10％毒死蜱颗粒剂的配方及加工工艺

[目的]通过试验筛选出10％毒死蜱颗粒剂的优惠配方和连续化加工工艺.[方法]以天然颗粒为载体,采用吸附法工艺,研究该制剂的配方组成、加工工艺和设备选型.[结果]试验产品质量稳定合格,流动性好,(54±2)℃、14d毒死蜱分解率≤5％,破碎率≤10％.[结论]在试验选定的配方条件下,所选的加工设备可以实现加工工艺连续化,各项技术指标符合颗粒剂的要求.     

无规共聚聚丙烯的结构与性能研究

通过核磁共振(13CNMR),红外光谱(IR)和差示扫描量热法(DSC)等表征分析手段对无规共聚聚丙烯(PPR)的物理结构与机械性能进行研究。结果表明:PPR具有典型的无规共聚物的结构,乙烯基团较均匀的无规分散于丙烯分子长链中;在分子序列结构中,EE和EEE联排的结构并不多;乙烯含量低的EP接点的含量偏低,相应的抗冲击强度偏低,乙烯含量高的EP接点的含量偏高,相应的抗冲击强度较高。乙烯在丙烯分子长链中的无规插入也适当的降低了共聚物的熔点。     

苯乙烯-丁二烯橡胶门尼黏度标准物质定值不确定度的评定

依照GB/T 1231.1-2000进行实验,利用JJF 1059-1999]对苯乙烯-丁二烯橡胶门尼黏度标准物质定值过程中的不确定度分量进行了分析和评定。该测定过程中所产生的不确定度主要由多家实验室测量重复性和定值样品均匀性、稳定性引入。定值样品苯乙烯-丁二烯橡胶SBR 1502的门尼黏度ML(1+4)100℃测量值49.1的不确定度为±0.8。     

硅橡胶喷霜物鉴定及喷霜原因分析

采用红外光谱、高效液相色谱、飞行时间质谱对硅橡胶表面喷霜物进行了鉴定,结果表明：喷霜物为硅橡胶原材料二苯基硅二醇（GRC）脱水生成的三聚体和四聚体,且三聚体含量大于四聚体。喷霜物化学成分与GRC杂质相同,但GRC杂质不是导致喷霜的原因。通过扫描电镜和粒度分析表明,不同批次GRC结晶物颗粒粒径存在较大差异,而大粒径GRC容易发生喷霜。     

氟碳型聚氨酯材料的结构与老化性能研究

采用4'-二环己基甲烷二异氰酸酯(HMDI)、自制含氟聚酯多元醇、乙二醇(EG)等为主要原料合成了含氟脂肪族聚氨酯树脂。通过对合成聚氨酯树脂制备皮膜的物性检测和以含氟聚氨酯为表层制备合成革的耐黄变性能测试,考查氟含量对聚氨酯力学性能、耐水解和耐黄变性能的影响。结果表明:当氟含量达6%时,通过适度交联方式可以弥补模量下降,拉伸强度保持在47MPa,吸水率由2.13%降至1.04%,QUV测试4级耐黄变时间由200h提高到300h。     

藻类-升流式外回流微氧污泥床处理生活污水研究

选取某高校生活污水为研究对象,采用绿藻复氧-升流式外回流微氧污泥床反应器,对经过厌氧预处理后的低碳氮比生活污水进行处理。结果显示,反应器处理效果良好,对COD、NH4+-N、TN和SS的去除率分别为69.23%、90%、82%和91.06%,出水水质达到GB 18918-2002的一级A标准。由于利用绿藻光合作用产氧,故节省了100%曝气能耗;且该系统采用菌藻分离的方式,对反应器内溶解氧含量控制更精确。     

Mechanical properties, corrosion behaviors and microstructures of 7075 aluminium alloy with various aging treatments

The influence of two novel aging treatments, T616 （130 ℃, 80 min ＋ 65℃, 240 h＋130℃, 18 h） and high-temperature pre-precipitation（HTPP） aging （445℃, 30 min＋120℃, 24 h） on the tensile properties, intergranular corrosion, exfoliation corrosion behaviors and microstructures of 7075 AI alloy was studied, which were compared with the T6, T73 and RRA treatments. Fine η＇ precipitate with high density was obtained in the alloy with the T6 and RRA treatments. The η＇ precipitate density in the HTPP aged alloy is decreased due to the formation of coarse particles during the pre-precipitation process at high temperature of 445℃. The 7075-T616 alloy possesses higher precipitate density and whole precipitate volume fraction within the grain than the 7075-T73 alloy, and its whole precipitate volume fraction is even greater than that of the 7075-T6 alloy. Compared with T6 treatment, the RRA, T73, T616 and HTPP aging treatments cause the discontinuous distribution of the η precipitates at the grain boundary, which decreases the intergranular corrosion and exfoliation corrosion susceptibility of the alloy. Meanwhile, the T616 and RRA treatments can keep the high strength of the 7075 AI alloy, but the studied HTPP aging and T73 treatments lower its strength.     

SPV50Q钢的应力腐蚀开裂实验研究

基于线弹性断裂力学的方法,以SPV50Q钢材为研究对象,选用不同部位的M-WOL楔形张开加载预裂纹试样,对其在不同硫化氢体积分数及不同状态条件下的应力腐蚀开裂性能进行研究。测定出应力腐蚀裂纹扩展速率da/dt和应力腐蚀开裂临界强度因子K_(ISCC)。结果表明:随着硫化氢体积分数的减小,SPV50Q钢的应力腐蚀裂纹扩展速率da/dt降低,应力腐蚀临界应力强度因子K_(ISCC)增大。对SPV50Q钢进行热处理后在一定程度上能降低裂纹扩展速率da/dt,同时可提高硫化氢环境下的抗应力腐蚀开裂能力。     

基于多边形重叠检测的冲裁件优化排样

由于制造业中部分零件的大批量生产,条料上采用冲裁件优化排样可以节省大量的原材料。提出了一种基于多边形重叠检测的冲裁件优化排样新算法。该算法包含重叠检测和零件进退两个部分,避免了复杂的数学运算和耗时的人工操作。通过算例结果可知,运用该算法可以显著节省原材料,并且两个相同冲裁件可以很快地进行靠接。     

手性Schiff碱——铜配合物的合成研究

利用合成的脱氢松香酸降解胺和工业生产的松香胺和水杨醛反应,制得手性Ｓｃｈｉｆｆ碱,再与醋酸铜反应,合成得两种新型的手性Ｓｃｈｉｆｆ碱－铜配合物,并对其进行了元素分析,红外光谱、紫外光谱表征。