LD7铝合金时效工艺的研究

通过试验系统地研究了ＬＤ７铝合金的单级和两级时效工艺。结果表明，与传统的单级时效相比，两级时效在不降低室温强度，硬度的前提下，可显著提高合金的电导率及高温性能。     

稳定态二氧化氯杀菌剂的制备及应用

稳定态二氧化氯(C1O2)是一新型杀菌消毒剂，具有高效、广谱、安全的特性，适用范围广，不产生对人体有害物质。介绍了稳定态ClO2的性质、检测、制备条件及其在有关领域的应用。     

扩链剂在PVC树脂生产中的应用

讨论了常见扩链剂的功能及在聚氯乙烯树脂生产中的应用。     

用瞬时法测定液体导热系数

以珠状热敏电阻为加热元件,建立了用瞬时法测定液体导热系数的装置,在25℃下用乙二醇等7个标准样品,对该装置进行了标定,平均偏差为2%.为了核实装置和所得关系式的可靠性,又测定了13个已知导热系数的样品,多数偏差在2%以内,最大偏差为5%.单次测量的精度为0.2%.本文叙述了这一方法的原理,并对实验结果进行了讨论.     

Rheological properties of mixtures of molten polymer and fluorocarbon blowing agent. I. Mixtures of low-density polyethylene and fluorocarbon blowing agent

The viscosities of mixtures of low-density polyethylene and fluorocarbon blowing agent were determined from the measurement of wall normal stress along the longitudinal axis of a capillary die. For the study, three different grades of commercial high-pressure low-density polyethylene were used, together with the following fluorocarbon blowing agents, dichlorodifluoromethane (FC-12), dichlorotetrafluoroethane (FC-114), and blends of FC-12 and FC-114. In the experiment, blowing agent concentration and melt temperature were varied for each combination of polymer and blowing agent employed. Analysis of the experimental data has led to a correlation between the viscosity reduction factor (VRF) and the blowing agent concentration, in which VRF is defined as the ratio of the viscosity of polymer-blowing agent mixture to that of the polymer alone. It was found that the correlation obtained is independent of shear rate and temperature and dependent upon only the type of fluorocarbon blowing agent. The practical significance of the correlation is discussed. We have shown that the entrance pressure drop obtained in the absence of phase separation in the entrance region may be used as a measure of the elastic properties of mixtures of fluorocarbon blowing agent and low-density polyethylene resin.     

浅析呼和浩特市大气SO2发展趋势及防治对策

本文通过对二氧化硫的形成及危害的阐述，以及对我市近几年大气中二氧化硫监测结果的分析，针对发展趋势和存在的问题，根据实际情况提出相应的建议。     

Morphologies and microstructures of tree-like carbon produced at different reaction conditions in a CVD process

Centimeter-size multi-branched tree-like carbon structures have been generated by the catalytic chemical vapor deposition of toluene using ferrocene as the catalyst precursor and investigated by means of SEM, TEM, and EDX. It is found that a temperature of 1000-1200 °C and a carrier gas flow rate of 1000-2500 ml/min are necessary for the generation of the carbon trees. Their morphologies and microstructures change greatly with the changing reaction conditions. The fractal dimensions of the trees are calculated to quantitatively investigate the influence of different reaction temperatures on the morphologies.     

Electrochemical micromachining of nitinol by confined-etchant-layer technique

The confined etchant layer technique has been applied to fabricate complex three-dimensional microstructures on nitinol for the first time. HF and HNO₃ were locally and simultaneously electrogenerated at the mold surface to etch a nitinol workpiece. NaOH was used as an efficient scavenger to confine the etchant close to the mold. Cyclic voltammetry was employed to study the electrochemical behavior of a Pt electrode in the etching solution in order to choose an appropriate potential for etchant generation on the mold. The thickness of the confined etchant layer was estimated to be several micrometers by inspecting the deviation of the sizes of the etched spots from the sizes of those on the microelectrode. Thus, the composition of the electrolyte could be optimized for better etching precision. By optimizing the composition of the electrolyte, complex microstructures on a Pt-Ir mold bearing the logo “XMU” of Xiamen University were successfully fabricated on nitinol. The etched patterns were approximately negative copies of the mold, and the precision of duplication could easily reach the micrometer scale.     

矾土尖晶石钢包浇注料的研制与应用

采用特级矾土熟料为骨科，天然出合成的镁铝尖晶石为部分基质，选用新型复合结合剂研制成矾土尖晶石质钢包浇注料．使用结果表明：一次性寿命较传统的铝镁浇注料提高８０％以上．