Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Fabrication of core–shell nanocomposites with enhanced photocatalytic efficacy

The current study establishes the unprecedented involvement in the evolution and production of novel core–shell nanocomposites composed of nanosized titanium dioxide and aniline‐o‐phenylenediamine copolymer. TiO₂@copoly(aniline and o‐phenylenediamine) (TiO₂@PANI‐o‐PDA) core–shell nanocomposites were chemically synthesized in a molar ratio of 5:1 of the particular monomers and several weights of nano‐TiO₂ via oxidative copolymerization. The construction of the TiO₂@PANI‐o‐PDA core–shell nanocomposites was ascertained from Fourier transform IR spectroscopy, UV–visible spectroscopy and XRD. A reasonable thermal behavior for the original copolymer and the TiO₂@PANI‐o‐PDA core–shell nanocomposites was investigated. The bare PANI‐o‐PDA copolymer was thermally less stable than the TiO₂@PANI‐o‐PDA nanocomposites. The core–shell feature of the nanocomposites was found to have core and shell sizes of 17 nm and 19–26 nm, respectively. In addition, it was found that the addition of a high ratio of TiO₂ nanoparticles increases the electrical conductivity and consequently lowers the electrical resistivity of the TiO₂@PANI‐o‐PDA core–shell nanocomposites. The hybrid photocatalysts exhibit a dramatic photocatalytic efficacy of methylene blue degradation under solar light irradiation. A plausible interpretation of the photocatalytic degradation results of methylene blue is also demonstrated. Our setup introduces a facile, inexpensive, unique and efficient technique for developing new core–shell nanomaterials with various required functionalities and colloidal stabilities. © 2018 Society of Chemical Industry     

Matrilin-3-Primed Adipose-Derived Mesenchymal Stromal Cell Spheroids Prevent Mesenchymal Stromal-Cell-Derived Chondrocyte Hypertrophy

Adipose-derived mesenchymal stromal cells (Ad-MSCs) are a promising tool for articular cartilage repair and regeneration. However, the terminal hypertrophic differentiation of Ad-MSC-derived cartilage is a critical barrier during hyaline cartilage regeneration. In this study, we investigated the role of matrilin-3 in preventing Ad-MSC-derived chondrocyte hypertrophy in vitro and in an osteoarthritis (OA) destabilization of the medial meniscus (DMM) model. Methacrylated hyaluron (MAHA) (1%) was used to encapsulate and make scaffolds containing Ad-MSCs and matrilin-3. Subsequently, the encapsulated cells in the scaffolds were differentiated in chondrogenic medium (TGF-β, 1–14 days) and thyroid hormone hypertrophic medium (T3, 15–28 days). The presence of matrilin-3 with Ad-MSCs in the MAHA scaffold significantly increased the chondrogenic marker and decreased the hypertrophy marker mRNA and protein expression. Furthermore, matrilin-3 significantly modified the expression of TGF-β2, BMP-2, and BMP-4. Next, we prepared the OA model and transplanted Ad-MSCs primed with matrilin-3, either as a single-cell suspension or in spheroid form. Safranin-O staining and the OA score suggested that the regenerated cartilage morphology in the matrilin-3-primed Ad-MSC spheroids was similar to the positive control. Furthermore, matrilin-3-primed Ad-MSC spheroids prevented subchondral bone sclerosis in the mouse model. Here, we show that matrilin-3 plays a major role in modulating Ad-MSCs’ therapeutic effect on cartilage regeneration and hypertrophy suppression.     

Method for Predicting the Strength of Pellets Produced from Dry Fine-Grained Materials

Powder Metallurgy and Metal Ceramics - The mechanisms of phase interactions in granular media were studied to elaborate the results obtained previously at the Nekrasov Iron and Steel Institute of...     

Chitosan Microspheres as Carriers for pH‐Indicating Species in Corrosion Sensing

Chitosan microspheres containing bromocresol green, cresol red, and phenolphthalein for corrosion detection, through pH change, are synthesized in order to be used in protective coatings for aluminium alloys. Microspheres containing corrosion detection species are characterized morphologically (SEM) and physico‐chemically (FTIR, TGA). Release studies (UV–vis) are performed in corrosion‐promoting conditions (pH, NaCl), and detection studies by immersion in media associated with corrosion activity while microspheres' sensing activity is evaluated visually. Electrochemical characterization of AA2024 substrates in the presence of chitosan spheres is performed to understand material performance, and a color change is observed as a result of local pH increase in cathodic areas when corrosion takes place. These findings can be correlated with the results from release studies and seem a promising approach for corrosion sensing purposes, not only because pH increase is possible to detect due to corrosion, but also because chitosan is considered an environmentally friendly material.     

Extended preservation of raw beef and pork meat by hyperbaric storage at room temperature

Hyperbaric storage (HS) was evaluated as a new food preservation methodology at room temperature (RT) for beef and pork meat, both minced and in pieces, and compared to refrigeration (RF) storage. The meat samples were stored at 50, 75 and 100 MPa and variable RT up to 60 days. HS at 75 and 100 MPa could not only inhibit microbial growth but also inactivate microorganisms. Regarding physicochemical analyses, an overall equal to better pH maintenance in HS samples was achieved, and similar colour differences between HS and RF were observed. Generally, similarities in moisture content and drip loss between HS (mostly 75 and 100 MPa) and RF were detected (tendency for lower values in the former and higher values in the latter for the higher pressure level). Protein solubility revealed a decrease of sarcoplasmic protein values during storage with a pressure level dependency in some samples.     

Phase-Field Modeling of Nugget Zone for a AZ31-Mg-Alloy Friction Stir Weld

This work presents simulation of microstructure evolution in the nugget zone (NZ) of a AZ31-Mg-alloy friction stir weld. The process parameters (tool geometrical characteristics, rotational speed, travel speed, applied load) have been correlated with the resulting microstructural features in the NZ of the weld (grain size and population) with the aid of the MICRESS software, which provides the ability to simulate both nucleation and grain growth during dynamic recrystallization phenomena evolving in the NZ during the weld thermal cycle. The input parameters of the developed model include the tool geometry, the welding conditions as well as the recrystallization energy, the grain boundary mobility and specific material properties. NZ microstructure obtained by simulation shows good agreement with experimental measurements for both grain population and size.     

Towards Diastereomeric Pure Salts with Antisolvent Methods

Chiral molecules, especially enantiomers and diastereomers of purity > 99 %, present a significant market share within the chemical, pharmaceutical, and flavor industries. Antisolvent precipitations, both batch and semicontinuous operations to serve the current trends in flow chemistry were demonstrated to be environmentally benign and efficient tools in achieving high optical purities. Although salts are known to be insoluble in supercritical CO₂, instabilities of the nascent salts were detected and applied for increasing efficiency. Diastereomeric excess values of the crystalline products exceeded 99 % in maximum of three consecutive steps both by repeated resolution with half molar equivalent of the amine to the acid and by direct recrystallization of the salts.