550 MPa级中厚板矫直过程中表面凹坑缺陷的成因与对策

针对550 MPa级高强中厚板在矫直过程中极易出现氧化铁皮压入凹坑缺陷的问题，根据现场矫直工艺，研究了在不同温度下进行热变形时试样表面和横截面的形貌，钢基体与氧化铁皮界面处平直度的变化规律。结果表明，热变形温度为450 ℃时，表面氧化铁皮开始出现裂纹，且随着变形温度的降低，裂纹的数量逐渐增加；此外，氧化铁皮与钢基体之间的界面长度随变形温度的降低而呈直线增加，表明氧化铁皮与钢基体界面平直度随着热变形温度的降低越发粗糙、易脱落而形成凹坑缺陷。为此，应适当提高终轧温度以确保矫直时钢板表面温度大于450 ℃，同时提高钢板的运行速率，防止氧化铁皮在低温变形发生破碎和脱落的同时降低氧化铁皮厚度，从而减小因氧化铁皮脱落而造成凹坑缺陷的发生几率。     

MICROSTRUCTURE OF RAPIDLY SOLIDIFIED TiAl ALLOY POWDER

The rapidly solidified powder of Ti-34Al-2Mn alloy was obtained by means of ultrasonicgas atomisation (USGA) technique.The tupical size of the powder is 27 μm.X-ray diffractionresults show that the powder consists of major α_2-phase and minor γ-phase.Under opticalmicroscope both equiaxed and dendritical microstructure features were observed on RS pow-der sections.After annealing at 900 ℃/for 2 h in vacuum,most of α_2-phase transforms intoγ-phase,resulting in refinement of structure.     

铁在盐酸中的缓蚀剂的两种作用类型的研究

通过腐蚀电位、极化曲线与交流阻抗测量研究了3种伯胺和丙炔醇对铁在盐酸中的缓蚀作用类型。结果表明,3种伯胺的缓蚀作用是几何覆盖效应,而丙炔醇的缓蚀作用则来自负催化效应。还证明,在强阳极极化的Tafel 直线区间,十二烷胺吸附在电极表面的覆盖率θ不随电位改变,十四烷胺的θ随电位的升高而增大。丙炔醇使铁阳极溶解反应活化能位垒增高的量.fa(θ)随电位升高而减小,其数值为df_a(θ)/dE=-73J·mol_-1.mV-1。     

半固态A356合金微观组织特征对充型能力的影响

采用电磁搅拌法制备了具有不同微观组织特征的半固态A356合金浆料,用图像分析软件对浇注前浆料金相试样的初生相微观组织特征进行了测定,利用间接挤压铸造方法铸造阿基米德螺旋线试样,以挤压成形后的螺旋线试样长度衡量充型能力,通过多元回归,建立了半固态A356合金初生相微观组织特征与充型长度之间的数学表达式。结果表明:半固态浆料充型能力不仅与初生相微观组织特征参数有关,微观组织特征参数的交互作用对充型能力的影响也较大。利用该表达式可以对半固态浆料充型能力进行预测,进而指导半固态浆料制备参数设计、间接挤压铸造工艺设计和缺陷预测。     

Structure, magnetization, and magnetostriction of Sm-R-Fe （R = Pr, Nd） thin films

The structure, magnetization, and magnetostriction of Sm0.9Pr0.1Fex and Sm1-xNdxFel.9 thin films have been investigated using X-ray diffraction, vibrating sample magnetometer, and optical cantilever method. It is found that the structure of Sm0.9Pr0.1Fex thin films consists of an Sm-Pr-Fe amorphous phase when x≤2.69 and that of Sm1-xNdxFel.9 thin films consists of an Sm-Nd-Fe amorphous phase. The in-plane magnetization of Sm0.91Pr0.1Fex thin films increases with increase in the Fe content, and low values of the in-plane coercivity occur in the range of 1.62≤ x≤ 2.28. The magnetostriction value of Sm0.91Pr0.1Fex thin films increases with increasing the Fe content when x ≤ 1.94 and decreases when x 〉 1.94. The in-plane magnetostriction of Sm1-xNdxFe1.9 thin films under low magnetic fields has been improved by the substitution of Nd for Sm when x = 0.2.     

ANSYS优化设计若干问题探讨

应用ANSYS软件进行优化设计过程中,从几何建模、网格剖分到选择设计变量、状态变量、目标函数和优化算法,都可能会出现问题甚至导致循环中断。分析讨论了一些共性问题并研究了解决办法,为顺利实现优化循环,应尽量使循环分析文件中的所有操作均作参数化处理;相对于结构参数优化,拓扑优化结果对载荷情况和网格密度等更为敏感;为节省优化循环用时,除了考虑计算性能外,还可考虑对模型进行模型简化、子结构处理、放松目标函数允差、使用适当数量的设计变量、尽量避免指定材料密度并选用合适的优化算法等。     

铸件内析出性气孔形成及演化的直接观察与分析

采用透明模型合金实时观察了铸件析出性气孔的形成发展,结果发现,纯物质凝固时,析出性气孔的产生发生于凝固型壳形成之后,随着凝固自型壁向中心凝固,呈现自周边向中心的气条生长。对于合金凝固,析出性气孔在凝固基本完成之后伴随着热裂及缩松的发生开始产生,呈现一定的偏聚现象。浇注前熔体过热度的提高将使析出性气孔更加密集,铸型和环境温度的降低有利于降低气孔的数量及分布范围,采用真空除气,可有效地抑制析出性气孔的产生和热裂缩松缺陷的形成。     

Al-Pb-Si-Sn-Cu轴瓦合金的微观结构及特征

采用机械合金化、冷压与热挤压法制备了Al-15％Pb-4％Si—1％Sn—1．5％Cu(质量分数，％)轴瓦合金。试验结果表明，块体材料的组织分布很均匀。Pb粒子细小均匀弥散分布在Al基体上，呈纳米晶粒。Al基体晶粒大小约1．2μm，在其晶界和晶粒内都有粒子析出。在Al基体上还分布着由非晶和亚微米晶粒构成的混合相。研究表明，该工艺是制备Al-Pb系列轴瓦合金的较佳方法；并为制备室温不互溶、高温存在很宽固溶间隙、有较大密度差异的合金组元且组织均匀的合金奠定了工艺基础。     

3003铝合金热变形流变应力特征

采用Gleeble-1500热模拟机进行圆柱体压缩实验．研究了3003铝合金在变形温度为300～500℃、应变速率为0．01～10s^-1、真应变为0～0．8条件下的流变应力特征。结果表明．流变应力随温度升高而降低，随应变速率的提高而增大；在应变速率小于10s^-1。时，3003铝合金首先出现加工硬化，流变应力达到峰值后单调下降，趋于平稳，表现出动态回复的特征；而在应变速率为10s^-1、变形温度在350℃以上时，合金发生了局部动态再结晶；可用Zener-Hollomon参数的双曲正弦形式来描述3003铝合金热压缩变形时的流变应力行为。