Phase Equilibrium Investigations on Na–K–(β+β")-Alumina

The activities of Na₂O and K₂O dissolved in mixed-alkali Na–K–(β+β")-Al₂O₃ (NKBA) have been determined by using yttria stabilized zirconia (YSZ) as a solid electrolyte in the following galvanic cells: The approach enables to verify in situ the establishment and maintenance of the β/β"-equilibrium, and to characterize it as a function of the phase composition of NKBA. The results can be expressed as follows:      

Preparation and characterization of a series of polyamides with long alkylene segments: Nylons 12 20, 10 20,s 20,6 20, 4 20 and 2 20

Summary A series of nylons with long alkylene segments between amide groups were newly prepared by step-heating melt-polycondensation of 1,lS-octadecanedicarboxylic acid with various diamines. The prepared polyamides were characterized carefully. The results show that many properties of the prepared nylons change regularly with the length of methylene segments in diamines. In addition, nylon 2 20 has a relatively low molecular weight and much different melting and thermal decomposition behaviors in comparison with other nylons. Received: 21 June 2OO2/Revised version: 18 September 2002/ Accepted: 18 September 2002 Correspondence to Deyue Yan E-mail: dyyan@mail.sjtu.edu.cn Tel: 0086-21-54742863 Fax: 0086-21-54741297     

视频服务器拥塞控制算法的研究与实现

分析现有网络拥塞控制算法的优缺点,在此基础上,根据多媒体数据和嵌入式设备的特点提出改进的基于视频服务器的拥塞控制算法。此算法以UDP协议为基础,通过控制传输速率来降低丢包率和网络时延,提高了嵌入式设备的多媒体数据传输质量。同时,将此算法应用于基于TMS320DM6467T硬件开发平台和Linux操作系统的视频服务器上,并通过实验验证了算法的可靠性与实用性。     

Interbay物料自动搬运系统性能分析

Interbay物料自动搬运系统的运行效率对于晶圆制造系统影响较大,研究Interbay物料自动搬运系统的绩效具有较大的意义[1]。该文以带有捷径的单闭环背脊式布局的物料自动搬运系统为研究对象,通过问题描述,简化、假设将实际问题抽象为导引运输模型。然后,建立数学模型,采用Dijkstra算法确定工件搬运的最短路径。最后,利用Arena仿真软件建立含有导引运输设备的模型,采用控制变量法探究小车数量小车占用轨道的方式、调度规则等因素对于产出的影响,发现对于本文中的模型,其它条件相同时,搬运系统采用Release-at-end的控制方式,系统最大搬运量越大。     

浅谈信息管理技术在建筑施工企业项目管理中的应用简

信息技术与先进的管理思想相结合,创造性地利用信息技术,可以高效提升企业管理创新能力。本文从施工管理的视角,阐述了在石油化工行业大型炼化工程项目管理中,如何利用信息管理技术,构架起综合项目管理平台,采用工程验收平台和POWER ON项目管理软件来进行二次开发,结合具体工程实践,实现网上机械车辆结算。     

特殊教育幼儿园中的导视系统设计分析简

随着我国越来越重视对特殊需要儿童的教育,特殊儿童幼儿园的人性化设计也成为了近几年热门的设计方向。导视系统的设计在特殊儿童幼儿园中起着非常重要的作用,完善的导视系统设计能够创造人性化的特殊教育幼儿园环境、儿童主体意识的确立和强化、对特殊儿童意愿需求的尊重和理解。同时,也能够让特殊教育儿童在使用中感到非常方便、自然。本文旨在构建功能合理的、具有人情味的、准确体现环境意象的导视系统设计,并且通过优秀的导视系统设计提高儿童在空间内行动的便捷性和安全性,提高空间环境使用的品质。     

IN SITU LEACHING OF URANIUM USING DILUTE SULFURIC ACID AND MOLECULAR OXYGEN

The technical feasibility of in situ uranium leaching using dilute sulfuric acid and molecular oxygen has been assessed and the important process parameters examined by use of laboratory high pressure leaching columns.

The dilute H₂SO₄/O₂ lixiviant was effective in leaching uranium from the ore samples tested. The leaching process was chemical reaction rate limited and can be represented using pseudo first-order kinetics. The leaching rate constant is proportional to the proton concentration of the lixiviant.

Much of the uranium was leached from the ore before decomposition of carbonate minerals by the acid was complete. Acid consumption per pound of U₃O₈ increased sharply as the uranium recovery level exceeded 70%. There appears to be a minimum oxygen pressure for effective uranium leaching. A pressure of 2758 KPa was adequate for the ore samples tested     

PA66/UHMWPE合金的力学性能和微观结构研究

制备了PA66／uHMwPE／HDPE-g-MAH共混合金，并对其力学性能和微观结构进行了研究。结果表明，随着UHMWPE质量分数的增加，共混合金常温和低温下的缺口冲击强度都显著提高，拉伸强度和拉伸模量下降，但仍能保持较高的力学性能；添加了UHMWPE的PA66合金的断裂面有大量的空穴产生和应力发白现象。     

陶瓷注射成形技术进展

陶瓷粉末注射成形是从现代粉末注射成形技术中发展起来的一项新型成形技术。本文着重论述了陶瓷注射成形发展的历史、技术特点、工艺及进展情况，并介绍了CIM的典型产品和应用领域。     

Preparation of ordered mesoporous SiCN ceramics with large surface area and high thermal stability

For the first time, highly ordered two-dimensional (2-D) and three-dimensional (3-D) mesoporous SiCN ceramics with high surface area and high thermal stability were prepared by nanocasting a preceramic polymer solution into mesoporous carbon templates, CMK-3 and CMK-8, respectively. As a negative replica of CMK-3 carbon, the obtained mesoporous SiCN ceramic possessed an ordered 2-D hexagonal mesostructure, which is similar to the structure of SBA-15 silica except for the reduced dimensions. An ordered 3-D cubic mesoporous SiCN ceramic was also fabricated using CMK-8 as a template. The wall of the mesoporous SiCN replicas consisted of an amorphous SiCN ceramic phase, which possessed high thermal stability at high temperature up to 1000 °C. N₂-sorption isotherms revealed that these ordered mesoporous SiCN ceramics have high BET surface areas (up to 472 m² g⁻¹) and narrow pore-size distributions, which was preserved even after a re-treatment at 1000 °C in air. The use of carbon template played an important role in the preparation of mesoporous SiCN replicas and enhanced the thermal stability of the SiCN products. It is expected that many other types of ordered mesoporous ceramics can be prepared from nanoporous carbon by nanocasting method.