Wear mechanism of a novel AlSiMgAl2O4Al2O3 composite used in the low vessel of an RH secondary refining furnace

A novel AlSiMgAl₂O₄Al₂O₃ composite brick was prepared and evaluated in the low vessel of an RH (the initials of Ruhrstahl and Hereaeus) secondary refining furnace; it was characterized by X-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy. The results show that after use, the AlSiMgAl₂O₄Al₂O₃ composite has a functional gradient with an erosion zone–reinforced zone–original zone phase distribution, in which the phases in the erosion zone (0–1.8?cm) are a Mg-hercynite spinel solid solution, α-Al₂O₃, and minor amount of Al₃Fe₅O₁₂. Furthermore, the phases in the reinforced zone (1.8–5.0?cm) are γ-AlON, 21RSiAlON, SiC, Mg_0.388Al_2.408O₄, and α-Al₂O₃; i.e., the Al and Si in the composite are completely converted into non-oxide reinforced phases. Finally, the phases in the original zone (>5.0?cm) show no change. The reaction mechanism is as follows. During operation, a Mg-hercynite spinel solid solution is formed in the erosion zone due to a reaction between MgAl₂O₄ and FeO from a refinery operation. Therefore, the slag erosion of the material is improved. The Al and Si metals undergo active oxidation, and 21RSiAlON flakes are subsequently formed from the products of the metastable Al₂O(g), SiO(g), and N₂(g) in the ambient. The γ-AlON is formed by a carbothermal reduction nitridation of the α-Al₂O₃ and residual active carbon from the resin binder. The 21RSiAlON and γ-AlON reinforce the composite brick and improve its high temperature performance accordingly. Its service life is 110% that of the magnesia-chrome bricks used in the same period. The reaction model was also established.     

Fabrication of dense nano-laminated tungsten carbide materials doped with Cr3C2/VC through two-step sintering

This work investigates the critical roles of two-step sintering (TSS) and laminated structure on the sintering behavior and mechanical properties of functionally graded WC-TiC-Al₂O₃ nanostructured composite materials doped with Cr₃C₂/VC. Results show that excellent mechanical properties are achieved for tailored TSS conditions with a hardness of 27.91?±?2.3?GPa and a flexural strength of 1423.3?±?23.5?MPa. The desirable mechanical properties are attributed to the suppressed grain growth without densification deterioration. TSS is more effective in facilitating the favorable dispersion of secondary phase toughening nano-particulates in a WC matrix than conventional sintering (CS). Cr₃C₂/VC dopant plays an important role in maximizing and shifting the temperature range of the kinetic window for WC-Al₂O₃ composites. Al₂O₃ crack deflection, transgranular Al₂O₃, microcracking, WC crack bridging and plate-like WC crack deflection are the major toughening mechanisms. Residual surface compressive stress induced by the graded structure is also an appreciated contribution to the improvement of mechanical properties.     

Super-oleophilicity Co-doping Co2+/F-/TiO2 one-dimensional nanotubes for photocatalytic denitrification of light oil

In this study, a simple hydrothermal synthesis method was adapted for the preparation of Co-doping Co²⁺/F^-/TiO₂ nanotubes photocatalyst, and the micro-nano structure of catalysts prepared by biomimetic technology which makes the catalyst have super-oleophilicity property. Co²⁺/F^-/TiO₂ revealed improved photocatalytic performance for denitrification of light oil compared to single TiO₂ photocatalysts. The enhance of photocatalytic activity can be attributed to narrowing the band gap, increasing the light response wavelength and exposing more highly active crystal surfaces due to synergistic effects of Co²⁺ and F^? in the photocatalyst.     

课程群案例嵌入协同教学模式的探索

在课程群的教学中由于每门课程各自独立开展教学,缺乏知识的融合和衔接,导致学生运用综合知识解决问题的能力较弱。在课程群的教学中采用案例嵌入协同教学模式,将完整的工程案例嵌入到课程群各门课程的教学中,协同规划各门课程的教学任务,每门课程再围绕案例展开研究性教学。通过嵌入的工程案例衔接各门课程的知识点,帮助学生建构完整的知识体系,强化工程应用的概念；同时通过研究性教学,培养学生分析问题和解决问题的能力,两部分相结合,提高了学生运用综合知识解决复杂问题的能力。     

Mixed-Metal MOF-74 Templated Catalysts for Efficient Carbon Dioxide Capture and Methanation

The vast chemical and structural tunability of metal–organic frameworks (MOFs) are beginning to be harnessed as functional supports for catalytic nanoparticles spanning a range of applications. However, a lack of straightforward methods for producing nanoparticle-encapsulated MOFs as efficient heterogeneous catalysts limits their usage. Herein, a mixed-metal MOF, NiMg-MOF-74, is utilized as a template to disperse small Ni nanoclusters throughout the parent MOF. By exploiting the difference in Ni O and Mg O coordination bond strength, Ni²⁺ is selectively reduced to form highly dispersed Ni nanoclusters constrained by the parent MOF pore diameter, while Mg²⁺ remains coordinated in the framework. By varying the ratio of Ni to Mg in the parent MOF, accessible surface area and crystallinity can be tuned upon thermal treatment, influencing CO₂ adsorption capacity and hydrogenation selectivity. The resulting Ni nanoclusters prove to be an active catalyst for CO₂ methanation and are examined using extended X-ray absorption fine structure and X-ray photoelectron spectroscopy. By preserving a segment of the Mg²⁺-containing MOF framework, the composite system retains a portion of its CO₂ adsorption capacity while continuing to deliver catalytic activity. The approach is thus critical for designing materials that can bridge the gap between carbon capture and CO₂ utilization.