Structures and electrochemical performances of La_(0.75-x)Zr_xMg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1) (x=0-0.2) electrode alloys prepared by melt spinning

The La-Mg-Ni system A2B7-type electrode alloys with nominal composition La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1(x=0,0.05, 0.1,0.15,0.2)were prepared by casting and melt-spinning.The influences of melt spinning on the electrochemical performances as well as the structures of the alloys were investigated.The results obtained by XRD,SEM and TEM show that the as-cast and spun alloys have a multiphase structure,consisting of two main phases(La,Mg)Ni3 and LaNi5 as well as a residual phase LaNi2.The melt spinning leads to an obvious increase of the LaNi5 phase and a decrease of the(La,Mg)Ni3 phase in the alloys.The results of the electrochemical measurement indicate that the discharge capacity of the alloys(x≤0.1)first increases and then decreases with the increase of spinning rate,whereas for x0.1,the discharge capacity of the alloys monotonously falls.The melt spinning slightly impairs the activation capability of the alloys,but it significantly enhances the cycle stability of the alloys.     

Fe72.5Ga27.5合金的定向凝固工艺与磁致伸缩性能研究

研究了晶体生长过程中的不同参数(温度梯度GL,晶体生长速度V)对Fe72.5Ga27.5合金晶体取向规律的影响。Fe72.5Ga27.5合金经过炉冷、空冷及淬火等热处理后,研究了热处理对<110>取向多晶合金磁致伸缩性能的影响,并通过微观组织分析进行必要的解释。结果表明:样品的性能与温度梯度和生长速度有着密切的关系。取向多晶样品热处理前后组织形貌没有明显变化,淬火后<110>轴向取向多晶FeGa样品的性能明显提高。     

快淬纳米晶/非晶Mg2-xLaxNi（x=0～0.6）电极合金的电化学贮氢性能

为了改善Mg2Ni型合金的电化学贮氢性能,用La部分替代Mg,并用铸造及快淬工艺制备了Mg2-xLaxNi（x=0、0.2、0.4、0.6）电极合金,获得长度连续,厚度约为30μm,宽度约为25mm的薄带。用XRD、SEM和HRTEM分析了快淬合金薄带的微观结构,测试了合金薄带的电化学性能、电化学交流阻抗谱（EIS）及氢在合金中的扩散系数（D）。结果发现,在快淬无La合金中没有出现非晶相,但快淬La替代合金显示了以非晶相为主的结构,表明La替代Mg提高了合金的非晶形成能力。当x≤0.2时,La替代Mg不改变合金的Mg2Ni型主相,但出现少量的LaMg3及La2Mg17相。La替代及快淬明显改善合金的电化学贮氢性能。其中,Mg2La0.2Ni合金具有最佳的综合电化学性能。当淬速从0m/s（铸态被定义为淬速0m/s）增加到30m/s时,Mg2La0.2Ni合金的放电容量从197.2mAh/g增加到406.5mAh/g,20次充放循环后的容量保持率从52.7%增加到81.4%,高倍率放电能力从48.3%增加到56.8%,氢扩散系数（D）从8.12×10-12cm2/s增加到1.80×10-11cm2/s。     

萨中油田节能技术综合评价（第二部分）

大庆萨中油田在依靠节能技术降低能耗工作中,注重生产工艺中的节能技术改造,努力提高五大系统效率,不断提高供配电质量、降低电力网损率,引进和推广节能“四新”技术。本文就各项节能技术措施的应用情况分别进行阐述,对实际应用过程中的节能效果作了分析和评价,可为油田成选节能技术措施取向提供参考。     

CoFe_2O_4@FeCo纳米核壳颗粒的制备与磁性研究

利用化学共沉淀法合成Co Fe2O4纳米颗粒,并在氢气气氛下还原获得Co Fe2O4@Fe Co核壳结构磁性纳米颗粒。用XRD和TEM对所得样品进行结构分析,用SQUID测量样品在300 K时的磁滞回线,发现随着壳厚度的增加,核壳结构样品的矫顽力呈现先增加后减小的趋势,而其饱和磁化强度表现出逐渐增加的趋势。为了探究所制备样品的核壳磁性层之间的交换相互作用,还测量了M-T曲线以及T=5 K时的零磁场冷却(ZFC)和带磁场冷却(FC)磁滞回线。     

An investigation on electrochemical hydrogen storage performances of Mg-Y-Ni alloys prepared by mechanical milling

The nanocrystalline and amorphous Mg2Ni-type electrode alloys with a composition of Mg20?xYxNi10 (x=0, 1, 2, 3 and 4) were fabricated by mechanical milling. Effects of Y content on the structures and e...     

FeGa/BTO/FeGa层状复合结构中的磁电效应

采用区域熔炼法制备了FeGa磁致伸缩材料并测量了其磁致伸缩性能.利用该材料制备了FeGa/BTO/FeGa层状复合结构,并对该样品的磁电性能进行了系统研究.结果表明,该材料在共振频率95kHz下,磁电性能高于低频下性能7～10倍.磁电电压随直流偏磁场的变化发生明显变化,出现5.97×104A/m的优化偏置场,这主要是由FeGa层的压磁系数q随偏磁场的变化所致.3层复合材料的磁电系数与交流驱动场变化呈线性关系.另外,较薄的BTO压电层可以提高压应力,从而获得较高的磁电性能.     

La0.75Mg0.25Ni3.5Si0.10贮氢合金高温动力学性能的研究

贮氢合金在高温下会表现出与常温不同的电化学特性,以La0.75Mg0.25Ni3.5Si0.10合金为研究对象,采用交流阻抗谱和电位阶跃方法,对其高温使用环境下（30～70℃）的高倍率放电特性和动力学性能进行了深入的研究。研究结果表明合金的动力学性能是由电化学反应与氢的扩散共同控制的,合金的电荷传递电阻随温度升高而减小,高温有助于电极表面电化学反应速度的提高;但对于La0.75Mg0.25Ni3.5Si0.10合金存在最佳氢扩散温度,当温度高于其最佳温度时,由于释氢等副反应的进行,以及氧化腐蚀反应的加剧等,使合金的扩散系数反而减小;在合金表面电化学反应速度与氢扩散系数共同作用下,La0.75Mg0.25Ni3.5Si0.10合金高倍率放电性能在45℃时最优异,当温度高于45℃时反而降低。     

La2Ni7和LaMgNi7储氢合金电子结构的研究

采用密度泛函理论研究了La2Ni7和LaMg-Ni7储氢合金的电子结构,探讨了微观结构和合金宏观性能之间的关联性.结果表明,含Mg元素的LaMgNi7体系形成成键作用的Ni-Mg键,体系稳定性高于纯La2Ni7体系.同时LaMgNi7体系中的Ni-Ni键强度弱于La2Ni7体系中的相应键,降低了H进入体系的能量壁垒,改...     

Mg-Ni基储氢合金的研究进展与发展趋势

系统阐述了近年来Mg-Ni基储氢合金的研究开发概况,指出Mg-Ni基储氢合金具有放电容量高、资源丰富、价格低廉等突出优点,分析了影响Mg-Ni基储氢合金储氢性能的主要因素,总结了近年来采用的行之有效的改进方法,主要有制备非晶/纳米晶、元素替代、添加催化剂等,并对Mg-Ni基储氢合金今后的发展方向进行了探讨与展望,指出Mg-Ni基储氢合金虽然前景可观,但是要实现实际应用仍然存在一些问题需要解决。