Thermodynamic Assessments of Ternary Ga-As-P,Ga-P-Sb,In-As-P and In-P-Sb Systems

1 ＩｎｔｒｏｄｕｃｔｉｏｎＭｕｃｈａｔｔｅｎｔｉｏｎｈａｓｂｅｅｎｐａｉｄｔｏⅢ Ⅴｓｅｍｉｃｏｎｄｕｃｔｏｒｃｏｍｐｏｕｎｄｓｆｏｒｄｅｃａｄｅｓｂｅｃａｕｓｅｏｆｔｈｅｉｒｉｍｐｏｒｔａｎｔａｐｐｌｉｃａｔｉｏｎｓｉｎｏｐｔｏｅｌｅｃｔｒｏｎｉｃａｎｄｈｉｇｈｓｐｅｅｄｅｌｅｃｔｒｏｎｉｃｄｅ ｖｉｃｅｓ .Ｔｈｅｍａｔｅｒｉａｌｓｏｒｄｅｖｉｃｅｓｃａｎｂｅｇｒｏｗｎｂｙｌｉｑｕｉｄｐｈａｓｅｅｐｉｔａｘｙ (ＬＰＥ ) ,ｃｈｅｍｉｃａｌｖａｐｏｒｄｅｐｏｓｉｔｉｏｎ(ＣＶＤ) ,ｍｏｌｅｃｕ ｌａｒ…     

Effect of elastic strain energy on the core-shell structures of the precipitates in Al-Sc-Er alloys

The effect of the elastic strain energy on the core-shell structures was studied in an Al-0.06Sc-0.02Er (at.%) alloy. A theoretical model for the calculation of the elastic strain energy caused by core-shell precipitates, which is applicable to materials with weak elastic ani-sotropy, was adopted. It was demonstrated that the partitioning of Er to the precipitate core did not reduce the elastic strain energy as expected in the previous study. The resistance due to the elastic strain energy to form an Al3(Sc0.36Er0.64)-Al3(Sc0.8Er0.2) core-shell precipitate was quite small, and could be easily overcome by the decrease of the total interfacial energy, which was consistent with the previous experimental re-sults. On the other hand, the resistance due to the elastic strain energy to form an Al3Er-Al3Sc core-shell precipitate was much larger than that to form an Al3(Sc0.36Er0.64)-Al3(Sc0.8Er0.2) core-shell precipitate, thus the partitioning of all the Er atoms to the core was strongly hindered by the elastic strain energy and was not observed in the experiment of the previous study.)     

45钢活塞杆表面发纹产生原因

用45钢圆钢生产工程机械高压油缸用活塞杆时,发现2支活塞杆电镀后存在发纹缺陷.对缺陷样进行了化学成分、金相组织、扫描电镜和能谱等分析,认为机加工中的表面划伤和原材料中的夹杂物是产生发纹的原因.     

二元合金过冷液态的形核驱动力和非晶形成能力的热力学分析

利用CALPHAD(calculation of phase diagrams)技术和已有热力学数据,通过对比分析亚稳过冷液态合金中各结晶相的形核驱动力大小,寻找结晶能力弱而非晶形成能力强的成分范围.选择典型的非晶形成体系,以平衡相图中共晶深度明显不同的3个二元合金体系Cu-Zr,Ni-Nb和Pd-Si为研究对象,预测各体系非晶形成能力与成分的关系,获得非晶形成最优成分,并与共晶点成分及实验数据进行对比.预测结果与实验确定的块体非晶最优成分相符.     

Thermodynamic Assessments of Al-In-Sb and Al-In-As Systems

1 ＩｎｔｒｏｄｕｃｔｉｏｎⅢ Ⅴｓｅｍｉｃｏｎｄｕｃｔｏｒｍａｔｅｒｉａｌｓｏｒｄｅ ｖｉｃｅｓｃａｎｂｅｇｒｏｗｎｂｙｌｉｑｕｉｄｐｈａｓｅｅｐｉｔａｘｙ(ＬＰＥ) ,ｃｈｅｍｉｃａｌｖａｐｏｒｄｅｐｏｓｉｔ(ＣＶＤ ) ,ｍｏｌｅｃｕｌａｒｂｅａｍｅｐｉｔａｘｙ(ＭＢＥ)ａｎｄｓｏｏｎ .Ｒｅｌｉａｂｌｅｔｈｅｒｍｏｄｙｎａｍｉｃｄａｔａａｒｅｒｅｑｕｉｒｅｄｆｏｒｔｈｅｔｈｅｒｍｏｄｙｎａｍｉｃａｎａｌｙｓｅｓｏｆｔｈｅｓｅｐｒｏｃｅｓｓｅｓｔｏｏｂｔａｉｎａｏｐｔｉｍｕｍｄｅｓｉｇｎ[1 ].ＡＡｌ Ｇａ …     

NH3分解率对GaN半导体MOVPE外延生长成分空间的影响

研究了以三甲基镓 (TMGa)和氨 (NH3 )为气源物质 ,以氢气 (H2 )为载气进行GaN半导体的金属有机物气相外延 (MOVPE)生长时 ,NH3 分解率对于GaN半导体外延生长的成分空间的影响。热力学计算结果表明 :随着NH3分解率的提高 ,用于生长GaN外延层的气 固两相区逐渐向高Ⅴ /Ⅲ比方向变小 ,解释了实际生长过程中Ⅴ /Ⅲ比要求很高的原因。预计高的Ⅴ /Ⅲ比及低的NH3 分解率有助于GaN的MOVPE外延生长。     

合金钢淬透性曲线预测

本工作通过计算标准顶端淬火冷却曲线,并利用计算得到的CCT曲线和数据,对合金钢淬透性曲线进行了预测。     

Fe-C基三元合金相图计算

本工作设计了Fe-C基三元合金热力学计算软件,它可计算Fe-C与Cr、Mn、Si、Cu、Mo、W、Ni、V、Ti、Nb组成的三元系在不同温度下的等温截面图,并可提供有关的热力学数据。     

气相分压对Co-Fe-Sb三元体系相平衡和相稳定性的影响

通过真空条件下Co-Fe-Sb三元体系1 073 K等温截面测定、Co-Fe-Sb三元体系凝聚态的热力学优化评估和气相组分的热力学数据计算,分析气相压力对该体系中二元和三元体系的相平衡和相稳定性的影响。结果表明:随着气相压力减小到一定程度,Co-Sb、Co-Fe、Fe-Sb和Co-Fe-Sb体系中的固相化合物相开始发生挥发分解,出现气液固三相平衡区,计算所得温度—压力曲线图表明每种化合物相都存在一个理论的压力极小值,并对应一个温度,在此压力之上或温度以下,不发生化合物由固相转变成气相的分解,凝聚态相保持与常压下基本相同的相平衡关系。计算结果从热力学上很好地解释了含Sb热电材料在试验研究和材料制备过程中存在的问题,对制备该化合物的工艺设计具有很好的参考作用。     

均匀化和深冷处理对3104铝合金变形行为的影响(英文)

利用电子万能拉伸试验机、扫描电子显微镜(SEM)、透射电子显微镜(TEM)研究3104铝合金经不同复合热处理制度(深冷处理+均匀化处理)处理后的力学性能和变形特征。先经深冷处理再均匀化处理的试样具有优异的综合力学性能,其抗拉强度、屈服强度和伸长率分别比仅经常规均匀化处理的试样提高了29%、41%和11%。经均匀化处理的试样的应力-应变曲线出现Portevin-Le Chatelier效应,而仅经受深冷处理的试样没有出现Portevin-Le Chatelier效应。这表明先深冷处理再均匀化处理可以促进3104铝合金中第二相弥散析出,大量细小、均匀分布的沉淀相强化了溶质原子对位错的钉扎效应,提高了3104铝合金的临界应变值。