Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.     

Enhance cycling performance of LiMn2O4 cathode by Sr2+ and Cr3+ doping

Spinel LiSr_0·1Cr_0·1Mn_1·8O₄ was synthesised by high temperature solid state method in order to enhance the electrochemical performance. The LiSr_0·1Cr_0·1Mn_1·8O₄ (LSCMO) materials were characterised by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. The XRD and SEM studies confirm that LSCMO had spinel crystal structure with a space group of Fd3m, and the particle of LSCMO shows irregular shape. The cyclic voltammetry data illustrated that the heavy current charge–discharge performance of LMO was improved by Sr²⁺ and Cr³⁺ doping. The galvanostatic charge–discharge of LSCMO cathode materials was measured at 1, 5, 10 and 20 C. The results indicated that LSCMO improved the capacity retention.     

Fabrication of tungsten oxide photoanode by doctor blade technique and investigation on its photocatalytic operation mechanism

WO₃ is a potential material candidate for construction of photoanode for solar driven water splitting. In this work, μm-thick porous WO₃ photoanode is prepared by depositing a stable ink made of WO₃ nanoparticles and Aristoflex velvet polymer in water using the doctor blade technique, followed by a sintering in air. The nature of WO₃ nanoparticles, its loading mass on F-doped tin oxide electrode as well as sintering temperature are examined in order to optimize the photocatalytic activity of the resultant WO₃ photoanode. The operation of WO₃ photoanode is investigated by varying the light illumination direction and light incident intensity as well as changing the nature of the electrolyte. Dissolved tungsten in electrolyte is quantified by ICP-MS providing insights into the influences of electrolyte nature and operating conditions to the corrosion of WO₃. It is proposed that the H₂O₂ and OH^. radical generated as by-products of the photo-driven water oxidation on the photoanode surface are harmful species that accelerate the dissolution of WO₃.