热压变形对灰口铸铁石墨形态的影响

研究了灰口铸铁(HTl50)在900℃大压下量塑性变形后石墨的分布形态，结果表明：随着压下量的增加，石墨片逐渐趋于平行分布；变形过程中发生了碳的回溶，同时伴随着石墨片的断裂；石墨片体积分数及片间距随压下量的增加而逐渐减少。     

稀土含量对喷熔层组织及耐蚀性的影响

本文通过在镍基自熔合金粉末中加入不同含量的稀土，研究了稀土含量对喷熔层组织及耐蚀性的影响规律及其作用机制。结果表明，在喷熔材料中加入适量稀土，可使喷熔层组织细化、晶界净化，从而使腐蚀过程中的表面活性点减少，耐蚀性提高。     

Preparation and properties of nanosize MnZn ferrite from δ-FeOOH

Ferrous ion was transformed into feroxyhyte (δ-FeOOH) by oxidation. Then, manganese sulfate and zinc sulfate in some ratio were added to the feroxyhyte solution. The co-precipitation was boiling reflux conditions sometime under constant stirring. The nanosize MnZn ferrite powder was formed. The mechanism of preparation of the nanosize MnZn ferrite was discussed, and the formation of feroxyhyte which was playing a key role during the process was mentioned. The properties of powder was tested by means of X-ray diffraction, transmission electron microscopy and vibrating sample magnetometer. The results show that the samples of spherical particles about 20 nm, which have characteristics of ferrimagnetism, has larger saturation magnetization, but the remanent magnetization and coercivity are comparatively smaller. The spinel MnZn ferrite nanosize powder was successfully prepared from δ-FeOOH at low temperature, with low-carbon steel and peroxide as main material.     

多孔β-TCP陶瓷药物载体的制备与体外释药速率的研究

本文用注浆成形的方法制备了以β-TCP为主晶相的多孔药物载体，体外测定了利福平的释药速率。实验结果表明，利福平在模拟体液中能够达到稳定的释放，可以作为骨结核手术后的辅助治疗。多孔β-TCP药物载体有望成为一种理想的药物缓释载体。     

Effect of cobalt oxide on surface structure of alumina supported molybdena catalysts studied by in situ Raman spectroscopy

A set of Co promoted 10% Mo/Al₂O₃ samples have been characterized by means of Raman spectroscopy under ambient as well as in situ dehydrated conditions. Under ambient conditions, the degree of the polymerization of surface molybdenum oxide species decreases with increasing Co loading. Under dehydrated conditions, the polymeric molybdenum oxide species is absent with the addition of only 0.2% Co. At low Co loadings (2%), before the formation of CoMoO₄ compound, the spectral features are very similar under ambient conditions. Dehydration causes the upward shift of the Mo=O symmetric stretching mode. A broad band around 920–930 cm^–1 was thus observed. This band has been suggested to be associated with the Co-Mo interaction species. In contrast to crystalline CoMoO₄, this species shows a reversibility on H₂ reduction-O₂ reoxidation treatments. From the results obtained, it is proposed that cobalt oxide interacts with the most polymerized molybdenum oxide species to form Co-Mo interaction species and/or crystalline CoMoO₄; therefore, the amount of the surface molybdenum oxide species decreases with a change in the molecular structure as a function of the Co concentration.     