纳米共晶晶须复相陶瓷的刚度预报

用SHS技术制备的纳米共晶晶须复相陶瓷具有较大的断裂韧性和较高的塑性形变行为,其组织结构以纳米共晶晶须为基体.运用Mori-Tanaka方法研究了复合共晶晶须的等效本征应变,并得到了复合共晶晶须的应力应变关系.通过应力应变关系计算出复合共晶晶须的刚度,复合共晶晶须为横观各向同性,具有5个独立的弹性常数.根据复相陶瓷的应变均值,考虑复合共晶晶须方位的随机性,计算出材料的有效弹性模量和泊松比,复相陶瓷材料为各向同性体.     

环境条件下Ni3Al类型金属间化合物的疲劳行为

综述近年来Ni_3Al类型金属间化合物疲劳行为的研究进展，着重讨论了温度和介质对材料疲劳性能的影响。氢和水蒸汽的存在促进了裂纹的扩展；试验温度的升高使Ni_3Al类型合金的疲劳裂纹扩展速率增大。     

Vision-based detection of MAG weld pool

Weld pool contains significant information about the welding process. The weld pool images of MAG welding are detected by LaserStrobe system. An algorithm for extracting weld pool edge is proposed according to the characteristics of MAG weld pool images. The maximum weld pool length and width are calculated. The measurement data can be used to verify the results of welding process simulation and to provide a good foundation for automatic control of MAG welding process.     

外场作用下由工业TiOSO4液合成介孔二氧化钛

以工业硫酸氧钛为钛源,采用复合模板合成路线,分别于超声,微波和水热外场作用下合成了介孔二氧化钛前驱体.通过调节反应体系的pH值来控制TiOSO4液的水解和缩聚速率.煅烧脱除模板后得到锐钛型的介孔二氧化钛.产物采用XRD,氮等温吸附脱附,粒度分布,SEM,TEM,SAD和X射线能谱分析(XPS)等技术进行了表征.结果表明具有强极化作用和温和水热环境的外场利于制备结构更佳的介孔二氧化钛;超声振动利于介观结构的形成.在微波辐照下,所制得介孔二氧化钛的比表面积为146.6 m2/g,平均孔径2.57 nm,晶粒尺寸13.65 nm.超声、微波和水热较常规合成方法更利于形成和稳定介孔结构.     

Plasma spray forming of functionally graded materials mould

A new technology of functionally graded materials(FGM) mould fabricated by plasma spraying and arc spraying was developed. According to applied characteristic of plastic mould, the reasonable coatings of FGM were designed and their microstructures were analyzed. At the same time, some key problems were solved including spray mould fabricating, FGM forming and demoulding, etc. The results show that the service performance of the FGM mould is much more excellent than the one composed of the traditional materials, and the life span can also be greatly increased. The technology will have a significant influence on materials development in mould industry.     

A359-Zr(CO3)2体系反应合成复合材料的组织及润滑磨损性哪

研究了新型反应体系A359-Zr（CO3）2熔体反应法制备的（Al3Zr＋Al2O3）p／A359复合材料边界油润滑条件下的滑动磨损性能。结果表明，由于颗粒的支撑减磨作用，复合材料的磨损量随载荷的增大和时间的延长均远小于基体材料，当载荷为1176N时体积分数为12％的复合材料磨损量为4．9mg，而基体材料的磨损量为27．5mg，复合材料比基体材料耐磨性提高了6倍；由磨损表面SEN观察表明：基体A359合金存在严重粘着和变形，表现为粘着磨损和剥层磨损，复合材料的磨损类型表现为磨粒磨损。     

超音速微粒高能轰击16MnR钢表面纳米化的研究

采用冷气动力超音速微粒高能轰击技术对16MnR低合金钢表面进行处理,利用扫描电镜、透射电镜和X衍射方法对基体表面的微观形貌和结构进行分析.试验结果表明:试样经过超音速微粒轰击处理后可以使表层晶粒细化至纳米量级,平均晶粒的尺寸为14.2 nm;处理后表层主要产生压应力;处理后表层的显微硬度增加.     

我国锌的再生利用

锌是重要的金属材料,在国民经济的许多领域具有广泛的用途.近年来世界锌生产和消费均不断增长,目前全球锌的产量和消费量已经超过900万吨,从生产和消费数量上是仅次于铝、铜,居第三位的有色金属.     

大块非晶合金的形成能力及研究进展

综合评述了大块非晶合金形成的控制因素，从热力学、动力学和结构三个方面讨论了大块非晶合金的形成机理；并简介了大块非品合金的制备技术和研究现状。     

压缩机活塞挤压铸造成形技术研究

通过提出几种不同的挤压铸造工艺方案，研究了挤压铸造技术成形压缩机活塞的可行性。结果表明，采用直接式挤压铸造以1模4型腔，对保证制件质量，提高生产效率是有利的；采用间接式挤压铸造以液流从制件两端厚壁处进入型腔，模具以侧抽芯拉杆式卸料机构更为合理。