Reduction of defects and improvement in the performance of blue phosphor for thick‐dielectric electroluminescent displays using Color‐by‐Blue

Abstract— Defect‐free large‐area inorganic thick‐dielectric EL (TDEL) displays using Color by Blue (CBB) technology have been successfully developed. We have achieved the world's highest blue‐phosphor luminance of 900 cd/m² for a single‐pixel device by using CBB and by optimizing the e‐beam gun configuration and the flow rate of H₂S in the vacuum chamber. By analyzing the defects on panels with triple‐pattern phosphors and CBB panels, we also found that the number of defects on CBB panels can be drastically reduced compared with those on triple‐pattern panels. The defect‐free 17‐in. VGA CBB panels show better characteristics, a high peak luminance of 600 cd/m² and a high contrast ratio of 1000:1, compared with those of triple‐pattern panels.     

Lymphatic networks in the periodontal tissue and dental pulp as revealed by histochemical study.

The structural organization and fine distribution of the lymphatic networks in the periodontal tissues (gingiva, periodontal membrane, and alveolar process) and dental pulp of animals and humans were reviewed with special reference to histochemical examination by light and electron microscopy. The distinction between lymphatics and blood vessels was made on cryostat sections of undecalcified and calcified teeth treated with EDTA solution and whole mount preparations of periodontal membranes using 5'-nucleotidase (5'-Nase)-alkaline phosphatase (ALPase) double staining. This staining procedure allowed lymphatic vessels in the periodontal tissue and dental pulp to be differentiated from blood vessels. The specificity and localization of the enzyme reactions were confirmed by comparative histochemical studies of the same specimen with light microscopy and scanning or transmission electron microscopy. Well-developed 5'-Nase-positive lymphatic networks were observed on the tissue sections and whole mount preparations of the gingiva, periodontium, and dental pulp. More lymphatic vessels were seen in the root area of the periodontium than in the cervical area. In the dental pulp, lymphatic vessels were more numerous in the central part than in the peripheral odontoblastic layer. These distributions of the lymphatic capillary networks are discussed in relation to their ability to supply lymph to the teeth.     

Properties of novel diallyl phthalate resin modified with sulfur‐containing allyl ester compounds

Sulfur‐containing allyl ester, which reacts with diallyl phthalate (DAP) resin to have allyl groups, was synthesized by the reaction of allyl phthalic acid with bisphenol having sulfur atoms. The sulfur‐containing allyl ester compound was blended with DAP resin to improve the adhesive properties to copper. By modification with sulfur‐containing allyl ester compound, the T‐peel adhesive strength and the lap shear adhesive strength to copper was improved. In particular, the adhesive strength was greatly improved when the resin was modified with the allyl ester compound having a disulfide bond (?S?S?) (DADS). It is concluded that this result is due to the improvement of the interfacial adhesive strength because the sulfur atom was found to be located in the surface of the copper by Fourier transform infrared (FTIR) analysis. The glass transition temperature (T_g) and the thermal decomposition temperature (T_d) of the cured DAP resin modified with DADS slightly decreased with increasing concentration of DADS. The lowering of T_g is because the crosslinking density of the DAP resin modified with DADS is smaller than that of DAP resin. Moreover, from thermogravimetric analysis, the lowering of Td of the DAP resin modified with DADS is because DADS is likely to pyrolyze. © 2013 Society of Chemical Industry     

Die quenching limit of AA2024 aluminum alloy billet on servo press

Die quenching of AA2024 aluminum alloy billets was carried out on a servo press with ram-motion control of WC-20 mass%Co dies directly after solution heat treatment (SHT). To clarify the dependence on billet size for die quenching, two billets with a height of h₀ = 8 mm or 16 mm and with the same diameter of 16 mm were prepared. The cylindrical billets were heated in an electric furnace at 823 K and transferred to the press. Then the billets were uniaxially compressed with a reduction in height (Δh/h₀) of 2% or 5%, and further held between the dies. The sandwiching duration by dies (t_d.q.) was varied from 0 to 8 s. Based a measured temperature change, hardness and TG–DTA analysis, it is found that die quenching is successfully carried out without precipitation hardening only in the case of the billet with a height of 8 mm and t_d.q. > 6 s. The reduction in height is limited less than 5% by intergranular fracture on side surface of billet during the die quenching process.