Experimental investigation of unconfined spherical and cylindrical flame propagation in hydrogen-air mixtures

This paper presents results of experimental investigations on spherical and cylindrical flame propagation in pre-mixed H₂/air-mixtures in unconfined and semi-confined geometries. The experiments were performed in a facility consisting of two transparent solid walls with 1 m² area and four weak side walls made from thin plastic film. The gap size between the solid walls was varied stepwise from thin layer geometry (6 mm) to cube geometry (1 m). A wide range of H₂/air-mixtures with volumetric hydrogen concentrations from 10% to 45% H₂ was ignited between the transparent solid walls. The propagating flame front and its structure was observed with a large scale high speed shadow system. Results of spherical and cylindrical flame propagation up to a radius of 0.5 m were analyzed. The presented spherical burning velocity model is used to discuss the self-acceleration phenomena in unconfined and unobstructed pre-mixed H₂/air flames.     

Facile growth of novel morphology correlated Ag/Co-doped ZnO nanowire/flake-like composites for superior photoelectrochemical water splitting activity

In this paper, novel morphology correlation between silver nanowires (AgNWs) and cobalt (Co)-doped ZnO (Co-ZnO) flake-like thin films (nanowire/flake-like) has been proposed for enhanced photoelectrochemical (PEC) water splitting activity. Here in, high-quality AgNWs/Co-ZnO heterostructures enabled superior visible light water splitting activity compared to the pure ZnO and AgNWs/ZnO. To address the strategic effect of AgNWs coupling and transition metal (Co-2?at%) doping into the ZnO host lattice, we have carried out the X-ray diffraction, field emission scanning microscopy, X-ray photoelectron spectroscopy, UV–Vis transmittance, water contact angle and PEC analyses. In this way, PEC water splitting activity was mainly examined by linear sweep voltammetry (I-V), amperometric I-t and photoconversion efficiency (η) studies. The experimental results provide clear evidence of morphology correlation between AgNWs and Co-ZnO flake-like structures for strong visible light absorption. Specifically, AgNWs/Co-ZnO composites exhibited significant enhancement in the photocurrent density (7.0?×?10^?4 A/cm²) than AgNWs/ZnO (3.2?×?10^?4 A/cm²) and pure ZnO (1.5?×?10^?6 A/cm²). As a result, detailed AgNWs/Co-ZnO geometry has great potential for photoconversion efficiency (0.73%). In a word, the merits of controllable AgNWs/Co-ZnO heterostructure are proposed to improve the visible light harvesting and charge carrier generation for energy conversion devices.     

Towards optimization of the osmotic drying process of alumina-gelatin objects: Regression analysis and verification

In this study, further analysis of the osmotic drying process was conducted to identify the optimum combination of parameters for drying rectangular alumina-gelatin beams. This study was designed to determine the effect of three variables related to the osmotic drying process (osmotic pressure, molecular weight, and immersion time) on the interaction between the liquid desiccant and the submerged alumina-gelatin samples. The water loss from the alumina-gelatin samples was positively correlated with the molecular weight, osmotic pressure, and immersion time. Up to 40% by weight of the initial water content was removed during the osmotic drying process. The samples also experienced solids gain due to the counterflow of solute from the liquid desiccant. The least amount of solids gain resulted from drying for the shortest immersion time at low osmotic pressure and high molecular weight. Evidence of possible interactions between variables was noted for the sintered density metric. Statistical methods were used to form regression equations for the measured responses (water loss, solids gain, bulk density). A verification experiment was conducted to compare the experimental outcomes to the predicted outcomes. The responses were simultaneously optimized to identify the combination of variable settings required to meet specified goals. In order to maximize water loss, minimize solids gain, and maximize bulk density, the ceramic-gelatin object should be immersed for approximately 60?min in an aqueous solution of 100,000?g/mol poly(ethylene oxide) at an osmotic pressure of 2.50?MPa. These values are valid for the range of parameter settings tested and the sample fabrication and drying methods used.     

A robust feature extraction with optimized DBN-SMO for facial expression recognition

Multimedia Tools and Applications - Facial expression is the most common technique is used to convey the expressions of human beings. Due to different ethnicity and age, faces differ from one...     

Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.