将填充热丝应用到高光束质量、长焦距的光纤激光窄间隙焊接中,不锈钢母材通过激光加热,镍基焊丝通过电流加热,有效利用复合热源的优势,提高了焊丝过渡稳定性和熔覆效率。通过高速摄像机对送丝过程进行在线观察,分析工艺参数对焊丝过渡的影响。研究不锈钢和镍基合金异种金属窄间隙焊接接头的凝固组织,并对焊缝金属进行元素分布扫描。研究发现,由焊丝电流和送丝速度等工艺参数决定的送丝稳定性是影响填充热丝激光焊接质量的最主要因素。对于窄间隙焊接,采用与间隙宽度相当的离焦光斑激光热导焊,可形成较好的侧壁熔合,由熔融金属曲面和侧壁构成的激光反射是侧壁熔合的主要原因。焊缝冷却速度较快,焊缝金属的凝固组织呈明显的对生生长,在坡口侧壁附近其生长方向与侧壁近似垂直,焊缝不存在宏观偏析。在间隙底部直角处容易出现未熔合现象,采用底部圆弧过渡的U型坡口后,可较好地解决底部未熔合问题,获得了无宏观缺陷的焊接接头。     

A Quaternary van der Waals Ferromagnetic Semiconductor AgVP2Se6

The recent realization of 2D magnetism in van der Waals (vdWs) magnets holds promise for future information technology. However, the vdWs semiconducting ferromagnets, which remain rare, are especially important in developing 2D magnetic devices with new functionalities due to the possibility of simultaneous control of the carrier charge and spin. Metal thiophosphate (MTP), a multifunctional vdWs material system that combines the sought‐after properties of complex oxides, is a promising vdWs magnet system. Here, single crystals of a novel vdWs ferromagnetic semiconductor MTP AgVP₂Se₆ with a room‐temperature resistivity of 1 Ω m are successfully synthesized. Due to the nature of vdWs bonding along the c‐axis, the magnetic properties of the few‐layer AgVP₂Se₆ with different thicknesses are characterized on the exfoliated samples. The AgVP₂Se₆ flakes exhibit significant thickness‐dependent magnetic properties, and a rectangular hysteresis loop with a large coercive field of 750 Oe at 2 K and an undiminished Curie temperature of 19 K are observed in the 6.7 nm AgVP₂Se₆ flake. The discovered vdWs ferromagnet AgVP₂Se₆ with semiconducting behavior will provide alternative platforms for exploring 2D magnetism and potential applications in spintronic devices.     

An evaluation method of the fluctuation characteristics of photovoltaic systems by using frequency analysis

Short-time fluctuations in solar irradiance will become an important issue with regard to future embedded photovoltaic (PV) systems. However, when PV systems are intensively installed, fluctuation of total output in clustered PV systems is not remarkable because there is the smoothing effect of irradiance in certain areas. In this paper, a new estimation method of irradiance fluctuation, which is based on the combination of the Fourier transform and the wavelet transform methods, is described.     

Preparation and properties of CuInS2 thin film prepared from electroplated precursor

Thin CuInS₂ films were prepared by sulfurization of Cu/In bi-layers. First, the precursor layer was electroplated onto the treated surface of Mo-coated glass. Observation of the cross-section prepared by focused ion beam (FIB) etching revealed that the void-free film was initially formed on the top surface of the precursor layer and continued to grow until the advancing front of the film reached the Mo layer. The nucleation of voids near the bottom of the CuInS₂ film followed. To determine whether the condition of the Cu/In alloy influences the CuInS₂ quality we investigated the Cu/In alloy state using FIB. We found that the annealed precursor of low Cu/In ratio (1.2) has several voids in the mid position in the layer compared with Cu-rich precursor (1.6). The cross-sectional view of the Cu-rich absorber layer is uniform compared with the low copper absorber layer. Thin film solar cells were fabricated using the CuInS₂ film (Cu/In ratio: 1.2) as an optical absorber layer. It was found that the optimization of a sulfurization period is important in order to improve the cell efficiency. We have not yet obtained good results with high Cu-rich absorber because of a blister problem. This blister was found before sulfurization. So, we are going to solve this blister problem before sulfurization.     

A formation of compatible poly(vinyl alcohol)/alumina gel composite and its properties

A formation of poly(vinyl alcohol) (PVA)/alumina gel composite was investigated with a viewpoint of compatibility of the composite. An alumina sol was prepared from aluminium iso-propoxide (Al(iPro)₃). The alkoxide was hydrolyzed and the resultant hydrate was peptized to a clear sol with acetic acid. The composite were transparent in whole content of alumina. The effects of dispersed alumina on the sorption of water and mechanical properties of composite were examined. The composites containing PVA 40–50% are flexible. They are folded in various forms and can be drawn five times the initial length in humid state. The residues obtained by calcination to remove PVA at 600°C keep its original form and transparency.     

Polymerization of [2,5-bis(trifluoromethyl)phenyl]acetylene and polymer properties

Summary [2,5-Bis(trifluoromethyl)phenyl]acetylene [BTFPA; HCCC₆H₃-2, 5-(CF₃)₂]polymerized with W, Mo, and Nb catalysts to produce methanol-insoluble polymers in high yields. The poly(BTFPA) produced by the W(CO)₆-based catalyst at 30 °C was soluble in p-(CF₃)₂C₆H₄, and had relatively high molecular weight ([]=0.352 dL/g in p-(CF₃)₂C₆H₄). The main chain of the polymer was composed of alternating double bonds, and the polymer was a dark brown solid. The temperature at which the weight loss of the polymer started was higher than 300 °C. The polymerization behavior and polymer properties for BTFPA are compared with those for phenylacetylene and [o-(trifluoromethyl)phenyl]acetylene.     

Male pheromone of swift moth,Hepialus hecta L. (Lepidoptera: Hepialidae)

(R)-6-Ethyl-2-methyl-2,3-dihydro-4H-pyran-4-one, (1R,3S,5R)-3-ethyl-1,8-dimethyl-2,9-dioxabicyclo[3.3. 1]non-7-ene, and (1R,3S,5R)-3-ethyl-1,8-dimethyl-2,9-dioxabicyclo[3.3.1]non-7-en-6-one represent the main components in the male pheromone of the swift moth,Hepialus hecta. The amounts of the three components were 40, 5, and 5 g per male, respectively. Structure elucidation of the compounds was based on spectroscopic data as compared to synthetic reference samples. The absolute configurations were determined by gas chromatography on chiral stationary phases; optically active samples served as reference compounds. Electrophysiological and behavioral experiments with natural material and synthetic samples clearly showed the three heterocyclic compounds to act as pheromones. (E, E)--Farnesene represents the main component of the scent secretion of maleHepialus humuli.     

Contrasting effects of water-soluble and water-insoluble dietary fibers on bile acid conjugation and taurine metabolism in the rat

The effect of the type of dietary fiber on the bile acid and taurine metabolism was examined in rats. Diets containing 10% of various water-soluble fibers (citrus pectin, konjak mannan, guar gum) as compared to a fiber-free diet increased biliary excretion of total bile acids. In contrast, water-insoluble dietary fibers (cellulose, corn bran, chitin; 10% in the diets) as well as cholestyramine (5% in the diet) considerably, decreased bile acid excretion. Water-soluble dietary fibermediated increases in bile acid excretion were totally attributable to increases in glycine-conjugates. Thus, these fibers greatly increased by the bile acid glycine-to-taurine ratio (G/T). Excretio of glycine conjugates decreased more than that of taurine conjugates in rats fed various water-insoluble dietary fibers. As a results, G/T in rats fed water-insoluble fibers was significantly lowered as compared to G/T in animals fed a fiber-free diet. Cholestyramine did not affect the G/T ratio of bile acids. Fecal bile acid excretion and the activities of hepatic cholesterol 7α-hydroxylase (EC 1.14.13.17) in rats fed various water-soluble dietary fibers approximately doubled as compared to the respective values for rats fed a fiber-free diet. Whereas cholestyramine greatly increased these parameters, water-insoluble fibers did not significantly affect them. Various water-soluble fibers decreased hepatic concentration and urinary excretion of taurine as well as the activity of hepatic cysteine dioxygenase (EC 1.13.11.20). In contrast, water-insoluble fibers considerably increased hepatic taurine concentrations and enzyme activities. The parameters for taurine metabolism were unaffected by cholestyramine. It was suggested that the types of dietary fiber affected hepatic taurine synthesis and thus modified bile acid glycine/taurine ratios.     

Far infrared reflection spectra in narrow-gap semiconductors

Far infrared reflection spectra of Cd_XHg_1?X Se are measured in the region 20 to 600 cm^?1 at temperatures between 5 and 77 K. Reflection spectra are explained well by the dynamic dielectric function which is constructed as a sum of Γ₈?Γ₈ interband, intraband and phonon contributions. The plasmon-LO phonon coupling effect is also discussed.