompatibility, relatively high compressive strength and can be uniformly coated onto gelatin film. Thus, C-75 is a promising material for further investigation as a coating on other biopolymers.