A novel bio‐based phthalonitrile resin derived from catechin: synthesis and comparison of curing behavior with petroleum‐based counterpart

The development of bio‐based thermosetting resins with good thermal stability can potentially afford sustainable polymers as replacements for petroleum‐based polymers. We report a practical route to a novel catechin‐based phthalonitrile resin precursor (CA‐Ph), which contains free phenolic hydroxyl groups that result in ‘self‐curing’ at elevated temperatures to afford a thermostable polymer. Comparison of the performance of this CA‐Ph resin with that of a conventional petroleum‐based bisphenol A phthalonitrile resin (BPA‐Ph; containing 5 wt% of the curing agent 4,4′‐diaminodiphenylsulfone) revealed that CA‐Ph exhibits a lower melting point and curing temperature. Cured CA‐Ph resin retains 95% of its weight at 520 °C under a nitrogen atmosphere, which compares favorably with results obtained for BPA‐Ph resin that retains 95% of its weight at a lower temperature of 484 °C. Kinetic results indicated that the curing reactions of both CA‐Ph and BPA‐Ph systems follow an autocatalytic mechanism. These results suggest that catechin is a useful bio‐based feedstock for the preparation of self‐curing and thermally stable phthalonitrile resins for advanced technological applications. © 2017 Society of Chemical Industry     

内插法在相关干涉仪测向体制中的应用

测向误差的减小一直以来都是无线电测向精度提高的一个难点,对于不同的测向体制所采用的减小测向误差的方法都不尽相同。本文主要介绍的是相关干涉仪测向体制的基本原理以及通过内插法的应用来减小测向误差的方法。     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

我公司延长耐火砖寿命的工艺管理措施

正0引言我公司有两条2 500 t/d的熟料生产线,于2000年先后投产,现正常生产,随着近年来对耐火材料使用的技术攻关和精心管控,烧成带窑砖使用寿命超过40个月。下面就我公司的延长耐火砖寿命的工艺管理措施进行介绍,供借鉴研讨。     

碱蓬多糖SSP1-1的分离纯化及其抗肿瘤活性

目的:本实验对水溶性碱蓬(Suaeda salsa)多糖SSP1-1进行分离纯化并对其抗肿瘤活性进行初步研究。方法:采用水提醇沉法提取碱蓬粗多糖,通过DEAE-52纤维素柱和Sephadex G-75葡聚糖凝胶柱分离纯化碱蓬粗多糖,得到单一碱蓬多糖SSP1-1,利用高效凝胶渗透色谱法(HPGPC)对其纯度及分子量进行分析,利用MTT、Hoechst 33342染色,Western blot方法对碱蓬多糖SSP1-1的抗肿瘤活性进行研究。结果:SSP1-1分子量为60.32 kDa;SSP1-1具有时间-剂量依赖性抑制肿瘤细胞增殖作用,当SSP1-1浓度为500 μg/mL时,HepG2细胞在24和48 h的细胞活力分别为52.8%和50.2%,Hoechst 33342染色实验观察到SSP1-1可引起HepG2细胞核出现典型的细胞凋亡特征;Western blot证明SSP1-1可以降低Bcl-2的蛋白表达,提高Bax和Caspase-3的蛋白表达,各组蛋白含量与对照组相比均具有显著性(P<0.05)。结论:SSP1-1为均一组分多糖,并对肿瘤细胞具有显著的抑制作用,为进一步开发利用碱蓬多糖奠定了基础。     

Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Single-Crystalline TiO2(B) Nanobelts with Unusual Large Exposed {100} Facets and Enhanced Li-Storage Capacity

The {100} facet of single-crystalline TiO₂(B) is an ideal platform for inserting Li ions, but it is hard to be obtained due to its high surface energy. Here, the single-crystalline TiO₂(B) nanobelts from H₂Ti₃O₇ with nearly 70% {100} facets exposed are synthesized, which significantly enhances Li-storage capacity. The first-principle calculations demonstrate an ab in-plane 2D diffusion through the exposed {100} facets. As a consequence, the nanobelts can significantly accommodate Li ions in LiTiO₂ formula with specific capacity up to 335 mAh g⁻¹, which is in good agreement with the electrochemical characterizations. Coating with conductive and protective poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate), the cut-off discharge voltage is as low as 0.5 V, leading to a capacity of 160.7 mAh g⁻¹ after 1500 cycles with a retention rate of 66% at 1C. This work provides a practical strategy to increase the Li-ion capacity and cycle stability by tailoring the crystal orientation and nanostructures.