Preparation of oriented linear copper fiber sintered felt and its performance

Long metal fibers were manufactured in horizontal lathe with a multi-tooth tool. Based on the coarse antler surface structure of copper fibers, a new sintering technology was put forward to manufacture a kind of oriented linear copper fiber sintered felt. The sintering mechanism of oriented linear copper fiber sintered felt was studied. Compared with sintered copper-wire felt, the characteristics of sintered copper-fiber felts were analyzed in details. Owing to the coarse antler surface structure of copper fibers, oriented linear copper-fiber felt was sintered under the condition ofmicro/nano scale range, and copper fibers easily bonded together in the sintering process. Microchannels with micro-scale coarse antler surface structure were constructed. These characters give oriented linear copper fiber felt some new merits： high filtration accuracy, high flow capability, low resistance loss, good capability to resistance pressure, stable and uniform pore, high specific surface area. The properties of oriented linear copper fiber sintered felt were analyzed.     

基于焊接机器人的三维快速成形的方法研究

将RP技术与熔焊技术结合．依据焊接工艺的特点对切片和多径规划算法进行了研究，得出了根据不同类型零件使用不同路径规划算法的结论。据此。使用Visual C^ 基于UniGraphics二次开发的方式实现了切片、路径规划算法，完成了面向焊接机器人性速成形软件的编写，实现UG实体模型的切片、路径规划以及机器人数控代码的生成。利用MotoMan机器人远程控制接口软件包MotoCom32编写了用于机器人快速成形的远程成形控制软件。采用CO2气体保护焊成功实现了基于焊接机器人的典型零件的快速成形。     

Effect of surface free energy of ceramic glaze on oil droplet shape and its behavior in water

A super-hydrophilic functional ceramic was prepared by adjusting the chemical components of ceramic glaze. Effect of surface flee energy of ceramic glaze on oil droplet shape and its behavior in water were studied. The results show that water can spread on ceramic surface with high surface free energy, and oil droplet can aggregate rapidly and separate from the ceramic surface in water. For the ceramic with lower surface free energy, the polar shares are dependant on its easy-cleaning property. The higher the polar shares, the better the easy-cleaning property, and the easier the droplet separates from the ceramic surface in water.     

两面顶金刚石单晶耐热性分析

本文通过热失重（TGA），示差扫描量热（DSC）法，扫描电镜（SEM），热侵蚀等方法分析了国产两面顶压机合成的金刚石单晶在空气中的耐热性。还分析了热侵蚀后金刚石的形貌变化并进行了抗压强度，T1、TT1的测量，将国产金刚石与进口金刚石作了大量的对比试验，发现两者的耐热性非常接近。发现金刚石的起始氧化温度在700℃左右，此时开始失重；剧烈氧化温度在850％左右，此时失重最为严重。在加热温度超过1200℃时在DSC图中出现了第二个放热峰，表明金刚石在受热温度超过1200℃时经历了第二次剧烈氧化阶段。这可能是由于在高温下触媒的反催化作用引起的。这为金刚石工具制造者及使用者提供了参考价值。     

小功率整体式电液伺服传动装置的动态性能分析

本文运用古典控制理论，对C335小功率整体式电液伺服传动装置进行了动态性能理论分析，并提出了改进系统动态性能的具体措施。     

导流槽阴极导杆安装方式对阴极表面电流分布的影响

将某厂现有的160kA Hall—Heroult铝电解槽改造成导流槽后，在阴极上表面和阳极底面呈斜坡状的条件下，计算了采用不同阴极导杆安装方式时阴极的电位和电流分布，即通过建立导流槽内部从阳极到阴极的一个半切片电热场模型，用有限元法分别对水平和平行于阴极斜坡两种不同导流槽阴极导杆的安装方式下阴极电位和表面电流密度分布进行了计算。结果表明，不同的阴极导杆安装方法对导流槽阴极的总电位降大小没有明显影响，但是水平阴极导杆安装更有利于阴极表面电流密度的均匀分布。     

基于UG参数化快速设计方法的研究及应用

基于UG三维软件阐述3种参数化设计方法及程序设计技术,论述了冷冲压模具中三维模型参数化设计方法,并提供了部分设计实例.综合运用3种参数化设计方法进行快速设计.     

Fe掺杂对Bi2Sr2Co2Oy热电性能和自旋关联的影响

采用固相合成法制备出系列Fe掺杂的Bi2Sr2Co2Oy，样品，并对样品进行XRD分析，电阻率（p）、热电势（固和顺磁共振研究。结果表明：Fe掺杂浓度x≤0．3时样品基本为单相。Fe掺杂使体系的电阻率略微增大，热电势显著升高，这可能与Fe掺杂降低了空穴载流子浓度有关。Fe掺杂浓度x=0．05样品获得最大的功率因子（power factor，S^2／P）。顺磁共振结果显示，不掺Fe的样品有着较强的顺磁共振（ESR）信号，随着Fe含量的增加，ESR信号向低频方向移动，并逐渐宽化减弱直至消失。这表明Fe掺杂改变了体系的自旋关联状态，占据了Co位参与了Co—O—Co之间的自旋关联。研究结果表明合适的元素掺杂可以有效地调整体系的自旋关联状态，改善材料的热电性能。     

氮基气氛碳渗炉气控制的实际

在讨论主题以前,得先回顾一下气体渗碳的炉气控制的历史。按传感器区分,大致可分为:露点仪时代,红外线式CO_2仪时代和氧分析仪时代。它们各约以十年为一个周期。现在是处于CO_2仪和氧分析仪的中间时代。按气氛区分为,碳氢化合物系气体,甲醇系和真空等多种。现在,氮基气氛引人注目。由于数次的石油危机冲击。气氛的主要原料碳氢化合物系气体的价格急刷上涨,采取怎样的对策已成了迫切的问题。其结果产生了氮基气氛渗碳技术。氮基气氛渗碳的特点氮基气氛渗碳的基本点是,不使用以前的Rx吸热式气氛,而是以氮气作为运载气,富化气和以前一样添加碳氢系气体,控制所要求的碳浓度的渗碳方法。     

氧化物弥散强化铁素体钢的电子辐照行为SCIEI

本文利用超高压电子显微镜进行电子辐照实验，分析了我国试制的氧化物弥散强化（ＯＤＳ）铁素体钢的辐照行国．在６７０－７２０Ｋ下辐照时观察到了辐照空洞的形成．辐照条件为７２０Ｋ，９ｄｐａ时的辐照肿胀率小于０．１％．同时在电子衍射图样中发现了明显的衍射环，分析表明这些衍射环的出现是由于电子辐照促进了Ｙ２Ｏ３微细相形成的缘故．