A practical reliability assessment approach and its application for pile-stabilized slopes using FORM and support vector machine

Bulletin of Engineering Geology and the Environment - Many uncertainties exist in pile-stabilized slopes which make their design substantially complicated. In this paper, a first-order reliability...     

500 kV 开关弹簧机构支架螺栓断裂的原因分析及处理

HPL500B2型弹簧机构支架(BA)螺栓断裂可能导致开关分合闸失败,对其原因进行分析,发现BA螺栓由于预紧固力矩过大,接近其扭断力矩,使得作用在BA螺栓上的力偏高,BA螺栓安全系数仅为12%,安全系数较低。列出BA螺栓更换步骤及注意事项,并详细介绍分闸、合闸弹簧调整步骤,为类似事件的处理提供参考。     

Tensile testing and fracture mechanism analysis of polyvinyl alcohol nanofibrous webs

A tensile properties testing study was conducted to understand the influence of thickness, cross-head speed (speed of testing), gauge length (GL; specimen test length), and sample shape on important tensile properties of polyvinyl alcohol (PVA) nanofiber webs. The effects of each testing parameter on load at break, extension at break, Young's modulus, and tensile stress–strain curve of PVA nanofiber webs are analyzed. The Welch two sample t-tests show the significant difference among tested data. Using interaction plots, two-way analysis of variance, and margin mean plots, the interaction effects among testing parameters have been analyzed. Of all the factors, cross-head speed, the interaction among GL, and sample thickness (GL: Thickness) and the interaction among GL, testing speed and sample thickness (GL: Speed: Thickness) have significant influence on the tensile properties of PVA nanofiber webs. Moreover, the hypothesized model of mechanism of tensile strain–stress curve of PVA nanofiber webs has been proposed. Based on the model, the tensile strain–stress curve can be split into three stages: linear elastic, partial break up, and complete breakage. This study will provide a better understanding of tensile testing parameters' effects and their interaction effects on the tensile properties of nanowebs.     

Room Temperature Ferromagnetism in Co-doped CuAlO2 Nanofibers Fabricated by Electrospinning

One-dimensional, diluted magnetic semiconductor nanofibers have attracted increasing attention for their unique magnetic properties, large specific surface area, and high porosity. These qualities lead to excellent performance in magneto-optical devices, magnetic resonance imaging, ferrofluids and magnetic separation. The purpose of this study is to fabricate P-type one dimensional CuAlO2-based diluted magnetic semiconductor nanofibers. First, we fabricated Cu Al0.95Co0.05O2 nanofibers with an average diameter of 1 μm with the electrospinning method. The annealed nanofibers were thermally treated at a temperature of 1 100 ℃ and then shrunk to a diameter of about 650 nm. We used X-ray diffraction measurements and Raman spectra to confirm that the Cu Al0.95Co0.05O2 nanofibers had a single impurity free delafossite phase. The X-ray photoelectron spectroscopy analysis indicates that Co was present in the +2 oxidation state, resulting in an room temperature ferromagnetism in the Cu Al0.95Co0.05O2 fiber. This contrasts with nonmagnetism in pristine CuAlO2 fiber. The coercivity(Hc) value of 65.26 Oe and approximate saturation magnetization(Ms) of 0.012 emu/g demonstrate good evidence of ferromagnetism at room temperature for Cu Al0.95Co0.05O2 nanofibers.     

Hopping transport in the space-charge region of p-n structures with InGaN/GaN QWs as a source of excess 1/f noise and efficiency droop in LEDs

Semiconductors - It is shown that the emission efficiency and the 1/f noise level in light-emitting diodes with InGaN/GaN quantum wells correlate with how the differential resistance of a diode...     

In situ characterization of LiY(WO4)2 nanotubes for electrochemical energy storage

Here, LiY(WO₄)₂ nanotubes are prepared via a feasible electrospinning technique. This new anode material shows excellent electrochemical properties. The capacity loss of LiY(WO₄)₂ nanotubes is as low as 6.9% after 156 cycles, while bulk LiY(WO₄)₂ presents the capacity loss higher than 55.0%. Even after 600 long-life cycles, the capacity loss of the nanotubes is only 9%. It can be seen that the hollow structure with a rough surface and a porous morphology contributes to the improvement of electrochemical performance. Furthermore, online X-ray diffraction (XRD) method is firstly applied to understand the lithium ions insertion/extraction mechanism of LiY(WO₄)₂ nanotubes. It can be concluded that it is an asymmetrical two-phase reaction. A phase transformation from LiY(WO₄)₂ to Li₃Y(WO₄)₂ can be obviously seen from the in situ XRD during discharge process. While Li₂Y(WO₄)₂ appears as an intermediate phase with a reverse charge reaction. In addition, in situ XRD also demonstrates that LiY(WO₄)₂ nanotubes have surprised electrochemical reversibility. All the above results indicate that LiY(WO₄)₂ nanotubes can be expected to be anode candidate for rechargeable lithium ion batteries (LIBs).