研究了全层片状组织Ti-Al基合金的室温拉伸性能与品团尺寸的关系。Ti-Al基合金的室温拉伸屈服强度和断裂强度与晶团尺寸成Hall-Petch关系。当合金中添加替代元素Cr和Nb时，其Hall-Petch斜率不变；而添加间隙元素C和B时，其Hall-Petch斜率增加。Ti-Al基合金的室温延伸率与晶团尺寸不满足Hall-Petch关系。     

Fe(Ⅲ)改性膨润土光催化降解水溶液中的4-氯苯酚

以Fe（Ⅲ）离子交换改性膨润土,制得一种多相Fenton催化剂;以4-氯苯酚为模型污染物,研究不同反应条件的影响。结果表明,复合催化剂主要含SiO2及α-Fe2O3两种晶型,Fe是以高催化活性的α-Fe2O3形式存在。复合催化剂在H2O2及紫外光的协同作用下,经60 min反应后对4-氯苯酚的降解率约100%,TOC去除率约70%,且其循环使用性能较好。在实际操作过程中,控制溶液体系的pH值为6以及H2O2与4-氯苯酚浓度比约15较为适宜;在4-氯苯酚的降解过程中,C—Cl键持续断裂,Cl-被释放出来,降解过程生成了一些不含氯的中间产物。     

Textures in high purity aluminum foils and AA3004 sheets

1　INTRODUCTIONWithincreasingdemandsofhighmaterials properties ,thetexturesinAlandAlalloysplaymoreandmoreimportantrole .Highpurityaluminumfoilsneedverystrongcubetexture ,whichwillfavorthe“channeletching”effectforhighvoltageelectrolyticcapacitors ,andAA30 0 4aluminumalloysheetsneedcertaincubetexturetosuppressthe 4 5°earingbehav iorresultingfromstrongrollingtexturecompo nents[1] .InAlandAlalloys ,heavycoldrollingwillresultinstrongβ fibertexturescomposedofthewellknownCu ({ 112 }〈111〉…     

Study On the Tribological Behavior of the Arc-added Glow Discharge Plasma Non-hydrogen Carburization On Titanium Alloy Surfaces

This paper introduces a new titanium alloys surface strengthening treatment by using the arc-added glow discharge plasmas non-hydrogen carburization technique. High purity and high strength graphite is selected as cooling cathode arc source for supplying carbon atoms and particle, which migrate to the titanium alloy(Ti6Al4V) surface and form modified layer. Thus, the hydrogen embrittlement is avoided while the tfibological behavior of the titanium alloy surface is improved in the respects of anti-friction and anti-wear ability.The tribological behavior of the modified layer under dry sliding against SAE52100 steel was evaluated on a ball-on-disc test rig. The results showed that the modified layer obtained a thickness of 30μm at 980℃, 30minutes. The microhardness of the Ti6Al4V alloy surface attained 936 HV, which was much larger than that of the Ti6AI4V alloy. The Ti6AI4V alloy was characterized by adhesion wear and scuffing under dry sliding against the steel, while the surface modified layer experienced much abated adhesion wear and scuffing under the same testing condition. This could be attributed to the carbon dement with different modalities exists in the modified layer.The modified layer showed good friction-reducing and fair anti-wear ability in dry sliding against the steel. Using the SEM,XRD and XPS, the phase structure and morphology of the carburization modified layer was analyzed.     

剪切变形方向特征对高纯铝箔轧制织构的影响

运用取向分布函数(ODF)研究了每个轧制道次的剪切变形特征对高纯铝箔轧制织构的影响.提出用中性角的相对大小来量化轧制剪切变形作用方向改变的位置,运用Taylor晶体塑性变形理论模拟计算了中性角的相对大小对轧制织构演变的影响.实测与模拟的轧制织构特征表明:中性角靠近轧制变形区的中心位置有利于形成{001}<110>剪切织构,从而证实了除剪切变形的程度外,剪切变形方向改变的位置也是影响高纯铝箔轧制织构的重要因素.     

纳米晶Fe72.8Cu1Nb1.7V1.5Mn0.5Si13.5B9软磁合金的磁性能

本文报道了高导磁纳米晶Fe72．8Cu1Nb1．7V1．5Mn0．5Si13．5B9合金的直流和交流磁性能水平，磁导率频散行为以及高频铁损行为，给出了描述高频区频散行为和铁损行为的近似表达式。     

点扩展函数与采样频率及量化精度对图像边缘的影响分析

文章在建立理想边缘成像模型的基础上,分析研究了一般成像系统的点扩展函数与空间采样频率的关系及对图像边缘定位精度的影响,给出了边缘定位误差.同时,还分析研究了量化精度对图像边缘的移位影响,给出了移位误差.最后,给出了本文的分析研究在零件视觉精密检测的应用情况.     

铁精矿粒度对球团强度的影响

以大红山、曼南坎和滇滩等精矿的粒度以及膨润土用量和润磨时间为因子,以生球落下强度、生球爆裂温度、预热球抗压强度和焙烧球抗压强度为评价指标,进行了五因子二次回归组合实验研究。结果表明:随着铁精矿小于0.074mm粒级含量的增加,生球爆裂温度下降,预热球和焙烧球抗压强度提高;当铁精矿小于0.074mm粒级含量小于75%(质量分数)时,生球落下强度逐渐上升,当小于0.074mm粒级含量为75%时,生球落下强度达到最大值,之后有下降趋势。并不是铁精矿粒度越细球团强度就会越好,铁精矿粒度还应该满足一个合适的粒度组成。     

40Cr钢电火花表面强化层的磨损特性研究

分析了在大接触应力的磨损条件下,表面残余应力和硬度对40Cr电火花强化层耐磨性的影响,探讨了其磨损机理。结果表明:滚动磨损和滚、滑动磨损时,随着试样表层硬度的提高,试样的耐磨性增大;强化层中的残余压应力可以提高强化层的硬度并增强其耐磨性。滚动磨损时,电火花强化层的磨损方式主要为粘着磨损、疲劳磨损和磨粒磨损三种机制;在滚、滑动磨损时,除上述三种机制外,还发生了氧化磨损。