表面渗铬T8钢中碳迁移的热力学分析

采用双辉等离子渗铬技术，对T8钢进行了900℃温度表面渗铬合金化；使用GDA750．测量了试样渗铬合金层中Fe、Cr和C等元素的浓度分布。通过热力学分析计算，研究了渗铬合金化层形成过程中碳迁移机理和规律。指出驱动碳迁移的动力是碳的括度梯度，并推导出富碳区碳质量分数随铬质量分数变化的数学关系式：w(C）=0．8 0.3536w(Cr)。计算结果与试验结果相当吻合。     

Thermal expansion anomaly and spontaneous magnetostriction of Dy2AlFe14Mn2 compound

The structure and magnetic properties of Dy₂AlFe₁₄Mn₂ compound were investigated by X-ray diffractometry and magnetization measurements. Dy₂AlFe₁₄Mn₂ compound has a hexagonal Th₂Ni₁₇-type structure. Zero thermal expansion and negative thermal expansion were found in Dy₂AlFe₁₄Mn₂ compound in the temperature range from 184 to 264 K, and from 264 to 383 K, respectively, by X-ray dilatometry. The spontaneous magnetostrictive deformations from 104 to 400 K were calculated. The results show that the spontaneous volume magnetostrictive deformation increases firstly with increasing temperature, and then decreases with further increasing temperature.     

基于视觉传感的焊缝中心检测技术研究

通过视觉传感器获取焊缝图像，采用多种去噪技术对焊缝图像中的噪声进行滤波试验。针对焯缝图像中的干扰噪声特性，对各种滤波方法进行了分析和比较，并对滤波效果较好的焊缝图像进行边缘检测计算。提出3种识别焊缝特征的组合图像处理方法，并研究提取焊缝中心特征信息的效果和精度。试验结果表明，对焊缝图像采用Wiener滤波与Robert边缘检测算法能较好地提取焊缝中心位置的特征信息。     

WCp增强钢基表层复合材料的两体磨粒磨损性能

在室温条件下,选用销盘磨粒磨损试验机,绿碳化硅磨料,研究增强相WC颗粒直径对WCp增强钢基表层复合材料磨损性能的影响,以正火ZG45作为标样,计算相对耐磨性ε值.研究结果表明,WCp增强钢基表层复合材料相对于正火ZG45的相对耐磨性ε值,随其增强相WC颗粒直径的变小而降低,当增强相WC颗粒直径大于150μm时,相对耐磨性ε值高达40左右,而当增强相WC颗粒直径小于100μm时,相对耐磨性ε值降低到5以下.     

基于VERICUT的虚拟龙门加工中心建模和仿真关键技术研究

为减少零部件试切,检验数控工艺合理性,构建了虚拟龙门加工中心。研究了龙门加工中心运动,阐述了侧面铣头运动由旋转中心和换刀点控制,提出了虚拟机床侧面铣削运动构建方法,可实现各角度侧面铣。搭建了虚拟加工环境,通过零件仿真加工,完成了零件顶面及4个侧面的铣削加工,验证了数控代码的正确性,检验了数控工艺合理性,减少了零件试切,缩短了开发周期,仿真结果表明虚拟龙门加工中心的正确性。     

基于MATLAB的节流阀调速液压回路计算机仿真

以进油节流阀调速液压回路为例,建立了描述液压调速回路动态特性的集中参数数学模型,给出了在MATLAB环境下建立其仿真模型的方法.应用计算机仿真的方法,研究了节流阀开口度的不同和油液体积弹性模量值的改变对进油节流调速回路动态特性的影响,给出了仿真结果.     

浇注法制备表面复合材料用复合剂的强度表征及测试

用改进后的强度测试仪，检测分析了三种自制复合剂不同温度下的抗弯强度，探讨了复合剂强度的测试方法，结果表明：抗弯强度可用来表征用于浇注法制备金属基复合材料的复合剂强度，抗弯强度越高，铸件浇铸成型率越高。     

The Study of Plasma Nitriding of AISI304 Stainless Steel

This paper presents results on the plasma nitriding of AISI 304 stainless steel at different temperatures in NH3gas. The working pressure was 100～200 Pa and the discharge voltage was 700～800V. The phase of nltrided layer formed on the surface was confirmed by X-ray diffraction. The hardness of the samples was measured by using a Vickers microhardness tester with the load of 50g. After nitriding at about 400℃ for two hours a nitrided layer consisting of single γN phase with thickness of 51.tm was obtained. Microhardness measurements showed significant increase in the hardness from 240 HV (for untreated samples) up to 950 HV (for nltrided samples at temperature of 420℃). The phase composition, the thickness, the microstructure and the surface topography of the nltrided layer as well as its properties depend essentially on the process parameters.     

表面完整性对马氏体不锈钢疲劳性能的影响

研究了马氏体不锈钢表面喷丸强化后表面粗糙度，表面形貌，表面残余应力和表面层残余压应力场等表面完整性的变化及其对疲劳性能的影响，结果表明：马氏体不锈钢对表面粗糙度比较敏感，经喷丸强化后产生的残余压应力有利于提高疲劳寿命，且采用低喷丸强度时对疲劳性能更加有利。     

FeAl/FeAlSi非对称膜材料的制备及膜基结合性能

目的制备高温腐蚀环境下应用的Fe Al/Fe Al Si非对称膜材料,研究膜与基体的结合性能。方法采用粉末反应合成法制备大孔径、高孔隙度的FeAlSi多孔体作为支撑体,通过浸渍法在支撑体表面制备小孔径的FeAl涂层作为膜层,再经烧结得到Fe Al/Fe Al Si非对称膜材料。研究Fe Al/Fe Al Si非对称膜材料的孔结构性能及膜基结合性能。采用XRD和SEM研究多孔膜材料的物相组成及微观形貌,采用孔结构测试仪及压汞法测试支撑体与膜层的孔结构参数,采用拉伸法和反吹实验研究Fe Al/Fe Al Si非对称膜材料的膜基结合性能。结果 Fe Al/Fe Al Si非对称膜材料表面膜层均匀、完整,膜层与支撑体之间具有冶金结合。支撑体的孔隙度和平均孔径分别为43.0%和22.7μm,膜层的孔隙度和平均孔径分别为36.5%和7.5μm。当膜层厚度增加时,膜材料的透气度下降,最大孔径在一定膜层厚度范围内变化不大,当膜层厚度在150～300μm范围内时,最大孔径约为7.8μm。膜层与支撑体的结合强度大于5.5 MPa。结论浸渍法制备的Fe Al/Fe Al Si非对称膜材料的孔结构性能优异,膜基结合性能满足工业应用。