Novel UV absorbers prepared from 2,4-dihydroxybenzophenone and hexachlorocyclotriphosphazene

The UV-stabilizing ability and thermal loss from the polystyrene film of novel UV absorbers, 2-[(3-hydroxy-4-benzoyl) phenoxy] pentachlorocyclotriphosphazene (HBPC) and hexakis[ (2-hydroxy-4-benzoyl) phenoxy] cyclotriphosphazene (HBPP), were investigated. The UV-stabilizing ability of HBPC estimated by the formation of carbonyl groups in polystyrene was comparable to that of 2,4-dihydroxybenzophenone (DHB), suggesting that the phosphazene moiety does not affect the efficiency of the stabilizing ability of DHB units. No significant difference of efficiency per stabilizing units between HBPC and HBPP was observed. HBPC and HBPP are noteworthy for their low thermal losses from the polystyrene film, i.e., the thermal loss of HBPP was completely suppressed and the diffusion coefficient of HBPC at 160°C was two orders of magnitude smaller than that of DHB. The thermogravimetric analysis and differential scanning calorimetry measurement showed that HBPC and HBPP are nonvolatile and stable up to 230 and 300°C, respectively. © 1993 John Wiley & Sons, Inc.     

Cognitive model of team cooperation in en-route air traffic control

Since controller teams are in charge of en-route air traffic control, team cooperation is a key issue for good control performance. We conducted ethnographic field observation at the Tokyo Area Control Center and then analyzed the obtained data to develop a cognitive model of team cooperation in en-route air traffic control. We segmented conversational records, behavioral records, and so on by control unit, and then clarified relations between the segments and identified expert knowledge and judgment behind them. Cognitive processes of controller teams were reconstructed based on a concept of distributed cognition. The analysis revealed that the mutual belief model is applicable to team cooperation processes, the role assignment of tasks within a controller team is implicit and that control plans are implemented smoothly once team situation awareness has been established. A cognitive model of controllers?? team cooperation has been constructed based on these findings.     

Electric field-induced concentration and capture of DNA onto microtips

Simple, high-yield concentration of DNA is important for high-throughput genetic analysis and disease diagnosis. Glass-based microfilters are popular but the process requires centrifugation steps with cumbersome chemical processes. As an alternative, a concentration method using an electric field has been explored previously, but with limited efficiency. In this paper, electric field-induced concentration and capture of DNA are studied by using high-aspect-ratio microtips coated with a gold layer. The microtips are immersed longitudinally into a solution of 100???L containing ??-phage DNA. After DNA concentration using an electric field, the microtips are withdrawn from the solution. Under AC- and biased AC fields, DNA is concentrated by electrophoresis (EP), dielectrophoresis (DEP), and electroosmotic flow (EOF). To reduce capillary effects in the withdrawal process, the microtips are coated with positively charged poly-l-lysine (PLL). The pattern of captured DNA is analyzed by fluorescence microscopy. DEP attracts DNA molecules at the edges of microtips, where the highest gradient of electric field exists. EP attracts DNA onto the surface of microtips following the vectors of an electric field. EOF generates vortexes that deliver DNA onto microtips. Using this method, 85% of DNA is captured on the PLL-coated microtips after three sequential captures. The concentration mechanism can potentially facilitate rapid and simple preparation of DNA for downstream analysis.     

Large magnetoresistivity of sputtered Al-(O or N)-Bi alloys

Application of the sputtering technique to (Al₂O₃)_xBi_100–x and (AIN)_x Bi_100–x (x = 0 to 100%) has been found to result in the formation of a duplex material consisting of hexagonal bismuth particles dispersed finely and homogeneously in amorphous Al_xO_y and Al_xN_y matrices. The particle size and interparticle distance of the bismuth phase were about 5 to 140nm and 5 to 35 nm. The duplex alloys have high electrical resistivities ranging from 1.82 × 10³ to 3.16 × 10⁵ cm combined with a negative temperature-dependent resistivity of 148 to 342% of ₂₇₃. Furthermore, all the Al-O-Bi and Al-N-Bi alloys have been found to exhibit a positive magnetoresistive change and the maximum value, (H), at 4.2 K and 7.5T reaches 5.85 × 10⁴ cm for (Al-O)_65.7Bi_34.3 and 1.99 × 10⁵ cm for (Al-N)_69.7 Bi_30.3. The large magnetoresistivities are probably due to the unique sputtered structure consisting of metallic bismuth particles with a long mean free path of electrons embedded finely and homogeneously in amorphous Al_xO_y or Al_xN_y matrix, resulting in the large difference of the relaxation times (different mobilities) of electron carriers. It has thus been demonstrated that the oxide- or nitride-based composite materials exhibiting large magnetoresistivities, which cannot be achieved in metallic composite materials, are obtained by sputtering simultaneously Al₂O₃ or AIN and bismuth which is immiscible to aluminium.     

Microstructure and mechanical properties of metastable lath martensite wires in the Fe-Ni-Cr-Al-C system produced by melt spinning in rotating water

Metastable lath martensite ( _L ) phase wires with high strengths have been produced in the Fe-Ni-Cr-Al-C alloy system by melt spinning in rotating water. These wires have a circular cross section and a white lustre and the wire diameter is in the range of 100 to 140m. The width and length of each lath in the _L phase are as small as about 0.3 and 2m, respectively. The _y, _f and _p are about 900 and 1650 MPa and 2.0% for the _L wires. The subsequent annealing causes an increase in _p as well as _y and _f and the attained values are about 1000 and 1700 MPa and 3.0% for Fe-10Ni-10Cr-6.5 Al-1.0C wire annealed at 773 K for 1 h owing to the precipitation strengthening of a very fine unidentified carbide and to a high density of dislocations and lath boundaries in the _L phase. Further annealing causes a significant decrease in _p through decomposition of _L to+M₇C₃+M₂₃C₆. Therefore, the high strength combined with relatively good ductility for the _L wires is interpreted as due to the suppression of the phase transformation of _L to a mixed structure of+M₇C₃+M₂₃C₆ by melt quenching.     

Microstructure and superconducting properties of rapidly-quenched copper-based alloys containing immiscible lead and bismuth elements

Copper-based superconducting alloys including finely dispersed f c c lead or h c p (Pb- Bi) particles in f c c copper matrix have been obtained by rapid quenching (Cu-M)_100-x Pb_x and (Cu-M)_100-x (Pb_0.6Bi_{0.4 x} (M = aluminium, silicon or tin;x < 10 at%) alloys containing immiscible elements such as lead and bismuth. The particle size and interparticle distance were about 30 to 130 nm and 20 to 200 nm for had particles and about 30 to 60 nm and 30 to 150 nm for (Pb- Bi) particles. The transition temperature,T _c, was in the range of 3.2 to 5.5 K for the Cu-M-Pb alloys and 6.2 to 6.3 K for the Cu-M-Pb-Bi alloys. Critical magnetic field,H _c2, and critical current density,J _c, for the later alloys were 0.47 to 0.93T at 4.2 K and 1.1 × 10⁵ to 2.7 × 10⁵ Am^–2 at zero applied field and 4.21 K. The mechanism of the appearance of such a soft-type superconductivity for the rapidly quenched copper-based alloys was discussed, and inferred to be due to the formation of a percolation path of a superconducting lead or Pb-Bi phase along the grain boundaries, sub-boundaries and/or tangled dislocations where the lead or Pb-Bi phase precipitated preferentially, rather than the proximity effect based on lead or Pb-Bi particles.     

High-field superconductivity in Al-O-Pb and Al-O-Pb-Bi sputtered films

The sputter-quenched Al _x O _y alloys containing lead and bismuth elements, which are insoluble to aluminium; have been found to exhibit a remarkably enhanced upper critical field,H _c2, which is higher by about 6 to 66 times than those of pure lead metal and Pb₆₀Bi₄₀ alloy. The sputtered structure consists of amorphous Al _x O _y and f c c lead or h c p (lead-bismuth) phases. The lead and phases disperse homogeneously in the amorphous matrix and their particle sizes and interparticle distances are about 10 to 20 nm and 5 to 20 nm, respectively, for lead and particles. The superconducting transition temperature,T _c, upper critical magnetic field,H _c2, at 4.3 K, and residual resistivity at 10 K are 7.74 K, 3.3 T and 2.09 × 105cm, respectively, for (Al-O)_92.8 Pb_7.2 and 7.45 K, 8.2 T and 1.70 × 106 cm, respectively, for (Al-O)_86.2(Pb_0.6 Bi_0.4)_13.8. The remarkable enhancement ofH _c2 is interpreted as being mainly due to a remarkable decrease of the coherence length resulting from a large reduction of the effective mean free path of electrons. Additionally, the fluxoid pinning force under applied field has also been markedly enhanced for the duplex structure films than for sputtered lead film, probably because of the change of the dispersed lead phase into a type-II superconductor and an effective fluxoid pinning action at the interface between Al _x O _y and fine lead particles.     

MiR-10a in Pancreatic Juice as a Biomarker for Invasive Intraductal Papillary Mucinous Neoplasm by miRNA Sequencing

New biomarkers are needed to further stratify the risk of malignancy in intraductal papillary mucinous neoplasm (IPMN). Although microRNAs (miRNAs) are expected to be stable biomarkers, they can vary owing to a lack of definite internal controls. To identify universal biomarkers for invasive IPMN, we performed miRNA sequencing using tumor-normal paired samples. A total of 19 resected tissues and 13 pancreatic juice samples from 32 IPMN patients were analyzed for miRNA expression by next-generation sequencing with a two-step normalization of miRNA sequence data. The miRNAs involved in IPMN associated with invasive carcinoma were identified from this tissue analysis and further verified with the pancreatic juice samples. From the tumor-normal paired tissue analysis of the expression levels of 2792 miRNAs, 20 upregulated and 17 downregulated miRNAs were identified. In IPMN associated with invasive carcinoma (INV), miR-10a-5p and miR-221-3p were upregulated and miR-148a-3p was downregulated when compared with noninvasive IPMN. When these findings were further validated with pancreatic juice samples, miR-10a-5p was found to be elevated in INV (p = 0.002). Therefore, three differentially expressed miRNAs were identified in tissues with INV, and the expression of miR-10a-5p was also elevated in pancreatic juice samples with INV. MiR-10a-5p is a promising additional biomarker for invasive IPMN.