磁控溅射制备In2O3-SnO2薄膜与分析

选择In2LO3与SnO2质量比11的靶材为溅射源,采用磁控溅射法沉积了ITO薄膜,讨论了溅射氩气压强、氧流量、基体温度对薄膜透射率和方阻的影响,深入分析了其机理.研究结果表明溅射时采用低Ar压强更有利于降低ITO薄膜的电阻率,并确定最佳氩气压强为0.2 Pa,厚度为120 nm的ITO薄膜在可见光区的透过率可达到90%;氧流量能明显改变薄膜的性能,随着氧流量从0增加10 L/min(标准状态下,下同),载流子浓度(N)则由3.2×1020降低到1.2×1019/cm3,N值的变化与ITO薄膜光学禁带宽度(Eg)的变化密切相关.振子模型与实验结果吻合,并确定了ITO薄膜的等离子波长(λp=1 510 nm).薄膜随方阻减小表现出明显的"B-M"效应.通过线性外推,建立了直接跃迁的(αE)2模型,并确定了薄膜的Eg值(3.5～3.86 eV).     

STUDY OF INTERFACES AND SURFACES OF YBa_2Cu_3O_(7-x)-Ag

Interfaces and surfaces of YBa_2Cu_3O_(7-x)(YBCO)-Ag have been studied by SEM-EDXand AES.No effect of Ag on 123 structure in X-ray diffraction pattern was observedfor 0.4 mol Ag doped YBCO.AES analysis indicated that Ag segregated on surfaceof YBCO and resulted in decrease of YBCO-metal lead resistance.In addition,solutionand segregation of Ag as elemental state were often appeared on interfaces and surfacesof high temperature annealed YBCO,whether elemental Ag or compound Ag_2O andAgNO_3 adopted as doping material.     

黄铜中纳米级微裂纹的形核与钝化

黄铜薄膜试样在透射电镜中原位拉伸观察表明，在平衡条件下加载裂发出的位错纯化成无位错区，它是一个应变很高的异常弹性区。当缺口足够锐，外加载荷足够大时，这个非线弹性区中的应力有可能达到原子键合力，从而使纳米级微裂纹在无位错区中不连续形核，或从钝化的原裂纹顶端形核。这个微裂纹一昊形核，即使保持恒位移，也将钝化成空洞或缺口。     

生产非调质N80级石油套管的新工艺可行性实验研究

对国内生产非调质N80级石油套管的现状做了简述,在包钢φ180 mm机组上取轧卡样,用Gleeble-1500热模拟试验机测定34Mn2VN钢的动态CCT曲线并进行控冷实验.借助光镜和扫描电镜对显微组织和断口进行分析.通过实验研究,提出了一种新的生产非调质N80级石油套管的工艺,在包钢进行大批量生产试验.结果表明,选用合理的终轧温度和冷速,采用加热→穿孔→连轧→脱管→定减径→冷却,可实现大批量生产.该工艺与传统生产工艺相比有减少工序、提高生产率、节约能源的优点.     

热压变形对灰口铸铁石墨形态的影响

研究了灰口铸铁(HTl50)在900℃大压下量塑性变形后石墨的分布形态，结果表明：随着压下量的增加，石墨片逐渐趋于平行分布；变形过程中发生了碳的回溶，同时伴随着石墨片的断裂；石墨片体积分数及片间距随压下量的增加而逐渐减少。     

Magnetic and mechanical properties of FeSi alloys with high Si content

The chemical vapor（CVD） deposition-diffusion method was applied to prepare FeSi alloys with high silicon content up to 6.5%. In spite of various deposition and post-annealing, the sample remains α-Fe bcc structure. The cross section of the composition was analyzed to evaluate the Si content and distribution before and after annealing. The results show that the soft magnetic properties are improved by increasing the silicon content. For the samples containing about 6.5% Si, the coercivity decreases to 60 from 237.3 A/m of the original. It is also obtained that, in addition to the Si content, Si distribution has a large influence on the core loss due to the effect of resistivity. The micro-hardnesses were also evaluated along the cross-section after various annealings.     

(ZrAl3+ZrB2)/Al复合材料的制备和微观组织结构

采用混合盐反应法,以KBF4和K2ZrF6粉剂为原料在铝熔融体中制备了(ZrAl3 ZrB2)/Al复合材料.借助于X射线衍射仪、电子探针和透射电镜对复合材料的物像和增强相进行了观察,结果表明ZrB2颗粒呈等轴或等轴颗粒状,为六方结构,尺寸大部分小于1μm,ZrAl3相大部分呈长条状,两种增强相整体分布较为均匀,且与Al的界面光滑洁净,没有其它界面生成物.对复合材料的硬度做了测试,原位合成增强相的引入显著提高了复合材料的HRB硬度.     

40Cr钢电火花表面强化层的磨损特性研究

分析了在大接触应力的磨损条件下,表面残余应力和硬度对40Cr电火花强化层耐磨性的影响,探讨了其磨损机理。结果表明:滚动磨损和滚、滑动磨损时,随着试样表层硬度的提高,试样的耐磨性增大;强化层中的残余压应力可以提高强化层的硬度并增强其耐磨性。滚动磨损时,电火花强化层的磨损方式主要为粘着磨损、疲劳磨损和磨粒磨损三种机制;在滚、滑动磨损时,除上述三种机制外,还发生了氧化磨损。     

二氯苯同分异构体的毛细管气相色谱分析

选用聚乙二醇-20000(PEG-20M)高效石英毛细管气相色谱柱分析二氯苯异构体。在选用的色谱条件下，难分离物质间二氯苯和对二氯苯分离度达4．042。结果表明该法分离效果好，分析速度快。     

Li_20对AlN陶瓷低温烧结的影响

利用XRD,SEM和TEM研究了Li2O-CaF2-Y2O3体系在/AlN陶瓷低温烧结中的作用机理,研究发现,添加Li2O的/AlN陶瓷有着更低的收缩开始温度和更大的收缩率,这种收缩来自于含Li玻璃相与CaYAlO4液相的共同作用。在烧结过程中,Li2O不仅改变了AlN烧结过程中的相组成,而且改善了液相的性质。由于Li2O和Al2O3在l 100℃以下反应生成含Li玻璃相,使得AlN开始收缩的温度大为降低。在1 600℃以上,含Li玻璃相分解散失,有利于AlN晶界的纯化,同时,CaYAl3O7向CaYAlO4的转变以及液相CaYAlO4在烧结过程中稳定存在,保证了含Li玻璃相散失后AlN的持续收缩。