Magnetic properties and thermal stability of CoFeNi-based amorphous films

CoNiFe-based amorphous films were magnetron-sputtered to investigate their structural and magnetic properties, including annealing-induced effects and interfacial influence from additional layers of Ta and Cu. The amorphous structure was confirmed by diffraction experiments. The magnetic measurements showed a well-defined uniaxial anisotropy in plane, arising possibly from atom oblique incidence effects competing with the stray field of the magnetron. The anisotropy could be influenced by using a Ta buffer layer, though the interfacial reaction gives rise to a dead layer. A coercive force H _c of 1–2 Oe and a magnetization of 680 emu/cm³ were measured at room temperature; properties which show promise for application in magnetotunneling junction devices. Thermal analyses showed a two-stage crystallization behavior, which started at 400°C and ended at about 600°C. The Curie temperature of the amorphous phase was estimated to be about 440°C.     

Effects of Ca and Zr substitution upon structure and properties of Ba5LaTi3Ta7O30 low-loss dielectric ceramics

Effects of Ca and Zr substitution upon the dielectric properties of Ba₅LaTi₃Ta₇O₃₀ ceramics were investigated together with the structural characterization. All the samples of Ba₅La(Zr_xTi_1−x)₃Ta₇O₃₀ formed a filled tungsten-bronze structures, whereas the solid solution limit was determined as x=0.25 in (Ca_xBa_1−x)₅LaTi₃Ta₇O₃₀. Beyond this limit secondary phase of CaTa₂O₆ was detected and it would become the major phase for the Ca-rich compositions. The temperature coefficient of dielectric constant was improved with increasing Zr content while the dielectric constant decreased and the low dielectric loss varied little (in the order of 10⁻⁴). In the case of (Ca_xBa_1−x)₅LaTi₃Ta₇O₃₀, small temperature coefficient of dielectric constant could be obtained with increasing Ca content while the dielectric constant decreased significantly, and a small amount substitution of Ca for Ba induced decrease in dielectric loss.     

Synthesis of LiFePO4 with fine particle by co-precipitation method

LiFePO₄ is a potential candidate for the cathode material of the lithium secondary batteries. A co-precipitation method was adopted to prepare LiFePO₄ because it is simple and cheap. Nitrogen gas was needed to prevent oxidation of Fe²⁺ in the aqueous solution. The co-precipitated precursor shows the high reactivity with the reductive gas, and the single phase of LiFePO₄ is successfully synthesized with the aid of carbon under less reductive conditions. LiFePO₄ fine powder prepared by co-precipitation method shows high rate capability, impressive specific capacity and cycle property.     

Parallel path consistency

Filtering algorithms are well accepted as a means of speeding up the solution of the consistent labeling problem (CLP). Despite the fact that path consistency does a better job of filtering than arc consistency, AC is still the preferred technique because it has a much lower time complexity. We are implementing parallel path consistency algorithms on multiprocessors and comparing their performance to the best sequential and parallel arc consistency algorithms.^(1,2) (See also work by Kerethoet al. ⁽³⁾ and Kasif⁽⁴⁾) Preliminary work has shown linear performance increases for parallelized path consistency and also shown that in many cases performance is significantly better than the theoretical worst case. These two results lead us to believe that parallel path consistency may be a superior filtering technique. Finally, we have implemented path consistency as an outer product computation and have obtained good results (e.g., linear speedup on a 64K-node Connection Machine 2).     

High performance biofilm process for treating wastewater discharged from coal refining plants containing nitrogen, cyanide and thiocyanate.

Wastewater discharge from coal refining plants contains a number of biologically toxic compounds; 2000-2500 mg/l of COD of which 40% is composed of phenol, 100-400 mg/l of thiocyanate, 10-40 mg/l of cyanide, 100-250 mg/l of NH4+-N and 150-300 mg/l of total nitrogen. In order to treat this kind of high strength wastewater, we have developed a high performance biofilm process using fluidizing bio-carriers of the tube chip type. The fluidizing biofilm carriers are made of a composite of polyethylene and several inorganic materials, whose density is controlled at 0.97-0.98 g/ml. The fluidizing biofilm carriers show sound fluidization characteristics inside bioreactors. The wastewater is treated using three consecutive series reactors in oxic-anoxic-oxic arrangement. Each reactor is charged with the fluidizing biofilm carriers of 50 vol%. Furthermore, newly cultured active microorganisms for the thiocyanate biodegradation are added in the biofilm process. At total hydraulic retention time of 2.2 days, this process can achieve steady state removal efficiencies: COD, 99%; thiocyanate, 99%; NH4+-N, 99% and total nitrogen, 90%.