防锈铝表面喷丸强化冲击试验研究

采用仪器化（数字化）冲击试验机，对防锈铝表面喷丸强化后进行冲击试验，试验结果表明：喷丸后的最大冲击力比母材提高35％，最大力前弹塑性变形功提高166％。     

熔剂对高频熔覆耐磨覆层工艺性能的影响

采用高频感应加热可以在低碳钢表面熔覆一层耐磨材料，熔剂对覆层与基体的结合、覆层表面成形、脱渣性等工艺性能起着决定性的作用。本文探讨了熔剂对高频熔覆工艺性能的影响。在Fe基Cr13Ni2B合金粉末中加入适量的焊剂431、硼酐及氟化物，可以有效地去除粉料表面的氧化物，降低其熔点，促进粉料与基体的结合．形成一层脱渣容易、表面成形美观且与基体形成牢固冶金结合的耐磨覆层，覆层厚度可以达到2．5mm。     

Research on graphite powders used for HTR-PM fuel elements

Different batches of natural graphite powders and electrographite powders were characterized by impurity, degree of graphitization, particle size distribution, specific surface area, and shape characteristics. The graphite balls consist of proper mix-ratio of natural graphite, electrographite and phenolic resin were manufactured and characterized by thermal conductivity, anisotropy of thermal expansion, crush strength, and drop strength. Results show that some types of graphite powders possess very high purity, degree of graphitization, and sound size distribution and apparent density, which can serve for matrix graphite of HTR-PM. The graphite balls manufactured with reasonable mix-ratio of graphite powders and process method show very good properties. It is indicated that the properties of graphite balls can meet the design criterion of HTR-PM. We can provide a powerful candidate material for the future manufacture of HTR-PM fuel elements.     

石英表面蚀刻保护涂料的制备及其性能

采用聚苯乙烯(PS)和丁二烯与苯乙烯的嵌段共聚物(S BS)为成膜物，以硫酸钡、聚异丁烯为填料和改性剂，并加入偶联剂，获得有较强防腐能力的蚀刻用保护涂料并筛选出最佳工艺条件.在较高温度下，该涂料对饱和氟化氢、饱和氟化氢铵溶液等强腐蚀性介质有良好的化学稳定性，可用于玻璃、石英蚀刻中的表面防腐.     

近净成形制备SiCp/Al复合材料Ⅱ:SiC预成形坯自发熔渗Z101

以超细SiC粉(W7)为原料制备的SiC多孔骨架为先驱体,采用无压渗透工艺制备出致密、增强体分布均匀的SiC/Al复合材料.SiC-Al间存在厚度为0.3～0.5 μm的界面层,该界面层能很好地被铝液润湿,并阻止铝液与SiC的接触与反应.SiC坯体渗入铝合金后无形状和尺寸的变化,能够实现制品的近净成形.加入SiC后,铝合金的强度显著提高,弹性模量提高近1倍.细颗粒的SiC能更好地抑制铝基体的热膨胀.材料的热学性能可通过SiC的含量来调整,SiC体积分数介于37%至54%之间时,室温导热系数介于136 W/(m.K)至118 W/(m.K)之间,室温至100 ℃的平均线热膨胀系数介于9.98×10.6 K.1至7.69×10.6 K.1之间.     

Preparation and properties of （K0.5Na0.5）NbO3-LiNbO3 ceramics

The lead-free piezoelectric ceramics （1-x）（K0.5Na0.5）NbO3-xLiNbO3（abbreviated as KNLN） were synthesized by a traditional solid state reaction. The effects of Li^＋ on the sintering characteristic, the phase structure and piezoelectric properties of KNLN ceramics were investigated. The sintering temperature of KNN-based ceramics is decreased by doping Li^＋ and the range of the sintering temperature is narrow. The KNLN ceramics exhibit an enhanced piezoelectric properties with the piezoelectric constant d33 value of 180-200 pC/N, The electromechanical coupling coefficients kp is 35%-40%. The results show that （1-x）（K0.5Na0.5）-NbO3-xLiNbO3 （x=0.05, 0.06） is a promising high-temperature lead free piezoelectric ceramic.     

砧座振动特性的Simulink仿真分析

以单自由度系统为力学模型，以MATLAB的组件Simulink为工具，对电动液压锻锤砧座的振动过程进行动态模拟，从而分析了砧座的振动特性。由仿真得到的振幅值与实测值较为接近。     

激光熔覆镍基粉末涂层的研究

分析了激光熔覆表面处理技术对镍基自熔性合金粉末材料性能的要求，研究了合金粉末的化学成分、微观组织及熔覆层的性能，并对涂层的耐磨性进行了分析。     

添加SnO_2组元对RuO_2 SnO_2 TiO_2/Ti钛阳极组织形貌的影响

通过溶胶凝胶 (Sol gel)法经涂刷、烧结、退火等工艺制备了添加不同含量SnO2 的RuO2 SnO2 TiO2 /Ti三元涂层钛阳极。并通过X射线衍射 (XRD)、差热分析 (DTA)、透射电子显微 (TEM )分析了SnO2 组元对RuO2 TiO2 SnO2 /Ti阳极涂层组织、晶粒尺寸和外观形貌的影响。结果表明 ,所获三元涂层颗粒尺寸细小 ,均为纳米结构 ,且添加SnO2 组元后有显著细化涂层晶粒的效果。在不同退火温度下 ,随SnO2 含量的增加 ,涂层晶粒均能发生一定程度的细化。所获三元阳极涂层主要组成物相为金红石 (Ru ,Sn ,Ti)O2 固溶体 ,SnO2 组元含量较高的涂层出现不同成分金红石相共存的现象 ;当涂层退火温度由 45 0℃升高至 6 0 0℃后 ,SnO2 组元不能阻止 (Ru ,Sn ,Ti)O2 固溶体脱溶分解 ,并析出六方晶系Ru单质 ;添加SnO2 组元的RuO2 SnO2 TiO2 涂层晶粒外观呈较理想等轴状特征