Aging response of the young’s modulus and mechanical properties of Ti-29Nb-13Ta-4.6Zr for biomedical applications

Alloys for implant devices require improved strength but a reduced Young’s modulus, in order to become mechanically more compatible with adjacent bone tissues. In this study, a new metastable β-type titanium alloy, Ti-29Nb-13Ta-4.6Zr (wt pct), was subjected to aging treatment to produce different microstructures, and the resulting mechanical properties, including the Young’s modulus, were measured. The Young’s modulus of this alloy is found to be sensitive to microstructures generated by various heat treatments. For microstructures varying from (α + β) to (α + β + ω) and (β + ω), the Young’s modulus increases with an accompanying increase in tensile strength and hardness, but decreases in ductility. The (β + ω) microstructure has a low strength, high modulus, and poor ductility and cannot be used for biomedical applications. For an (α + β) microstructure, the volume fraction of the phases is shown to be the main factor that determines the mechanical properties.     

公司大门工程建设施工

大门小品建筑属多项目综合性工程。本文作者从管理者的角度 ,通过对公司大门及附属工程施工质量控制的总结 ,说明了质量控制应贯穿于工程施工的全过程     

On the binomial confidence interval and probabilistic robust control

The Clopper-Pearson confidence interval has ever been documented as an exact approach in some statistics literature. More recently, such approach of interval estimation has been introduced to probabilistic control theory and has been referred as non-conservative in control community. In this note, we clarify the fact that the so-called exact approach is actually conservative. In particular, we derive analytic results demonstrating the extent of conservatism in the context of probabilistic robustness analysis. This investigation encourages seeking better methods of confidence interval construction for robust control purpose.     

Sol-Gel Preparation of LaNiO3 and Its Physical and Chemical Properties

LaNiO3 was synthesized by sol-gel method in which lanthanum nitrate and nickel nitrate were used as start materials and citric acid was used as complex for gel formation.The precursor was dried and subsequently heated at elevated temperature to form the desired product.XRD analysis shows that pure LaNiO3 was synthesized.Electrical conductivity and electrochemical performance of the material were tested.The electrical conductivity decreases from 34.5that there are current peaks in the curve, which is the evidence of the electrochemical activity of LaNiO3.     

技术攻关提高成材率

介绍了广钢集团高速线材生产线的生产和工艺概况，分析了成材率的影响因素，阐述了技术攻关提高成材率所采取的措施和取得的良好效果及经济效益。     

赴日无线电监测技术考察报告

首先介绍了日本总务省关东综合通信局电波监理部的情况，然后对日本安立公司生产的RR510A型无线电监测接收机和技术参数以及MS8609A型数字移动无线发射机测试仪的功能进行了分析和介绍。     

Bipolar electric fatigue behaviour as a function of field strength in antiferroelectric (Pb,Ba,La)(Zr,Sn,Ti)O3 ceramics

The bipolar electric fatigue behaviour of antiferroelectric ceramics with the composition of Pb_0.88Ba_0.10La_0.02(Zr_0.55Sn_0.35Ti_0.10)O₃ was investigated under various cycling fields. The material exhibits a degradation in the maximum field induced strain, a diffuse AFE-FE phase transition and an enhancement in the diffusion character of the FE-AFE phase transition due to electric cycling. Those variations increase with cycle number, indicating a logarithmic fatigue up to 10⁸ cycles. There is no indication for the variations to be recovered, and the symmetry of the negative and positive parts of the strain hysteresis loops still remains. Higher cycling field results in a stronger deterioration of the maximum field induced strain and a larger extent of diffusion in AFE-FE and FE-AFE phase transitions. The normalized maximum strain shows nearly the same scale of degradation when the materials are cycled at various electric fields. After a heat treatment at 500°C for 1 h, the variations in the AFE-FE and FE-AFE phase transition due to cycling disappear, whereas the maximum strain resumes almost to its original value. Electrochemical variations are considered to contribute to the main fatigue mechanism for the material under investigation.