Trenched‐Sinker LDMOSFET (TS‐LDMOS) Structure for 2 GHz Power Amplifiers

This paper proposes a new LDMOSFET structure with a trenched sinker for high‐power RF amplifiers. Using a low‐temperature, deep‐trench technology, we succeeded in drastically shrinking the sinker area to one‐third the size of the conventional diffusion‐type structure. The RF performance of the proposed device with a channel width of 5 mm showed a small signal gain of 16.5 dB and a maximum peak power of 32 dBm with a power‐added efficiency of 25% at 2 GHz. Furthermore, the trench sinker, which was applied to the guard ring to suppress coupling between inductors, showed an excellent blocking performance below ?40 dB at a frequency of up to 20 GHz. These results confirm that the proposed trenched sinker should be an effective technology both as a compact sinker for RF power devices and as a guard ring against coupling.     

Tensile fracture and failure behavior of technical flax fibers

The apparent tensile strength of technical flax fibers was determined in single‐fiber tests at various clamping lengths (20, 40, and 80 mm) and the outcome was compared with literature data. It was demonstrated that the strength of flax at each clamping length obeyed the two‐parameter Weibull model. The failure mode and sequence were studied in situ (i.e., during loading) by SEM and acoustic emission (AE). The failure sequence (axial splitting of the technical fiber along its elementary constituents, radial cracking of the elementary fibers, multiple fracture of the elementary fibers) concluded reflected the hierarchical build‐up of the flax bast fibers. To the above failure events AE amplitude ranges were assigned. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3638–3645, 2003     

Positively Thermo‐Sensitive Monodisperse Core–Shell Microspheres

In this paper, we report on a novel family of monodisperse thermo‐sensitive core–shell hydrogel microspheres that is featured with high monodispersity and positively thermo‐responsive volume phase transition characteristics with tunable swelling kinetics, i.e., the particle swelling is induced by an increase rather than a decrease in temperature. The microspheres were fabricated in a three‐step process. In the first step, monodisperse poly(acrylamide‐co‐styrene) seeds were prepared by emulsifier‐free emulsion polymerization. In the second step, poly(acrylamide) or poly[acrylamide‐co‐(butyl methacrylate)] shells were fabricated on the microsphere seeds by free radical polymerization. In the third step, the core–shell microspheres with poly‐ (acrylamide)/poly(acrylic acid) based interpenetrating polymer network (IPN) shells were finished by a method of sequential IPN synthesis. The proposed monodisperse core–shell microspheres provide a new mode of the phase transition behavior for thermo‐sensitive “smart” or “intelligent” monodisperse micro‐actuators that is highly attractive for targeting drug delivery systems, chemical separations, sensors, and so on.     

High‐Performance,Monolithic Polyaniline Electrochemical Actuators

New polyaniline (PANI) asymmetric membranes were fabricated using a phase‐inversion technique with hexane as the coagulation bath. These membranes exhibit a dense structure with macrovoids distributed asymmetrically throughout the cross‐section. A stress–strain study demonstrated that the Young's modulus (1.421 GPa) and strain at break (7.6 %) of the new PANI asymmetric membranes prepared from hexane are approximately 12 and 4 times higher, respectively, than the values reported previously for the PANI integrally skinned asymmetric membranes (ISAMs) (123 MPa Young's modulus and 1.8 % strain at break). Furthermore, monolithic electrochemical actuators based on a single PANI asymmetric membrane were constructed, and a bending movement of up to 20 Hz was experimentally recorded in a hydrochloric acid aqueous solution. A lifetime of over 329 500 cycles was determined for these actuators at a ± 2° angular displacement (5 Hz). The lifetime is limited by a bending fatigue that creates a transversal crack on the PANI membrane at the air–water interface. Control over the actuator movement is also manifested by the linear dependences of the bending angle on the charge and of the angular velocity on the current. These relationships are independent of both the kind of applied electric signal and the frequency used.     

Possibilities and extension of XRD material response analysis in failure research for the advanced evaluation of the damage level of Hertzian loaded components

Due to clearly distinguishable damage symptoms, it is differentiated between the surface and sub‐surface failure mode of rolling bearings. Material states red out by X‐ray diffraction (XRD) residual stress measurements point to a variety of loading conditions especially at raceway surfaces that are associated with several competing failure mechanisms. The corresponding lifetime reduction can range from the lower fatigue strength region to material ratcheting in extreme cases. Relevant position of the microstructural changes and nature of the failure mechanisms are characterized. The time alteration of the XRD material parameters measured at or near the surface and at the depth of the maximum equivalent stress correlates, in a different manner, with the statistical parameter of the 10 % bearing life. Both failure modes are illustrated by concrete examples. Contaminated lubricant and boundary lubrication, which represent practically important surface‐induced failures, are discussed in more detail. Gray staining, i.e. shallow pitting, often occurs without distinct indication of global material aging by means of XRD characteristics. Here, scanning electron microscopy observations and electron microprobe analyses point to corrosion fatigue as acting surface failure mechanism. The interaction between material and lubricant under complex loading regimes particularly of mixed friction and corrosion opens further failure research areas in the field of tribology.     

Lipase‐catalyzed dynamic kinetic resolution of (R,S)‐fenoprofen thioester in isooctane

A lipase‐catalyzed enantioselective hydrolysis process under in situ racemization of the remaining (R)‐thioetser substrate with trioctylamine as the catalyst was developed for the production of (S)‐fenoprofen from (R,S)‐fenoprofen 2,2,2‐trifluoroethyl thioester in isooctane. Detailed investigations of trioctylamine concentration on the enzyme activation and the kinetic behavior of the thioester in racemization and enzymatic reactions were conducted, in which good agreement between the experimental data and theoretical results was observed. © 2002 Society of Chemical Industry     

Nickel- and copper-coated carbon fibre reinforced tin-lead alloy composites

Nickel and copper were deposited over brominated, surface treated, and pristine P-100 carbon fibres using cementation and electroplating techniques. The fibres were brominated by bromine vapour for 48 h and then desorbed at 200 °C in air for 12 h. The anodic oxidation treatment of the fibres involved electrochemical etching in a dilute sodium hydroxide electrolyte for 3 min. Electroplated coated fibres showed better tensile properties than cementation coated fibres. In addition, nickel coating exhibited better bonding with the carbon fibres compared to copper coating. The effect of bromination and surface treatment was improved adhesion between coating and fibres. Nickel- and copper-coated fibres, which were brominated, anodically oxidized, and pristine, reinforced tin-lead alloy composites were fabricated by squeeze casting. The composites containing coated treated carbon fibres had higher tensile and shear strength than the ones containing coated pristine carbon fibres. Moreover, the composite with coated brominated carbon fibres had better tensile strength and shear strength than the surface treatment. The results also showed the composites containing nickel-coated fibres had higher tensile and shear strength than the ones containing copper-coated fibres.     

Delayed delivery of surviving triplet after fetal reduction and spontaneous abortion

In multiple pregnancies, survival of remaining fetuses after premature death and delivery of one fetus is uncommon. We report a case of a triplet pregnancy that was reduced to twins at the 14th gestational week and then had preterm premature rupture of membranes and intrauterine fetal death of one twin at the 17th gestational week. To save the surviving fetus, delivery of the dead fetus and ligation of the umbilical cord at the cervical level were performed. We also performed McDonald cervical cerclage to keep the placenta of the dead fetus as well as that of the surviving one in the uterine cavity. After a series of aggressive procedures, including immediate administration of tocolytic agents, and antibiotic prophylaxis to prevent infection and preterm labor, the surviving fetus was delivered vaginally 73 days later due to intractable uterine contractions. After a 10-week hospital stay, the infant boy, weighing 2,500 g, was discharged without any sequelae. To our knowledge, this was the longest interval between deliveries in a triplet pregnancy reported in Taiwan. With adequate intensive management, a satisfactory outcome of the fetus and mother in such cases is possible.