Observation of large diamagnetism in La-Sr-Nb-O films up to room temperature

Large diamagnetic transitions along with sharp resistive transitions were observed in the La-Sr-Nb-O system near room temperature (290 K). The amplitude of the diamagnetism reaches 35% of that of a pure Nb sheet. In addition, a behavior similar to weak magnetic spin ordering was observed for some samples at a temperature of about 290 K, over a temperature range of 30 K. The diamagnetism reappears above this temperature and continues up toT 320 K. It is not clear what composition ratio of La-Sr-Nb-O is responsible for this large diamagnetism and the high critical temperature. The yield probability of these samples is around 50%. The characteristics of the samples having not passed through many thermal cycles remain stable for about 1 month.     

Possibility of superconductivity with highT c in La-Sr-Nb-O system

We prepared La-Sr-Nb-O system samples both in bulk form and as a film, with sharp resistive transitions at temperatures of 228–323 K, depending on the annealing conditions. The sharp resistive transitions might be attributable to superconductivity. Magnetic ordering was observed over a narrow temperature range around 40 K for some of the samples.     

Polymorphic behavior of gondoic acid and phase behavior of its binary mixtures with asclepic acid and oleic acid

Molecular properties of polymorphic forms of gondoic acid [cis-C_20:1Δ11ω9 (GOA)] have been studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC), optical microscopy, and Raman scattering, in comparison to those of six principal unsaturated fatty acids: oleic acid [cis-C_18:1Δ9ω9 (OA)], erucic acid [cis-C_22:1Δ13ω9 (ERA)], petroselinic acid [cis-C_18:1Δ6ω12 (PSA)], asclepic acid [cis-C_18:1Δ11ω7 (APA)], palmitoleic acid [cis-C_16:1Δ9ω7 (POA)], and elaidic acid [trans-C_18:1Δ9ω9 (ELA)]. In addition, phase behavior of binary mixtures of GOA and APA and OA was examined by XRD and DSC. The polymorphic structures of GOA are quite similar to those of APA, ERA, POA, and partly to OA. In particular, DSC and Raman scattering studies have shown that gondoic acid exhibits conformational disordering on heating at the ω-chain, a chain segment between the double bond and CH₃ group, as a transition from all-trans (γ form) to gauche-rich (α form) conformations. A miscible mixing phase was observed in the mixture of GOA and APA, yet eutectic phases were observed in the GOA and OA mixtures. This is a remarkable contrast because the binary mixture systems of varying combinations of cis-unsaturated fatty acids examined so far exhibited either eutectic nature or molecular compound formation. It is expected that specific molecular interactions between GOA and APA that originate from the equivalence of the length of the Δ-chain, the chain segment between the cis-double bond and COOH group, and also from the presence of the γ-α order-disorder transformation would be operating to form the miscible mixing phase.     

Hybrid negative example selection using visual and conceptual features

An application of Query-By-Example (QBE) is presented where shots that are visually similar to provided example shots are retrieved. To implement QBE, counter-example shots are required to accurately distinguish shots that are relevant to the query from those that are not (Li and Snoek (2009), Yu et al. (2004)). However, there are usually a huge number of shots, not relevant to a particular query, which can serve as counter-example shots. It is difficult for a user to provide counter-example shots that would aid retrieval. Thus, we developed a QBE method based on partially supervised learning where a retrieval model is constructed by selecting counter-example shots from shots without user supervision. To ensure the speed and accuracy of the QBE method, we select a small number of counter-example shots that are visually similar to given example shots but irrelevant to the query. Such shots are useful for characterizing the boundary between relevant and irrelevant shots. For our method, we first filter shots that are visually dissimilar to example shots based on SVMs on a visual feature. Then we filter shots relevant to the query based on concept detection results from pre-constructed classifiers. Shots that pass the above two tests are considered as counter-example shots. Experimental results obtained using TRECVID 2009 video data validate the effectiveness of our method.     

Lysozyme requires fluctuation of the active site for the manifestation of activity

Mutations around His15 which lie far away from the active site,stimulated glycol chitin activity of lysozyme at physiologicaltemperature. Del-Argl4Hisl5 lysozyme, a mutant lysozyme whoseArgl4 and Hisl5 were deleted together, and has the highest activityamong these mutant lysozymes, had a similar binding abilityto a trimer of N-acetyl-glucosamine, a substrate analogue, relativeto native lysozyme. This suggests that the increased activitywas due to an increased k_cat in the catalysis reaction. TheH-D exchange rate of the N-1 proton in the Trp63 which is locatedin the active site cleft, was enhanced in the Del-Argl4Hisl5lysozyme, while 2-D proton NMR analysis revealed no conformationalchange around Trp63. We conclude that some sort of fluctuationat the active site might be required for the manifestation ofactivity. This theory is supported by the finding that the Del-Argl4Hisl5lysozyme showed a shift in temperature dependency of activityto lower temperatures compared with that of native lysozyme.     

Pervaporation via silicon-based membranes: Correlation and prediction of performance in pervaporation and gas permeation

Pervaporation (PV) is a membrane technology that holds great promise for industrial applications. To better understand the PV mechanism, PV dehydrations of various types of organic solvents (methanol, ethanol, iso-propanol, tert-butanol, and acetone) were performed on five types of organosilica and two types of silicon carbide-based membranes, all with different pore sizes. Water permeance was dependent on the types of organic aqueous solutions, which suggested that organic solvents penetrated the pores and hindered the permeation of water. In addition, water permeance of various types of membranes in PV was well correlated with hydrogen permeance in single-gas permeation. Furthermore, a clear correlation was obtained between the permeance ratio in PV and that in single-gas permeation, which was confirmed via the modified-gas translation model. These correlations make it possible to use single-gas permeation properties to predict PV performance.     

Magnetic order and evolution of the electronic state aroundx=0.12 in La2?xBaxCuO4 and La2?xSrxCuO4

Muon spin rotation ( ⁺SR) measurement provides clear evidence of the antiferromagnetic order of Cu moments below 35 K for La_2–x Ba _x CuO₄ and below 15 K for La_2–x Sr _x CuO₄ in the narrow range ofx where the high-T _c superconductivity (SC) is suppressed remarkably. The results suggest that the change of the electronic state coupled with the lattice instability is relevant to the local suppression of SC and freezing of spin fluctuations of the Cu moment.     

Sensory evaluation of beef patties and sausages containing lipids with various component fatty acids

Sensory scores of beef patties and emulsion-type sausages containing varying levels of lipids with various component fatty acids were investigated. Sensory scores of beef patties containing solid fat were relatively constant at every fat level examined. However, scores of beef patties containing liquid oil decreased with increasing level of added oil. In the case of sausages, on the other hand, sensory evaluation scores markedly decreased with increasing the level of solid fat, while no significant change was observed in panel scores when liquid oil was mixed into sausages. Even 10% level of added lipids satisfactorily gave preferable acceptability to beef patties and sausages.     

Phonon anomalies in YNi2 11B2C

Recently we have discovered a new peak with phonon character which appears only below T_c in an intermetallic superconductor, YNi₂ ¹¹B₂C (Tc14-2K) by neutron inelastic scattering measurements. The peak intensity of the new peak shows the order-parameter-like temperature dependence of the superconductivity. The new peak grows by absorbing the spectral weight from the above-lying soft phonon mode. In the present study we investigate the magnetic field dependence of the new peak. With increasing magnetic field, the new peak is gradually suppressed and disappears by H=H_c2 (4.7T at T=5.5K). Beyond H_c2, the profile of the scattering function recovers that of the non-superconducting state above T_c These results strongly indicate that this new peak is undoubtedly associated with the superconducting state in YNi₂ ¹¹B₂C.     

Characteristics of sol-gel derived PZT thin films with lead oxide cover layers and lead titanate interlayers

The sol-gel derived PbZr_0.53Ti_0.47O₃ (PZT) films were fabricated on the bare Pt/Ti/SiO₂/Si substrates or the same substrates coated by the PbTiO₃ (PT) interlayers. The post-deposition annealing temperature and time were optimized when the PbO cover layers and PbO vapour-containing atmosphere were compared with each other and adopted as the method to diminish the lead-loss problem during the high-temperature post-deposition annealing. The X-ray diffraction patterns, microstructures, and electrical properties such as relative permittivity, _r, remanent polarization, P _r, and coercive electrical field, E _c, were investigated in relation to the annealing conditions. The PZT films deposited on the bare Pt/Ti/SiO₂/Si substrates under the PbO vapour-containing atmosphere showed better electrical properties. This indicates that the PbO vapour-containing atmosphere may be the better method of lead-loss-prevention to process the lead-containing films rather than the PbO cover layer method. The electrical characteristics of the PZT films, _r=1150, a dissipation factor of 0.039, P _r=26 C cm^–2, and E _c=40.5 kV cm^–1 were measured at 1 kHz. When PZT films were deposited on substrates coated by the PT layers, PZT-PT films with single perovskite phase were derived by post-deposition annealing at 500 °C for 1 h. However, the relative electrical properties are very poor, i.e. E _r=160, P _r=2.0 C cm^–2 and E _c=75 kVcm^–1. The optimum combination for preparing PZT-PT films is a 40 nm PbTiO₃ interlayer and annealing conditions of 6 h at 550 °C in a PbO vapour-containing atmosphere; the derived films exhibit electrical properties of E _r=885, P _r=21.5 C cm^–2 and E _c=64 kV cm^–1. The combination of inserting a PT interlayer and annealing in a PbO vapour-containing atmosphere can prevent the formation of electrical short paths. In this case, nearly pin-hole-free PZT films can be grown on the PT (interlayer) /Pt/Ti/SiO₂/Si substrates. It is believed that it is possible to prepare the PZT films with nano-scale uniformity, reproducible quality, which may be worth considering for commercial applications.