Transformation of Crystal Phase of Micron-sized Rutile TiO2 and Investigation on its Sonocatalytic Activity

The partial transformation of crystal phase of micron-sized TiO₂ powder from rutile to anatase was realized utilizing microwave irradiation in hydrogen peroxide solution. Afterwards, the ultrasound of low power was used as an irradiation source to induce the transition crystal TiO₂ powder to perform the sonocatalytic activity through the degradation of azo fuchsine in aqueous solution. The results show that the sonocatalytic activity of the transition crystal TiO₂ powder is obviously higher than that of pure micron-sized rutile and anatase TiO₂ powders. The degradation ratio of azo fuchsine in the presence of the transition crystal TiO₂ powder attains nearly 80% within 80 min ultrasonic irradiation.     

Effect of miscibility and forced compatibility on damping properties of CIIR/PAc blend

In this study, a kind of novel damping materials was prepared based on the blend of chlorinated butyl rubber (CIIR) and polyacrylate (PAc) synthesized by different molar ratio of butyl methacrylate and ethyl acrylate. Research results from experiments and analyses by employing DMA, TEM, and FTIR show that whether at a cocured system or noncocured system, it can be achieved to shift a loss peak of CIIR towards a higher temperature region and to keep the damping value from markedlly decreasing, which broadens the effective damping function area of CIIR to the vicinity of ambient temperature. In the former system, the thermodynamical miscibility of CIIR and PAc, to some extent, is predominated by the molecular design of PAc, while in the latter system, covulcanized networks play a more significant role in improving compatibility and abating the peak split, though the suppression effect of thermal stress on the transition of CIIR T_ll transition still can not be neglected. Furthermore, transition state derived from the cocuring CIIR and PAc cannot make the phase separation completely take place, and consequently results in the deformation of phase morphology of the cocured CIIR/PAc blend. It is the influence of thermodynamics miscibility and forced compatibility in different size that makes the suppression effect of foreign PAc on CIIR T_ll transition be controllable. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3127–3133, 2006     

PET/纳米SiO2复合材料的制备(Ⅱ):纳米SiO2在PET中的分散性研究

研究了分散方法、纳米材料的加入体系、分散时间、分散剂的种类及SiO2 的加入量对纳米SiO2 在PET/纳米SiO2 中分散性的影响 ,用TEM对其分散情况进行表征 ,并对其分散机理进行探讨与研究。其结果表明 :采用球磨分散法并以氨基硅烷A1 1 2 0分散剂时分散效果最佳 ;当分散时间达 7 5h时 ,分散液中SiO2 基本以纳米尺寸存在 ;将分散液加入对苯二甲酸二甲酯熔体中并在球磨状态下进行酯交换SiO2 的分散效果最好 ,1 0 0nm以下的SiO2 达 95 0 7% ;体系中随SiO2 量的增加 ,其分散性变差 ,当纳米SiO2 的加入量为 1 %～ 4 %时 ,粒径在 1 0 0nm以下的SiO2 由 88%下降到 61 %。     

高效乙烯聚合催化剂的制备——I．催化剂的制备规律

研究了新型含镁络合物的结构、性质及其用于制备高效乙烯聚合催化剂的制备规律。结果表明：将镁、有机醇以及不与镁发生“格式反应”的卤代烷相互作用可迅速发生反应形成新型含镁络合物溶液。该络合物在溶液中可析出结晶。具有特定的化学结构．可以均匀承载于多孔硅胶的孔隙中，负载TiCl4后制备出形态良好的球形高效乙烯集合催化剂。     

强酸性阳离子交换树脂催化合成氯乙酸异辛酯的研究

对采用７３２强酸性苯乙烯系阳离子交换树脂作催化剂合成氯乙酸异辛酯进行了实验研究，提出了适宜的反应条件。实验结果表明，该法酯化率高、过程简便、产物颜色浅，优于浓硫酸作催化剂。     

Low temperature SCR of NO with NH3 over carbon nanotubes supported vanadium oxides

A novel multiwalled carbon nanotube (CNTs) supported vanadium catalyst was prepared. The structure of catalyst prepared was characterized by TEM, BET, FTIR, XRD and temperature-programmed desorption (TPD) methods. The results indicated that vanadium particles were highly dispersed on the wall of carbon nanotubes. The V₂O₅/CNT catalysts showed good activities in the SCR of NO with a temperature range of 373–523 K. The Lewis acid sites on the surface of V₂O₅/CNT are the active sites for the selective catalytic reduction (SCR) of NO with NH₃ at low temperatures. It was suggested that the reaction path might involve the adsorbed NH₃ species reacted with NO from gaseous phase and as well as the adsorbed NO₂ species. The diameter of CNTs showed positive effect on the activities of the catalysts. Under the reaction conditions of 463 K, 0.1 Mpa, NH₃/NO = 1, GHSV = 35,000 h⁻¹, and V₂O₅ loading of 2.35 wt%, the outer diameter of CNTs of 60–100 nm, the NO conversion was 92%.     

3-甲基-4-硝基亚胺基全氢化-1,3,5-(口恶)二嗪的合成

3-甲基-4-硝基亚胺基全氢化-1,3,5-二嗪是合成第二代烟碱类杀虫剂噻虫嗪的重要中间体。介绍并评价了文献中所报道的合成3-甲基-4-硝基亚胺基全氢化-1,3,5-二嗪的方法。以硝基胍为起始原料成功的合成了3-甲基-4-硝基亚胺基全氢化-1,3,5-二嗪,总收率为68.2%。     

Texaco煤气化装置长周期运行影响因素分析

介绍了Texaco煤气化工艺流程,从原料煤种、水煤浆浓度、操作工艺、关键设备等几个方面讨论了影响装置长周期运行的因素,提出了延长气化装置运行周期的措施。     

北京地面沉降与地下水开采时空演变对比

区域地面沉降是世界上很多城市都要面对的一种"城市病"。地下水过量开采是这一问题最普遍的原因,北京也因此出现了严重的地面沉降问题。为了全面认识地下水开采格局变化下的地面沉降发育分布的新特点,推动实现《北京地面沉降防治规划(2013-2020年)》中的"控沉目标",对北京市从解放初期至今60多年间的地下水开采和地面沉降演变进行了时间和空间上的定性定量对比分析。结果表明:地面沉降的形成发展阶段与地下水开发利用阶段高度吻合;地面沉降中心区与地下水位降落漏斗区的时空变化高度相关;随着地下水开采深度整体上向地表以下更深层发展,主沉降层逐渐向深部(100m以下)地层转移,为地面沉降防控决策制定提供了依据。     

过氧化物交联聚乙烯的力学性能研究

采用过氧化物交联方法研究了交联聚乙烯的工艺、配方和性能，探讨了过氧化物用量对材料力学性能及凝胶含量的影响，以及炭黑、氧化锌、抗氧剂对材料性能的影响。结果表明，过氧化物交联聚乙烯的力学性能有一定的提高，随着DCP含量的增加，交联PE的凝胶含量提高，而随着凝胶含量的提高，交联PE的拉伸强度提高，断裂伸长率下降；炭黑对材料有一定的补强作用，氧化锌的加入有助于交联反应和拉伸强度的提高。