气体试样表面质量对氧含量的影响

低氧含量钢种是目前各钢铁企业开发的主要品种，尤其是齿轮钢、气瓶钢等对氧含量的要求较严，所以准确测定钢中的氧含量也是控制钢材性能指标的一种手段。     

高炉型熔渣中TiO2的活度

在1500℃下用金属Sn作熔剂,石墨作还原剂,采用“熔渣—金属Sn”化学平衡法和相图计算法,得到了高炉型熔渣中TiO_2的活度,并讨论了渣中TiO_2的活度和活度系数随其浓度变化的规律。     

Si对低碳贝氏体钢组织和性能的影响

Si在一定含量范围内,使低碳贝氏体钢中粒状贝氏体相对量、M—A岛体积分数、残余奥氏体量及其稳定性增加,从而提高钢的强度和韧性。在v_t=156℃/min冷速下,Si为1.62%时,钢的强韧性出现极大值;v_t=7.9和0.9℃/min时,Si>1.99%后,大量共析铁素体的析出降低了钢的强度和韧性,Si为1.99%时,强韧性最高,最佳Si含量为1.62—1.99%。     

MICROSTRUCTURE OF SILICON CARBIDE WHISKERS

The morphology,crystal defects and chemical compositions of surfaces in two kinds of SiCwhiskers related to their growth mechanism have been studied by means of electronmicroscopy and surface chemical analyses.Based upon the experimental results,five criteriafor evaluating the whisker microstructure were suggested as:proportion of the perfect singlecrystals,morphology and dimensions,defects and their distribution,the bulk and surfacechemistries,and crystallographic characteristics.     

300M超高强度钢板条马氏体的晶体学研究

电子衍射和晶体学测量证实,300M超高强度钢板条马氏体的惯习面为{335}_A型,与奥氏体的位向关系偏离K-S关系2.5°,为G—T关系,相邻板条间绕其公共面{110}_M法线相对旋转约60°,形成板条间不同的位向关系,包括近似{112}_M孪晶关系。     

THE LOW CYCLIC FATIGUE BEHAVIOUR OF GH133 SUPERALLOY

本文研究了GH133合金的循环应力应变反应和低周疲劳性能,并作了位错结构观察.通过对比拉压对称(R=-1)试验和恒定最大正应变(ε_(max)=C)试验,证明平均拉应力起降低寿命的作用.位错结构观察证明,循环使共格γ质点的相界处产生应力场,最终导致位错的萌生和运动,位错运动又进一步增殖位错.位错运动方式是变化的,由成对切割γ′质点到单位错切割γ′质点和位错绕过γ′质点,滑移带位错结构最终可以出现饱和的梯状结构.晶界和双晶界附近位错密度高,具有位错胞结构,同时可以出现沿晶界或双晶界裂纹.     

零电阻温度85.3K的Bi系氧化物超导体

用快淬工艺成功地制成起始转变温度112K、零电阻温度85.3K的Bi-Sr-Ca-Cu新型氧化物超导体.样品在84.0 K附近呈现明显的抗磁效应.     

42CrMo钢等离子渗氮动力学的数学模型

在42CrMo钢进行等离子渗氮工艺试验的基础上,参考有关数学关系,利用电子计算机处理实验数据,初步建立了扩散层、化合物层、温度控制的数学模型,实现了微处理机控制等离子渗氮参数.实验还得出CO_2对等离子体渗氮有加速作用.     

细晶处理对镍基合金疲劳蠕变交互作用行为的影响

本文研究了两种晶粒度的GH 698合金在700℃疲劳蠕变交互作用下的断裂寿命和形变行为.结果表明:在疲劳蠕变应力交互作用下的断裂寿命可以分成F,FC和C三个区.在FC及C区,交变应力的存在明显地阻碍蠕变形变过程,提高了断裂寿命.细晶处理后使这种阻碍作用加强,断裂寿命提高幅度变大.在大应力的疲劳区进行细晶处理,反而使合金寿命降低.     

测量不确定度与误差的区别及在评定中应注意的问题

介绍了测量不确定度与测量误差的区别以及在评定中应注意的几个问题。文中结合当前国际上的一些动态就可忽略的不确定度来源、标准差的安全因子、A类评定和B类评定的应用、Up和U的选用、测量不确定度评定的简化建议等问题进行了讨论。