00Cr22Ni5Mo3N双相不锈钢热加工性能的试验研究

采用热压缩和热拉伸试验方法,对00Cr22Ni5Mo3N双相不锈钢的高温变形抗力、高温塑性以及在高温变形时的奥氏体相的数量进行了研究。试验结果表明,00Cr22Ni5Mo3N双相不锈钢的高温变形抗力和高温塑性较0Cr18Ni10Ti奥氏体不锈钢低,在1100～1250℃变形时,钢中奥氏体相的数量可以控制在适合热加工的范围,使钢具有较好的热加工性能。     

Morphology, structure and formation mechanism of silicide coating by pack cementation process

The MoSi2 coating on C 103 niobium based alloy was prepared by pack cementation method. The formative mechanism, morphology and structure of coating were investigated. The silicide coating was formed by reactive diffusion obeying parabolic rule during pack cementation process. It is found that the composite structural coating is composed of three inferior layers as follows. The main layer is composed of MoSi2, the two phases＇ transitional layer consists of NbSi2 and a few NbsSi3 and the diffuse layer is composed of NbsSi3. The dense amorphous glass layer formed on the surface at high temperature oxidation circumstance can effectively prevent the diffusion of oxygen into coating.     

Temperature Dependence of the Magnetocrystalline Anisotropy in Nd_2Co_(14)B Compound

Easy and hard magnetization curves of Nd_2Co_(14)B compound have been measured withextracting-sample-magnetometer(μ_0H_(max)=6T)at 10～300 K.Magnetic anisotropy constants K_1 and K_2have been determined by fitting the hard magnetization curves,in which only K_1 ,K_2 and misalignment anglehave been taken as fitting parameters.The values of K_1 and K_2 at 4.2 K were derived by extrapolation.Anisotropy coefficients,x_2~° and x_4~°were derived from the anisotropy constants.The anisotropy constant K_2increases rapidly with increasing temperature when TT_(sr).The temperature depen-dence of the magnetic anisotropy coefficient x_2~° was fitted with the formula.The anisotropy coefficients x_2~°can be well described by the tenth-power law from 4.2 K to T_(sr)and by the sixth-power law from T_(sr_ to 300 K.     

差厚拼焊板拉延反鼓包方盒件的成形性研究

本文利用数值模拟技术对相同材质差厚拼焊板的冲压成形性和焊缝移动进行研究 ,分析了相同拉延深度、不同拉延方式下焊缝移动情况 ,揭示了不同拉延方式下焊缝移动的一般规律和焊缝移动量与差厚拼焊板成形性之间的关系。并提出一种控制焊缝移动的方法。     

Ti-4.5Al-3V-2Mo-2Fe钛合金板材加工与性能

Ti-4.5Al-3V-2Mo-2Fe钛合金是一种α+β两相钛合金,有优良的加工性,其冷轧加工率可达到70%.在很宽的热处理条件下,它的组织非常细,初生α晶粒尺寸不大于3μm.细的组织结构使它具有优良的综合力学性能,在700℃具有良好的超塑性.     

基于Petri网的多轴机床故障诊断研究

本文分析了多轴机床安装和生产中所面临的故障问题，结合故障诊断问题的特点，在基于Petri网基本原理的前提下，建立了故障诊断的Petri网模型，并分析了故障的传播机理。     

铝合金扁锭宽面竖状皱褶缺陷的成因

介绍了铝合金扁锭出现竖状皱褶缺陷的某些规律，分析了竖状皱褶缺陷产生的原因及其防止的途径，并进行了防止竖状皱褶缺陷的现场试验.     

熔模铸造型壳的现状

熔铸铸造正向大型、精密方向发展，对型壳提出了更高要求。由于环保要求的提高，醇基硅酸乙酯的使用受到限制，硅溶胶的应用越来越广泛。耐火材料的粘结剂的正确选择，涂料粉液比和涂料粘度的合理控制将大大提高型壳性能。介绍了型壳性能检测方法。     

TA15钛合金A-TIG焊接头组织和性能分析

以CaR与MgF2的混合物为活性荆，对TA15钛合金A-TIG焊接头组织和性能进行了分析，并和常规TIG焊进行了比较。结果表明：A-TIG焊能够有效减少气孔数量，提高接头的抗拉和抗弯性能；与常规TIG焊相比，A-TIG焊HAZ较窄且组织较细，而二者的焊缝区组织基本相同；活性荆的加入并没有降低A—TIG焊接头的耐腐蚀性能。     

消失模铸造传质过程与铸件品质控制

消失模铸造是1 种有利于环保的近净成形铸造方法，在消失模工艺的浇注过程中，模样分解为液态或气态产物。为了生产合格的铸件，须选用具有合适透气性和液态产物浸润能力的涂料，以控制分解产物的传质过程。说明设计在高温下测试涂料透气性的仪器是必要的。